Abstract Mechanical properties and degradation profile are important parameters for the applications of biodegradable polyester such as poly(glycerol sebacate) in biomedical engineering. Here, a strategy is reported to make palmitate functionalized poly(glycerol sebacate) (PPGS) to alter the polymer hydrophobicity, crystallinity, microstructures and thermal properties. The changes of these intrinsic properties impart tunable degradation profiles and mechanical properties to the resultant elastomers depending on the palmitate contents. When the palmitates reach up to 16 mol%, the elastic modulus is tuned from initially 838 ± 55 kPa for the PGS to 333 ± 21 kPa for the PPGS under the same crosslinking conditions. The elastomer undergoes reversible elastic deformations for at least 1000 cycles within 20% strain without failure and shows enhanced elasticity. The polymer degradation is simultaneously inhibited because of the increased hydrophobicity. This strategy is different with other PGS modifications which could form a softer elastomer with less crosslinks but typically lead to a quicker degradation. Because the materials are made from endogenous molecules, they possess good cytocompatibility similar to the PGS control. Although these materials are designed specifically for small arteries, it is expected that they will be useful for other soft tissues too.
more »
« less
Pair of Functional Polyesters That Are Photo-Cross-Linkable and Electrospinnable to Engineer Elastomeric Scaffolds with Tunable Structure and Properties
A pair of alkyne- and thiol-functionalized polyesters are designed to engineer elastomeric scaffolds with a wide range of tunable material properties (e.g., thermal, degradation, and mechanical properties) for different tissues, given their different host responses, mechanics, and regenerative capacities. The two prepolymers are quickly photo-cross-linkable through thiol-yne click chemistry to form robust elastomers with small permanent deformations. The elastic moduli can be easily tuned between 0.96 ± 0.18 and 7.5 ± 2.0 MPa, and in vitro degradation is mediated from hours up to days by adjusting the prepolymer weight ratios. These elastomers bear free hydroxyl and thiol groups with a water contact angle of less than 85.6 ± 3.58 degrees, indicating a hydrophilic nature. The elastomer is compatible with NIH/3T3 fibroblast cells with cell viability reaching 88 ± 8.7% relative to the TCPS control at 48 h incubation. Differing from prior soft elastomers, a mixture of the two prepolymers without a carrying polymer is electrospinnable and UV-cross-linkable to fabricate elastic fibrous scaffolds for soft tissues. The designed prepolymer pair can thus ease the fabrication of elastic fibrous conduits, leading to potential use as a resorbable synthetic graft. The elastomers could find use in other tissue engineering applications as well.
more »
« less
- Award ID(s):
- 2117318
- PAR ID:
- 10565776
- Publisher / Repository:
- ACS
- Date Published:
- Journal Name:
- ACS Applied Bio Materials
- Volume:
- 7
- Issue:
- 2
- ISSN:
- 2576-6422
- Page Range / eLocation ID:
- 863 to 878
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Electrospun fibrous scaffolds made from polymers such as polycaprolactone (PCL) have been used in drug delivery and tissue engineering for their viscoelasticity, biocompatibility, biodegradability, and tunability. Hydrophobicity and the prolonged degradation of PCL causes inhibition of the natural tissue-remodeling processes. Poliglecaprone (PGC), which consists of PCL and Poly (glycolic acid) (PGA), has better mechanical properties and a shorter degradation time compared to PCL. A blend between PCL and PGC called PPG can give enhanced shared properties for biomedical applications. In this study, we fabricated a blend of PCL and PGC nanofibrous scaffold (PPG) at different ratios of PGC utilizing electrospinning. We studied the physicochemical and biological properties, such as morphology, crystallinity, surface wettability, degradation, surface functionalization, and cellular compatibility. All PPG scaffolds exhibited good uniformity in fiber morphology and improved mechanical properties. The surface wettability and degradation studies confirmed that increasing PGC in the PPG composites increased hydrophilicity and scaffold degradation respectively. Cell viability and cytotoxicity results showed that the scaffold with PGC was more viable and less toxic than the PCL-only scaffolds. PPG fibers were successfully coated with polydopamine (PDA) and collagen to improve degradation, biocompatibility, and bioactivity. The nanofibrous scaffolds synthesized in this study can be utilized for tissue engineering applications such as for regeneration of human articular cartilage regeneration and soft bones.more » « less
-
Liquid crystalline elastomers (LCEs) are soft materials that associate order and deformation. Upon deformation, mechanically induced changes order affect entropy and can produce a caloric output (elastocaloric). Elastocaloric effects in materials continue to be considered for functional use as solid state refrigerants. Prior elastocaloric investigations of LCEs and related materials have measured ≈2 °C temperature changes upon deformation (100% strain). Here, the elastocaloric response of LCEs is explored that are prepared with a subambient nematic to isotropic transition temperature. These materials are referred as “isotropic” liquid crystalline elastomers. The LCEs are prepared by a two‐step thiol‐Michael/thiol‐ene reaction. This polymer network chemistry enhances elastic recovery and reduces hysteresis compared to acrylate‐based chemistries. The LCEs exhibit appreciable elastocaloric temperature changes upon deformation and recovery (> ± 3 °C, total ΔTof 6 °C) to deformation driven by minimal force (<< 1 MPa). Notably, the strong association of deformation and order and the resulting temperature change attained at low force achieves a responsivity of 14 °C MPa−1which is seven times greater than natural rubber.more » « less
-
In tissues and organs, the extracellular matrix (ECM) helps maintain inter- and intracellular architectures that sustain the structure–function relationships defining physiological homeostasis. Combining fiber scaffolds and cells to form engineered tissues is a means of replicating these relationships. Engineered tissues' fiber scaffolds are designed to mimic the topology and chemical composition of the ECM network. Here, we asked how cells found in the heart compare in their propensity to align their cytoskeleton and self-organize in response to topological cues in fibrous scaffolds. We studied cardiomyocytes, valvular interstitial cells, and vascular endothelial cells as they adapted their inter- and intracellular architectures to the extracellular space. We used focused rotary jet spinning to manufacture aligned fibrous scaffolds to mimic the length scale and three-dimensional (3D) nature of the native ECM in the muscular, valvular, and vascular tissues of the heart. The representative cardiovascular cell types were seeded onto fiber scaffolds and infiltrated the fibrous network. We measured different cell types' propensity for cytoskeletal alignment in response to fiber scaffolds with differing levels of anisotropy. The results indicated that valvular interstitial cells on moderately anisotropic substrates have a higher propensity for cytoskeletal alignment than cardiomyocytes and vascular endothelial cells. However, all cell types displayed similar levels of alignment on more extreme (isotropic and highly anisotropic) fiber scaffold organizations. These data suggest that in the hierarchy of signals that dictate the spatiotemporal organization of a tissue, geometric cues within the ECM and cellular networks may homogenize behaviors across cell populations and demographics.more » « less
-
Abstract Electrospinning has been used to create scaffolds with tunable micro/nano architecture, stiffness, and porosity to mimic native extracellular matrix. This study investigated the effects of electrospinning parameters and hydrogel formulation (solvent and crosslinker type) on the architecture and properties of fibrous poly(ethylene glycol) (PEG) hydrogels formed from a photoclick thiol‐norbornene reaction. Fibrous hydrogels were prepared using hydrogel precursors (four‐arm PEG norbornene and multi‐thiol crosslinker), sacrificial poly(ethylene oxide) (PEO, 400 kDa), and photoinitiator (I2959) in either 2,2‐triflouroethanol (TFE) or water. Three thiol crosslinkers‐ 2,2′‐(ethylenedioxy)diethanethiol (EDT), pentaerythritol tetrakis(3mercaptopropionate) (PTMP), and PEG dithiol (PEGDT)‐ were investigated. Fibrous PEG networks with uniform fibers were produced at applied voltages of 10 or 12 kV for TFE and 16 kV for water. Fiber diameters of electrospun hydrogels were largely affected by the solvent when combined with PEO concentration and ranged from 0.5 to 3.5 mm in dry state. While the effect of crosslinker type on fiber diameter, morphology, and porosity of the fibrous hydrogel was minimal, it did modulate its shear modulus. To this end, this study provides the groundwork for selecting processing parameters to achieve desired properties of fibrous PEG thiol‐norbornene hydrogels for intended tissue engineering applications ranging from neural, cardiovascular to musculoskeletal.more » « less
- Free Publicly Accessible Full Text
-
Accepted Manuscript1.0
- Journal Article:
- https://doi.org/10.1021/acsabm.3c00894