Chemically preintercalated dopamine (DOPA) molecules were used as both reducing agent and carbon precursor to prepare δ-V2O5∙nH2O/C, H2V3O8/C, VO2(B)/C and V2O3/C nanocomposites via hydrothermal treatment or hydrothermal treatment followed by annealing under Ar flow. We found that the phase composition and morphology of the produced composites are influenced by the DOPA:V2O5 ratio used to synthesize (DOPA)xV2O5 precursors through DOPA diffusion into the interlayer region of δ-V2O5∙nH2O framework. The increase of DOPA concentration in the reaction mixture led to more pronounced reduction of vanadium and a higher fraction of carbon in the composites’ structure, as evidenced by XPS and Raman spectroscopy measurements. The electrochemical charge storage properties of the synthesized nanocomposites were evaluated in Li-ion cells with non-aqueous electrolyte. δ-V2O5∙nH2O/C, H2V3O8/C, VO2(B)/C, and V2O3/C electrodes delivered high initial capacities of 214, 252, 279, and 637 mAh·g–1, respectively. The insights provided by this investigation open up the possibility of creating new nanocomposite oxide/carbon electrodes for a variety of applications such as energy storage, sensing and electrochromic devices.
more »
« less
3D printing carbon–carbon composites with multilayered architecture for enhanced multifunctional properties
Carbon–carbon (C–C) composites are highly sought-after in aviation, automotive, and defense sectors due to their outstanding thermal & thermo-mechanical properties even surpassing those of alloys and other composites for exterme operations.
more »
« less
- PAR ID:
- 10575776
- Publisher / Repository:
- RSC
- Date Published:
- Journal Name:
- Journal of Materials Chemistry A
- Volume:
- 12
- Issue:
- 29
- ISSN:
- 2050-7488
- Page Range / eLocation ID:
- 18269 to 18285
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Titanium nitride and vanadium nitride–carbon-based composite systems, TiN/C and VN/C, were prepared using a new synthesis method based on the thermal decomposition of titanyl tetraphenyl porphyrin (TiOTPP) and vanadyl tetraphenyl porphyrin (VOTPP), respectively. The structure of the TiN/C and VN/C composite materials, as well as their precursors, were characterized using Fourier Transformed Infrared Spectroscopy, X-Ray diffraction (XRD), X-Ray energy dispersive (EDS) and X-Ray photoelectron spectroscopy (XPS). Morphologies of the TiN/C and VN/C composites were examined by means of scanning electron (SEM) and transmission electron (TEM) microscopy. The synthesis of the non-metalated tetraphenyl porphyrin, the titanium, and vanadium tetraphenyl porphyrin complexes were confirmed using FTIR. The thermal decomposition of the titanium and vanadium tetraphenyl porphyrin complexes produced the respective metal nitride encapsulated in a carbon matrix; this was confirmed by XRD, SEM, TEM, and XPS. From the XRD patterns, it was determined that the TiN and VN were presented in cubic form with expected space group FM-3M and 1:1 (metal:N) stoichiometry. The XPS results confirmed the presence of both TiN and VN in the carbon matrix without metal carbides. The SEM and TEM results showed that both TiN and VN nanoparticles formed small clusters throughout the carbon matrix; the EDS results revealed a uniform composition. The synthesis method presented in this work is novel and serves as an effective means to produce TiN and VN NPs with good structure and morphology embedded in a carbon matrix.more » « less
-
Spread tow carbon fiber composites are receiving increased attention for diverse applications in space and sports gear due to their thin form, which is suitable for deployable structures, and high tensile strength. Their compressive strength, however, is much lower than their tensile strength due to low interlaminar strength. Herein we report a facile technique to enhance their performance through interlaminar insertion of aligned carbon nanotube (CNT) sheets. The inserted CNT sheets also provide electrical conductivity in the composites even at a low CNT loading below the electrical percolation threshold established for CNT-filled composites. Mechanical and electrical characterization was conducted on the CNT sheet-inserted composites and the baseline composites. Results show that the CNT sheets increase the compressive strength by 14.7% compared with the baseline. Such an increase is attributed to the increased adhesion provided by the inserted CNT sheets at the interface between neighboring plies, which also increases the interlaminar shear strength by 33.0% and the interfacial mode-II fracture toughness by 34.6% compared with the baseline composites without inserting CNT sheets. The well-aligned CNT sheet structure maintained between the neighboring plies contributed to a 64.7% increase in electrical conductivity compared with the baseline composites. The findings indicate that the insertion of well-aligned ultrathin CNT sheets in the interlaminar region of a spread tow carbon fiber composite provides significant enhancement in mechanical and electrical performance, paving the path toward applications where both mechanical and electrical performances are crucial, such as for structural health monitoring, lightning protection, and de-icing in aircraft and wind blades.more » « less
-
This research focused on testing the effect of the negative Poisson’s ratio of a carbon fiber composite on its critical buckling load. A secondary goal was to determine the accuracy of simulation compared to the experimental results for carbon fiber composites. In order to accomplish these two goals, both simulation and experimental testing were employed. For the simulation, ABAQUS software was used to determine predicted values for the critical buckling loads of auxetic and nonauxetic composites as well as the respective nonlinear force behavior of these composites. These results were then compared to experimental results of four auxetic and four non-auxetic specimens each experiencing uniaxial compressive tests. The results of simulation and experimentation showed that the critical buckling loads, and force sustained in general, of the auxetic composites were about three times higher than those of non-auxetic composites. While it appears that the negative Poisson’s ratio has a significant impact on the buckling strength of composite materials, further testing is required to determine the effects of other factors on the critical buckling loads. Along with this, the simulation was more accurate for the auxetic composites than for the non-auxetic composites. Therefore, further testing and simulation are required to determine the limits of simulation accuracy for composite structures.more » « less
-
Embedding carbon in metals has long been known to enhance the mechanical properties of metal carbon composites. We report the possibility of growing Al–C composites by the hot isostatic pressing method, with carbon embedded into an Al lattice in graphitic form without the formation of Al4C3. Raman spectroscopy confirms the formation of sp2-hybridized carbon clusters in the aluminum lattice. The bulk moduli of the samples were measured to be between 60 and 100 GPa. From the results of first principles density functional theory calculations, we show that the formation of sp2-hybridized carbon clusters is more stable than having isolated C scatterers in aluminum. Our results show that the extended network of C clusters shows a higher bulk modulus while isolated scattering centers could lower the bulk modulus. We explain this behavior with the analysis of total charge distribution. Localization of charge density decreases materials’ ability to respond to external stress, thus showing a reduced bulk modulus. Some defect configuration may reduce the symmetry while others keep the symmetry of the host configuration even for the same chemical composition of Al–C composites.more » « less
- Free Publicly Accessible Full Text
-
Accepted Manuscript1.0
- Journal Article:
- https://doi.org/10.1039/D4TA02267J