The stabilization of the threshold switching characteristics of memristive NbOx is examined as a function of sample growth and device characteristics. Sub-stoichiometric Nb2O5 was deposited via magnetron sputtering and patterned in nanoscale (50×50–170×170nm2) W/Ir/NbOx/TiN devices and microscale (2×2–15×15μm2) crossbar Au/Ru/NbOx/Pt devices. Annealing the nanoscale devices at 700 °C removed the need for electroforming the devices. The smallest nanoscale devices showed a large asymmetry in the IV curves for positive and negative bias that switched to symmetric behavior for the larger and microscale devices. Electroforming the microscale crossbar devices created conducting NbO2 filaments with symmetric IV curves whose behavior did not change as the device area increased. The smallest devices showed the largest threshold voltages and most stable threshold switching. As the nanoscale device area increased, the resistance of the devices scaled with the area as R∝A−1, indicating a crystallized bulk NbO2 device. When the nanoscale device size was comparable to the size of the filaments, the annealed nanoscale devices showed similar electrical responses as the electroformed microscale crossbar devices, indicating filament-like behavior in even annealed devices without electroforming. Finally, the addition of up to 1.8% Ti dopant into the films did not improve or stabilize the threshold switching in the microscale crossbar devices.
more »
« less
Enhancement in neuromorphic NbO2 threshold switching at cryogenic temperatures
The electrical properties and performance characteristics of niobium dioxide (NbO2)-based threshold switching devices are examined at cryogenic temperatures. Substoichiometric Nb2O5 was deposited via magnetron sputtering and patterned in microscale (2×2−15×15 μm2) crossbar Au/Ru/NbOx/Pt devices and electroformed at 3–5 V to make NbO2 filaments. At cryogenic temperatures, the threshold voltage (Vth) increased by more than a factor of 3. The hold voltage (Vh) was significantly lower than the threshold voltage for fast voltage sweeps (200 ms per measurement). If the sample is allowed to cool between voltage measurements, the hold voltage increases, but never reaches the threshold voltage, indicating the presence of nonvolatile Nb2O5 in the filament. The devices have an activation energy of Ea≈1.4 eV, lower than other NbO2 devices reported. Our work shows that even nominally “bad” selector devices can be improved by reducing the leakage current and increasing the sample resistance at cryogenic temperatures.
more »
« less
- PAR ID:
- 10584225
- Publisher / Repository:
- American Vacuum Society
- Date Published:
- Journal Name:
- Journal of Vacuum Science & Technology B
- Volume:
- 42
- Issue:
- 6
- ISSN:
- 2166-2746
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Abstract The development of cryogenic semiconductor electronics and superconducting quantum computing requires composite materials that can provide both thermal conduction and thermal insulation. We demonstrated that at cryogenic temperatures, the thermal conductivity of graphene composites can be both higher and lower than that of the reference pristine epoxy, depending on the graphene filler loading and temperature. There exists a well-defined cross-over temperature—above it, the thermal conductivity of composites increases with the addition of graphene; below it, the thermal conductivity decreases with the addition of graphene. The counter-intuitive trend was explained by the specificity of heat conduction at low temperatures: graphene fillers can serve as, both, the scattering centers for phonons in the matrix material and as the conduits of heat. We offer a physical model that explains the experimental trends by the increasing effect of the thermal boundary resistance at cryogenic temperatures and the anomalous thermal percolation threshold, which becomes temperature dependent. The obtained results suggest the possibility of using graphene composites for, both, removing the heat and thermally insulating components at cryogenic temperatures—a capability important for quantum computing and cryogenically cooled conventional electronics.more » « less
-
Abstract Workbench-size particle accelerators, enabled by Nb3Sn-based superconducting radio-frequency (SRF) cavities, hold the potential of driving scientific discovery by offering a widely accessible and affordable source of high-energy electrons and x-rays. Thin-film Nb3Sn RF superconductors with high quality factors, high operation temperatures, and high-field potentials are critical for these devices. However, surface roughness, non-stoichiometry, and impurities in Nb3Sn deposited by conventional Sn-vapor diffusion prevent them from reaching their theoretical capabilities. Here we demonstrate a seed-free electrochemical synthesis that pushes the limit of chemical and physical properties in Nb3Sn. Utilization of electrochemical Sn pre-deposits reduces the roughness of converted Nb3Sn by five times compared to typical vapor-diffused Nb3Sn. Quantitative mappings using chemical and atomic probes confirm improved stoichiometry and minimized impurity concentrations in electrochemically synthesized Nb3Sn. We have successfully applied this Nb3Sn to the large-scale 1.3 GHz SRF cavity and demonstrated ultra-low BCS surface resistances at multiple operation temperatures, notably lower than vapor-diffused cavities. Our smooth, homogeneous, high-purity Nb3Sn provides the route toward high efficiency and high fields for SRF applications under helium-free cryogenic operations.more » « less
-
We report the electrical properties of Al0.3Ga0.7N/GaN heterojunction field effect transistor (HFET) structures with a Ga2O3 passivation layer grown by metal–organic chemical vapor deposition (MOCVD). In this study, three different thicknesses of β-Ga2O3 dielectric layers were grown on Al0.3Ga0.7N/GaN structures leading to metal-oxide-semiconductor-HFET or MOSHFET structures. X-ray diffraction (XRD) showed the (2¯01) orientation peaks of β-Ga2O3 in the device structure. The van der Pauw and Hall measurements yield the electron density of ~ 4 × 1018 cm−3 and mobility of ~770 cm2V−1s−1 in the 2-dimensional electron gas (2DEG) channel at room temperature. Capacitance–voltage (C-V) measurement for the on-state 2DEG density for the MOSHFET structure was found to be of the order of ~1.5 × 1013 cm−2. The thickness of the Ga2O3 layer was inversely related to the threshold voltage and the on-state capacitance. The interface charge density between the oxide and Al0.3Ga0.7N barrier layer was found to be of the order of ~1012 cm2eV−1. A significant reduction in leakage current from ~10−4 A/cm2 for HFET to ~10−6 A/cm2 for MOSHFET was observed well beyond pinch-off in the off-stage at -20 V applied gate voltage. The annealing at 900° C of the MOSHFET structures revealed that the Ga2O3 layer was thermally stable at high temperatures resulting in insignificant threshold voltage shifts for annealed samples with respect to as-deposited (unannealed) structures. Our results show that the MOCVD-gown Ga2O3 dielectric layers can be a strong candidate for stable high-power devices.more » « less
-
A carboxylated thiophene polymer-based chemiresistive device in a field-effect transistor (FET) configuration with unusual and enhanced responses to the widespread pollutants nitrogen dioxide (NO 2 ) and ammonia (NH 3 ) is described. The device based on a polymeric thiophene carboxylic acid showed a dramatic and superlinear increase in drain current ( I D ) of over 15 000% to a ramped exposure to 10 ppm NO 2 over several minutes, while its ethyl ester counterpart had significantly lower response. Devices incorporating either an ester or carboxylic acid displayed comparable and previously unreported increases in I D from 10 ppm ramped NH 3 exposure of 200–300%. Conventional poly(alkylthiophenes) showed the expected current decreases from similar NH 3 exposures. Using threshold voltage shifts in silicon transistors coupled to our recently reported remote gate (RG) platform with thiophene polymer coatings, we determined that two differing response mechanisms are associated with the two gas exposures. By calculating the charge density induced in the polymers by NO 2 exposure using the silicon transistor voltage shifts, we conclude that proton conduction contributes significantly to the high sensitivity of the carboxylic acid to NO 2 , in addition to doping that was observed for all four polymers. Furthermore, hydrogen bonding moieties of the carboxylic acid and ester may be able to physisorb NH 3 and thus alter the charge distribution, rearrange polymer chains, and/or create a proton transfer network leading to the I D increase that is the opposite of the response obtained from non-carboxylated thiophene polymers.more » « less