Perovskite materials, of which strontium titanate (STO) and its thin films are an example, have attracted significant scientific interest because of their desirable properties and the potential to tune thermal conductivity by employing several techniques. Notably, strontium titanate thin films on silicon (Si) substrates serve as a fundamental platform for integrating various oxides onto Si substrates, making it crucial to understand the thermal properties of STO on Si. This work investigates the thermal conductivity of STO thin films on an Si substrate for varying film thicknesses (12, 50, 80, and 200 nm) at room temperature (∼300 K). The thin films are deposited using molecular beam epitaxy on the Si substrate and their thermal conductivity is characterized using the frequency domain thermoreflectance (FDTR) method. The measured values range from 7.4 ± 0.74 for the 200 nm thick film to 0.8 ± 0.1 W m−1 K−1 for the 12 nm thick film, showing a large effect of the film thickness on the thermal conductivity values. The trend of the values is diminishing with the corresponding decrease in the thin film thickness, with a reduction of 38%–93% in the thermal conductivity values, for film thicknesses ranging from 200 to 12 nm. This reduction in the values is relative to the bulk single crystal values of STO, which may range from 11 to 13.5 W m−1 K−1 [Yu et al., Appl. Phys. Lett. 92, 191911 (2008) and Fumega et al., Phys. Rev. Mater. 4, 033606 (2020)], as measured by our FDTR-based experiment. The study also explores the evaluation of volumetric heat capacity (Cp). The measured volumetric heat capacity for the 200 nm thin film is 3.07 MJ m−3 K−1, which is in reasonable agreement with the values available in the literature.
more »
« less
High thermal conductivity and ultrahigh thermal boundary conductance of homoepitaxial AlN thin films
Wurtzite aluminum nitride (AlN) has attracted increasing attention for high-power and high-temperature operations due to its high piezoelectricity, ultrawide-bandgap, and large thermal conductivity k. The k of epitaxially grown AlN on foreign substrates has been investigated; however, no thermal studies have been conducted on homoepitaxially grown AlN. In this study, the thickness dependent k and thermal boundary conductance G of homoepitaxial AlN thin films were systematically studied using the optical pump–probe method of frequency-domain thermoreflectance. Our results show that k increases with the thickness and k values are among the highest reported for film thicknesses of 200 nm, 500 nm, and 1 μm, with values of 71.95, 152.04, and 195.71 W/(mK), respectively. Our first-principles calculations show good agreement with our measured data. Remarkably, the G between the epilayer and the substrate reported high values of 328, 477, 1180, and 2590 MW/(m2K) for sample thicknesses of 200 nm, 500 nm, 1 μm, and 3 μm, respectively. The high k and ultrahigh G of homoepitaxially grown AlN are very promising for efficient heat dissipation, which helps in device design and has advanced applications in micro-electromechanical systems, ultraviolet photonics, and high-power electronics.
more »
« less
- Award ID(s):
- 1719875
- PAR ID:
- 10594603
- Publisher / Repository:
- American Institute of Physics
- Date Published:
- Journal Name:
- APL Materials
- Volume:
- 10
- Issue:
- 1
- ISSN:
- 2166-532X
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Gallium nitride (GaN)-based high electron mobility transistors (HEMTs) are essential components in modern radio frequency power amplifiers. In order to improve both the device electrical and thermal performance (e.g., higher current density operation and better heat dissipation), researchers are introducing AlN into the GaN HEMT structure. The knowledge of thermal properties of the constituent layers, substrates, and interfaces is crucial for designing and optimizing GaN HEMTs that incorporate AlN into the device structure as the barrier layer, buffer layer, and/or the substrate material. This study employs a multi-frequency/spot-size time-domain thermoreflectance approach to measure the anisotropic thermal conductivity of (i) AlN and GaN epitaxial films, (ii) AlN and SiC substrates, and (iii) the thermal boundary conductance for GaN/AlN, AlN/SiC, and GaN/SiC interfaces (as a function of temperature) by characterizing GaN-on-SiC, GaN-on-AlN, and AlN-on-SiC epitaxial wafers. The thermal conductivity of both AlN and GaN films exhibits an anisotropy ratio of ∼1.3, where the in-plane thermal conductivity of a ∼1.35 μm thick high quality GaN layer (∼223 W m−1 K−1) is comparable to that of bulk GaN. A ∼1 μm thick AlN film grown by metalorganic chemical vapor deposition possesses a higher thermal conductivity than a thicker (∼1.4 μm) GaN film. The thermal boundary conductance values for a GaN/AlN interface (∼490 MW m-2 K−1) and AlN/SiC interface (∼470 MW m−2 K−1) are found to be higher than that of a GaN/SiC interface (∼305 MW m−2 K−1). This work provides thermophysical property data that are essential for optimizing the thermal design of AlN-incorporated GaN HEMT devices.more » « less
-
Abstract High thermal conductivity electronic materials are critical components for high-performance electronic and photonic devices as both active functional materials and thermal management materials. We report an isotropic high thermal conductivity exceeding 500 W m −1 K −1 at room temperature in high-quality wafer-scale cubic silicon carbide (3C-SiC) crystals, which is the second highest among large crystals (only surpassed by diamond). Furthermore, the corresponding 3C-SiC thin films are found to have record-high in-plane and cross-plane thermal conductivity, even higher than diamond thin films with equivalent thicknesses. Our results resolve a long-standing puzzle that the literature values of thermal conductivity for 3C-SiC are lower than the structurally more complex 6H-SiC. We show that the observed high thermal conductivity in this work arises from the high purity and high crystal quality of 3C-SiC crystals which avoids the exceptionally strong defect-phonon scatterings. Moreover, 3C-SiC is a SiC polytype which can be epitaxially grown on Si. We show that the measured 3C-SiC-Si thermal boundary conductance is among the highest for semiconductor interfaces. These findings provide insights for fundamental phonon transport mechanisms, and suggest that 3C-SiC is an excellent wide-bandgap semiconductor for applications of next-generation power electronics as both active components and substrates.more » « less
-
In this paper, we demonstrate a method of measuring the flexural elastic modulus of ceramics at an intermediate (~millimeter) scale at high temperatures. We used a picosecond laser to precisely cut microbeams from the location of interest in a bulk ceramic. They had a cross-section of approximately 100 μm × 300 μm and a length of ~1 cm. They were then tested in a thermal mechanical analyzer at room temperature, 500 °C, 800 °C, and 1100 °C using the four-point flexural testing method. We compared the elastic moduli of high-purity Al2O3 and AlN measured by our method with the reported values in the literature and found that the difference was less than 5% for both materials. This paper provides a new and accurate method of characterizing the high-temperature elastic modulus of miniature samples extracted from representative/selected areas of bulk materials.more » « less
-
Epitaxial ScxAl1−xN thin films of ∼100 nm thickness grown on metal polar GaN substrates are found to exhibit significantly enhanced relative dielectric permittivity (εr) values relative to AlN. εrvalues of ∼17–21 for Sc mole fractions of 17%–25% ( x = 0.17–0.25) measured electrically by capacitance–voltage measurements indicate that ScxAl1−xN has the largest relative dielectric permittivity of any existing nitride material. Since epitaxial ScxAl1−xN layers deposited on GaN also exhibit large polarization discontinuity, the heterojunction can exploit the in situ high-K dielectric property to extend transistor operation for power electronics and high-speed microwave applications.more » « less
An official website of the United States government