Explore Research Products in the PAR
It may take a few hours for recently added research products to appear in PAR search results.


  • NSF Public Access
  • Search Results
  • Experimental investigation of the effect of nickel on the electrical resistivity of Fe-Ni and Fe-Ni-S alloys under pressure
Title: Experimental investigation of the effect of nickel on the electrical resistivity of Fe-Ni and Fe-Ni-S alloys under pressure
Abstract Electrical resistivity experiments were conducted on three alloys in the iron-rich side of the Fe-Ni(-S) system (Fe-5 wt% Ni, Fe-10 wt% Ni, Fe-10 wt% Ni-5 wt% S) at 4.5 and 8 GPa and up to 1900 K using the multi-anvil apparatus and the 4-electrode technique. For all samples, increasing temperature increases resistivity. At a specified temperature, Fe-Ni(-S) alloys are more resistive than Fe by a factor of about 3. Fe-Ni alloys containing 5 and 10 wt% Ni present comparable electrical resistivity values. The resistivity of Fe-Ni(-S) alloys is comparable to the one of Fe = 5 wt% S at 4.5 GPa and is about three times higher than the resistivity of Fe = 5 wt% S at 8 GPa, due to a different pressure dependence of electrical resistivity between Fe-Ni and Fe-S alloys. Based on these electrical results and experimentally determined thermal conductivity values from the literature, lower and upper bounds of thermal conductivity were calculated. For all Ni-bearing alloys, thermal conductivity estimates range between ~12 and 20 W/(m⋅K) over the considered pressure and temperature ranges. Adiabatic heat fluxes were computed for both Ganymede's core and the Lunar core, and heat flux values suggest a significant dependence to both core composition and the adiabatic temperature. Comparison with previous thermochemical models of the cores of Ganymede and the Moon suggests that some studies may have overestimated the thermal conductivity and hence, the heat flux along the adiabat in these planetary cores.  more » « less
Award ID(s):
2152686
PAR ID:
10589916
Author(s) / Creator(s):
Publisher / Repository:
MSA
Date Published:
Journal Name:
American Mineralogist
Volume:
105
Issue:
7
ISSN:
0003-004X
Page Range / eLocation ID:
1069 to 1077
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. ; ; (, Journal of Geophysical Research: Planets)
    Abstract We present a joint experimental‐modeling investigation of core cooling in small terrestrial bodies. Significant amounts of light elements (S, O, Mg, Si) may compose the metallic cores of terrestrial planets and moons. However, the effect of multiple light elements on transport properties, in particular, electrical resistivity and thermal conductivity, is not well constrained. Electrical experiments were conducted at 10 GPa and up to 1850 K on high‐purity powder mixtures in the Fe‐S‐O(±Mg, ±Si) systems using the multianvil apparatus and the four‐electrode technique. The sample compositions contained 5 wt.% S, up to 3 wt.% O, up to 2 wt.% Mg, and up to 1 wt.% Si. We observe that above the eutectic temperature, electrical resistivity is significantly sensitive to the nature and amount of light elements. For each composition, thermal conductivity‐temperature equations were estimated using the experimental electrical results and a modified Wiedemann‐Franz law. These equations were implemented in a thermochemical core cooling model to study the evolution of the dynamo. Modeling results suggest that bulk chemistry significantly affects the entropy available to power dynamo action during core cooling. In the case of Mars, the presence of oxygen would delay the dynamo cessation by up to 1 Gyr compared to an O‐free, Fe‐S core. Models with 3 wt% O can be reconciled with the inferred cessation time of the Martian dynamo if the core‐mantle boundary heat flow falls from >2 TW to ~0.1 TW in the first 0.5 Gyr following core formation. 
    more » « less
  2. ; ; ; ; ; ; ; ; ; (, Journal of Geophysical Research: Solid Earth)
    Abstract The presence of light elements in the metallic cores of the Earth, the Moon, and other rocky planetary bodies has been widely proposed. Carbon is among the top candidates in light of its high cosmic abundance, siderophile nature, and ubiquity in iron meteorites. It is, however, still controversial whether carbon‐rich core compositional models can account for the seismic velocity observations within the Earth and lunar cores. Here, we report the density and elasticity of Fe90Ni10‐3 wt.% C and Fe90Ni10‐5 wt.% C liquid alloys using synchrotron‐based X‐ray absorption experiments and first‐principles molecular dynamics simulations. Our results show that alloying of 3 wt.% and 5 wt.% C lowers the density of Fe90Ni10liquid by ∼2.9–3.1% at 2 GPa, and ∼3.4–3.6% at 9 GPa. More intriguingly, our experiments and simulations both demonstrate that the bulk moduli of the Fe‐Ni‐C liquids are similar to or slightly higher than those of Fe‐Ni liquids. Thus, the calculated compressional velocities (vp) of Fe‐Ni‐C liquids are higher than that of pure Fe‐Ni alloy, promoting carbon as a possible candidate to explain the elevatedvpin the Earth's outer core. However, the values and slopes of both density andvpof the studied two Fe‐Ni‐C liquids do not match the outer core seismic models, suggesting that carbon may not be the sole principal light element in Earth's outer core. The highvpof Fe‐Ni‐C liquids does not match the presumptivevpof the lunar outer core well, indicating that carbon is less likely to be its dominant light element. 
    more » « less
  3. ; ; ; (, Journal of Geophysical Research: Planets)
    Abstract The motion of liquid iron (Fe) alloy materials in the outer core drives the dynamo, which generates Mercury's magnetic field. The assessment of core models requires laboratory measurements of the melting temperature of Fe alloys at high pressure. Here, we experimentally determined the melting curve of Fe9wt%Si and Fe17wt%Si up to 17 GPa using in situ and ex situ measurements of intermetallic fast diffusion that serves as the melting criterion in a large‐volume press. Our determined melting slopes are comparable with previous studies up to about 17 GPa. However, when extrapolated, our melting slopes significantly deviate from previous studies at higher pressures. For Mercury's core with a model composition of Fe9wt%Si, the melting temperature‐depth profile determined in our study is lower by ∼150–250 K when compared with theoretical calculations. Using the new melting curve of Fe9wt%Si and the electrical resistivity values from a previous study of Fe8.5wt%Si, we estimate that the electronic thermal conductivity of liquid Fe9wt%Si is 30 Wm−1K−1at the Mercury'sCMBpressure of 5 GPa and 37 Wm−1K−1at an assumedICBof 21 GPa, corresponding to heat flux values of 23 mWm−2and 32 mWm−2, respectively. These values provide new constraints on the core models. 
    more » « less
  4. ; ; ; ; ; ; ; ; ; ; et al (, Proceedings of the National Academy of Sciences)
    Light elements in Earth’s core play a key role in driving convection and influencing geodynamics, both of which are crucial to the geodynamo. However, the thermal transport properties of iron alloys at high-pressure and -temperature conditions remain uncertain. Here we investigate the transport properties of solid hexagonal close-packed and liquid Fe-Si alloys with 4.3 and 9.0 wt % Si at high pressure and temperature using laser-heated diamond anvil cell experiments and first-principles molecular dynamics and dynamical mean field theory calculations. In contrast to the case of Fe, Si impurity scattering gradually dominates the total scattering in Fe-Si alloys with increasing Si concentration, leading to temperature independence of the resistivity and less electron–electron contribution to the conductivity in Fe-9Si. Our results show a thermal conductivity of ∼100 to 110 W⋅m −1 ⋅K −1 for liquid Fe-9Si near the topmost outer core. If Earth’s core consists of a large amount of silicon (e.g., > 4.3 wt %) with such a high thermal conductivity, a subadiabatic heat flow across the core–mantle boundary is likely, leaving a 400- to 500-km-deep thermally stratified layer below the core–mantle boundary, and challenges proposed thermal convection in Fe-Si liquid outer core. 
    more » « less
  5. ; ; ; ; ; ; ; (, Journal of Geophysical Research: Planets)
    Abstract Accurate knowledge of the phase transitions and thermoelastic properties of candidate iron alloys, such as Fe‐Si alloys, is essential for understanding the nature and dynamics of planetary cores. The phase diagrams of some Fe‐Si alloys between 1 atm and 16 GPa have been back‐extrapolated from higher pressures, but the resulting phase diagram of Fe83.6Si16.4(9 wt.% Si) is inconsistent with temperature‐induced changes in its electrical resistivity between 6 and 8 GPa. This study reports in situ synchrotron X‐ray diffraction (XRD) measurements on pre‐melted and powder Fe83.6Si16.4samples from ambient conditions to 60 GPa and 900 K using an externally heated diamond‐anvil cell. Upon compression at 300 K, thebccphase persisted up to ∼38 GPa. Thehcpphase appeared near 8 GPa in the pre‐melted sample, and near 17 GPa in the powder sample. The appearance of thehcpphase in the pre‐melted sample reconciles the reported changes in electrical resistivity of a similar sample, thus resolving the low‐pressure region of the phase diagram. The resulting high‐temperature Birch‐Murnaghan equation of state (EoS) and thermal EoS based on the Mie‐Gruneisen‐Debye model of thebccandhcpstructures are consistent with, and complement the literature data at higher pressures. The calculated densities based on the thermal EoS of Fe‐9wt.%Si indicate that bothbccandhcpphases agree with the reported core density estimates for the Moon and Mercury. 
    more » « less
  • Citation Formats
  • MLA
  • APA
  • Chicago
  • BibTeX
  • Save / Share this Record
  • Send to Email