skip to main content
US FlagAn official website of the United States government
dot gov icon
Official websites use .gov
A .gov website belongs to an official government organization in the United States.
https lock icon
Secure .gov websites use HTTPS
A lock ( lock ) or https:// means you've safely connected to the .gov website. Share sensitive information only on official, secure websites.

Attention:

The NSF Public Access Repository (PAR) system and access will be unavailable from 11:00 PM ET on Friday, July 11 until 2:00 AM ET on Saturday, July 12 due to maintenance. We apologize for the inconvenience.

Explore Research Products in the PAR
It may take a few hours for recently added research products to appear in PAR search results.


This content will become publicly available on January 28, 2026

Title: Surface Manipulation on Pt 2.2 Ni(111) Nanocatalysts for Boosting Their ORR Performance in Alkaline Media
We have previously shown that Pt–Ni alloy nano-octahedra with {111} facets exhibit outstanding electrochemical performance in the oxygen reduction reaction (ORR) in acidic media when their surfaces are finely tailored at the atomic level. In this investigation, we further refine the surface structure of Pt2.2Ni octahedral nanocatalysts to improve ORR performance in a 0.1 M KOH solution using diverse surface manipulation techniques. Through systematic analysis using electrochemical CO stripping, cyclic voltammetry, and X-ray photoelectron spectroscopy, we examined the surfaces of Pt2.2Ni octahedral nanocatalysts pretreated with various methods, including etching in acetic acid or perchloric acid, and subsequent electrochemical activation in an alkaline solution or an acidic solution. Among these treatments, those involving acidic media, particularly electrochemical cycling in acidic electrolytes, demonstrated significantly enhanced ORR activity in 0.1 M KOH. The latter exhibited a mass activity of 2.95 A/mgpt and a specific activity of 8.71 mA/cm2 at 0.90 V, surpassing state-of-the-art Pt/C by 12-fold and 34-fold, respectively. Furthermore, this identified nanocatalyst displayed robust stability, with negligible activity decay observed after 10,000 cycles. This study suggests that the improved ORR activity can be attributed to the Pt-rich surfaces with well-preserved {111} lattices on the surface-modified Pt–Ni nano-octahedra.  more » « less
Award ID(s):
2347030 1808383 2303712
PAR ID:
10583478
Author(s) / Creator(s):
; ; ; ; ; ; ; ; ;
Publisher / Repository:
ACS
Date Published:
Journal Name:
Chemistry of Materials
Volume:
37
Issue:
2
ISSN:
0897-4756
Page Range / eLocation ID:
776 to 785
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. ; ; ; ; (, ChemElectroChem)
    Abstract The electrochemical oxygen reduction reaction (ORR) is critical for fuel cell application, and modifying surface structures of electrocatalysts has proven effective in improving their catalytic performances. In this study, we investigated surface‐engineered Pt−Ni nano‐octahedra subjected to annealing in various atmospheres. All octahedral nanocrystals retained their Pt−Ni {111} facets at an elevated temperature following the annealing treatments. Air annealing led to the formation of nickel‐rich shells on the Pt−Ni surface. In contrast, hydrogen (H₂) as a reducing gas facilitated the reduction of surface Ni species, incorporating them into the Pt−Ni bulk alloy, which resulted in superior mass activity and specific activity for ORR‐approximately 2.4 and 2.3 times as high as those from the unmodified counterpart, respectively. After 20,000 potential cycles, the H₂/Ar‐annealed Pt−Ni nano‐octahedra maintained a mass activity of 3.92 A/ , surpassing the initial mass activity of the unannealed counterparts (2.95 A/ ). These findings demonstrate a viable approach for tailoring catalyst surfaces to enhance performance in various energy storage and conversion applications. 
    more » « less
  2. ; ; ; ; ; ; ; ; ; ; et al (, Nano Letters)
    This study demonstrates an atomic composition manipulation on Pt–Ni nano-octahedra to enhance their electrocatalytic performance. By selectively extracting Ni atoms from the {111} facets of the Pt–Ni nano-octahedra using gaseous carbon monoxide at an elevated temperature, a Pt-rich shell is formed, resulting in an ∼2 atomic layer Pt-skin. The surface-engineered octahedral nanocatalyst exhibits a significant enhancement in both mass activity (∼1.8-fold) and specific activity (∼2.2-fold) toward the oxygen reduction reaction compared with its unmodified counterpart. After 20,000 potential cycles of durability tests, the surface-etched Pt–Ni nano-octahedral sample shows a mass activity of 1.50 A/mgPt, exceeding the initial mass activity of the unetched counterpart (1.40 A/mgPt) and outperforming the benchmark Pt/C (0.18 A/mgPt) by a factor of 8. DFT calculations predict this improvement with the Pt surface layers and support these experimental observations. This surface-engineering protocol provides a promising strategy for developing novel electrocatalysts with improved catalytic features. 
    more » « less
  3. ; ; ; ; ; ; ; ; (, Angewandte Chemie International Edition)
    Abstract Fabrication of 3dmetal‐based core@shell nanocatalysts with engineered Pt‐surfaces provides an effective approach for improving the catalytic performance. The challenges in such preparation include shape control of the 3dmetallic cores and thickness control of the Pt‐based shells. Herein, we report a colloidal seed‐mediated method to prepare octahedral CuNi@Pt‐Cu core@shell nanocrystals using CuNi octahedral cores as the template. By precisely controlling the synthesis conditions including the deposition rate and diffusion rate of the shell‐formation through tuning the capping ligand, reaction temperature, and heating rate, uniform Pt‐based shells can be achieved with a thickness of <1 nm. The resultant carbon‐supported CuNi@Pt‐Cu core@shell nano‐octahedra showed superior activity in electrochemical methanol oxidation reaction (MOR) compared with the commercial Pt/C catalysts and carbon‐supported CuNi@Pt‐Cu nano‐polyhedron counterparts. 
    more » « less
  4. ; ; ; ; ; ; ; ; ; ; et al (, Advanced Energy Materials)
    Abstract Engineering the crystal structure of Pt–M (M = transition metal) nanoalloys to chemically ordered ones has drawn increasing attention in oxygen reduction reaction (ORR) electrocatalysis due to their high resistance against M etching in acid. Although Pt–Ni alloy nanoparticles (NPs) have demonstrated respectable initial ORR activity in acid, their stability remains a big challenge due to the fast etching of Ni. In this work, sub‐6 nm monodisperse chemically orderedL10‐Pt–Ni–Co NPs are synthesized for the first time by employing a bifunctional core/shell Pt/NiCoOxprecursor, which could provide abundant O‐vacancies for facilitated Pt/Ni/Co atom diffusion and prevent NP sintering during thermal annealing. Further, Co doping is found to remarkably enhance the ferromagnetism (room temperature coercivity reaching 2.1 kOe) and the consequent chemical ordering ofL10‐Pt–Ni NPs. As a result, the best‐performing carbon supportedL10‐PtNi0.8Co0.2catalyst reveals a half‐wave potential (E1/2) of 0.951 V versus reversible hydrogen electrode in 0.1mHClO4with 23‐times enhancement in mass activity over the commercial Pt/C catalyst along with much improved stability. Density functional theory (DFT) calculations suggest that theL10‐PtNi0.8Co0.2core could tune the surface strain of the Pt shell toward optimized Pt–O binding energy and facilitated reaction rate, thereby improving the ORR electrocatalysis. 
    more » « less
  5. ; ; ; (, Angewandte Chemie International Edition)
    Abstract To produce efficient ORR catalysts with low Pt content, PtNi porous films (PFs) with sufficiently exposed Pt active sites were designed by an approach combining electrochemical bottom‐up (electrodeposition) and top‐down (anodization) processes. The dynamic oxygen‐bubble template (DOBT) programmably controlled by a square‐wave potential was used to tune the catalyst morphology and expose Pt active facets in PtNi PFs. Surface‐bounded species, such as hydroxyl (OH*, *=surface site) on the exposed PtNi PFs surfaces were adjusted by the applied anodic voltage, further affecting the dynamic oxygen (O2) bubbles adsorption on Pt. As a result, PtNi PF with enriched Pt(111) facets (denoted as Pt3.5 %Ni PF) was obtained, showing prominent ORR activity with an onset potential of 0.92 V (vs. RHE) at an ultra‐low Pt loading (0.015 mg cm−2). 