Carbon nanotubes (CNTs) offer unique properties that have the potential to address multiple issues in industry and material sciences. Although many synthesis methods have been developed, it remains difficult to control CNT characteristics. Here, with the goal of achieving such control, we report a bottom-up process for CNT synthesis in which monolayers of premade aluminum oxide (Al2O3) and iron oxide (Fe3O4) nanoparticles were anchored on a flat silicon oxide (SiO2) substrate. The nanoparticle dispersion and monolayer assembly of the oleic-acid-stabilized Al2O3 nanoparticles were achieved using 11-phosphonoundecanoic acid as a bifunctional linker, with the phosphonate group binding to the SiO2 substrate and the terminal carboxylate group binding to the nanoparticles. Subsequently, an Fe3O4 monolayer was formed over the Al2O3 layer using the same approach. The assembled Al2O3 and Fe3O4 nanoparticle monolayers acted as a catalyst support and catalyst, respectively, for the growth of vertically aligned CNTs. The CNTs were successfully synthesized using a conventional atmospheric pressure-chemical vapor deposition method with acetylene as the carbon precursor. Thus, these nanoparticle films provide a facile and inexpensive approach for producing homogenous CNTs.
more »
« less
This content will become publicly available on March 1, 2026
Vertically aligned carbon nanotubes from premade binary metal oxide nanoparticles on bare SiO2
The synthesis of carbon nanotubes (CNTs) requires well-defined catalyst nanoparticles that can influence both diameter and chirality. Herein, catalyst nanoparticles containing both the catalyst and catalyst support material were developed. Bimetallic aluminum oxide–iron oxide (AlOx–Fe2O3) nanorice was synthesized from a mixture containing both aluminum and iron oleate precursors in the solution phase. The nanoparticles were assembled as a monolayer film on a silicon oxide (SiO2) substrate via organic linker molecules to synthesize vertically aligned carbon nanotubes (VA-CNTs). Microscopic and spectroscopic characterization of the premade catalyst nanoparticles and monolayer film assembly revealed the quality of the nanoscale assembly, which facilitated the successful growth of VA-CNTs. The length of the CNTs synthesized using these AlOx–Fe2O3 nanorice catalyst nanoparticles surpassed that of previously reported CNTs grown on bare SiO2 surfaces without oxide buffer layers. In addition, the CNTs appeared to be directly bonded/connected to the SiO2 substrate, suggesting CNT formation via the tip-growth mechanism. The effects of growth temperature and catalyst reduction time were evaluated to obtain high-yield VA-CNTs.
more »
« less
- Award ID(s):
- 2334039
- PAR ID:
- 10572120
- Editor(s):
- Liu, Chang
- Publisher / Repository:
- Elsevier
- Date Published:
- Journal Name:
- Carbon
- Volume:
- 235
- Issue:
- C
- ISSN:
- 0008-6223
- Page Range / eLocation ID:
- 120086
- Subject(s) / Keyword(s):
- Carbon nanotube synthesis, premade catalsyt, nanoparticles, monolayer film assemblies
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
null (Ed.)A series of Al2O3-supported Fe-containing catalysts were synthesized by incipient wetness impregnation. The iron surface density was varied from 1 to 13 Fe atoms/nm2 spanning sub- and above-monolayer coverage. The resulting supported Fe-catalysts were characterized with N2 physisorption, ex situ XRD, PDF, XAS, AC-STEM and chemically probed by H2-TPR. The results suggest that over this entire range of loadings, Fe was present as dispersed species, with only a very small fraction of Fe2O3 aggregates, at the highest Fe loading. The in situ sulfidation of Fe/Al2O3 resulted in the formation of a highly active and selective PDH catalyst. The highest activity with 52% propane conversion and ~99% propylene selectivity at 560 °C was obtained for the 6.4 Fe/Al2O3 catalyst suggesting that this is the highest amount of Fe that could be fully dispersed on the support in sulfided form. XRD and AC-STEM indicated the absence of any crystalline iron sulfide aggregates after sulfidation and reaction. H2-TPR results indicated that the amount of the reducible Fe sites in the sulfided catalyst remained constant above monolayer coverage, and increasing loading did not increase the number of reducible Fe sites. Consistent with these results, the reactivity per gram of catalyst showed no increase with Fe loading above monolayer coverage, suggesting that additional Fe remains conformal to the alumina surface.more » « less
-
Iron oxide nanomaterials participate in redox processes that give them ideal properties for their use as earth-abundant catalysts. Fabricating nanocatalysts for such applications requires detailed knowledge of the deposition and growth. We report the spontaneous deposition of iron oxide nanoparticles on HOPG in defect areas and on step edges from a metal precursor solution. To study the nucleation and growth of iron oxide nanoparticles, tailored defects were created on the surface of HOPG using various ion sources that serve as the target sites for iron oxide nucleation. After solution deposition and annealing, the iron oxide nanoparticles were found to nucleate and coalesce at 400 °C. AFM revealed that the particles on the sp 3 carbon sites enabled the nanoparticles to aggregate into larger particles. The iron oxide nanoparticles were characterized as having an Fe 3+ oxidation state and two different oxygen species, Fe–O and Fe–OH/Fe–OOH, as determined by XPS. STEM imaging and EDS mapping confirmed that the majority of the nanoparticles grown were converted to hematite after annealing at 400 °C. A mechanism of spontaneous and selective deposition on the HOPG surface and transformation of the iron oxide nanoparticles is proposed. These results suggest a simple method for growing nanoparticles as a model catalyst.more » « less
-
Iron oxide nanoparticles (IONPs) were synthesized via a block copolymer-assisted hydrothermal method and the phase purity and the crystal structure were investigated by X-ray diffraction. The Rietveld analysis of X-ray diffractometer spectra shows the hexagonal phase symmetry of α-Fe2O3. Further, the vibrational study suggests Raman active modes: 2A1g + 5Eg associated with α-Fe2O3, which corroborates the Rietveld analysis and orbital analysis of 2PFe. The superparamagnetic behavior is confirmed by magnetic measurements performed by the physical properties measurement system. The systematic study of the Congo red (CR) interaction with IONPs using a UV-visible spectrophotometer and a liquid chromatography–tandem mass spectrometry system equipped with a triple quadrupole mass analyzer and an electrospray ionization interface shows effective adsorption. In visible light, the Fe2O3 nanoparticles get easily excited and generate electrons and holes. The photogenerated electrons reduce the Fe3+ ions to Fe2+ ions. The Fe2+/H2O2 oxidizes CR by the Fenton mechanism. The strong adsorption ability of prepared nanoparticles towards dyes attributes the potential candidates for wastewater treatment and other catalytic applications.more » « less
-
While the physical properties of carbon nanotubes (CNTs) are often superior to conventional engineering materials, their widespread adoption into many applications is limited by scaling the properties of individual CNTs to macroscale CNT assemblies known as CNT forests. The self-assembly mechanics of CNT forests that determine their morphology and ensemble properties remain poorly understood. Few experimental techniques exist to characterize and observe the growth and self-assembly processes in situ. Here we introduce the use of in-situ scanning electron microscope (SEM) synthesis based on chemical vapor deposition (CVD) processing. In this preliminary report, we share best practices for in-situ SEM CVD processing and initial CNT forest synthesis results. Image analysis techniques are developed to identify and track the movement of catalyst nanoparticles during synthesis conditions. Finally, a perspective is provided in which in-situ SEM observations represent one component of a larger system in which numerical simulation, machine learning, and digital control of experiments reduces the role of humans and human error in the exploration of CNT forest process-structure-property relationships.more » « less