We have carried out joint theoretical and experimental investigations of three Heusler compounds CoMoFeAl, CoMo0.5Fe1.5Al, and Co1.5Mo0.5FeAl. Our first-principle calculations show that all three compounds show either ferro- or ferrimagnetic order with CoMoFeAl and CoMo0.5Fe1.5Al exhibiting high spin polarization of almost 80%. The investigated samples were prepared using arc melting and high vacuum annealing. All the samples show cubic crystal structure with disorder. The parent compound CoMoFeAl shows a small saturation magnetization of 12 emu/g, and a Curie temperature of 440 K. The other two compounds, namely, Co1.5Mo0.5FeAl and CoMo0.5Fe1.5Al, show much higher saturation magnetizations of 62 emu/g and 59 emu/g, and substantially higher Curie temperatures of 950 K and 780 K, respectively.
more »
« less
Magnetocrystalline anisotropy of interstitially and substitutionally Sn-doped MnBi for high temperature permanent magnet applications
First-principles calculations were performed to calculate the electronic structures of low temperature phase (LTP) MnBi (Mn50Bi50) and substitutionally and interstitially Sn-doped MnBi [Mn50Bi25Sn25, (Mn0.5Bi0.5)66.7Sn33.3]. Brillouin function predicts the temperature dependence of saturation magnetization M(T). Sn substitution for Bi in MnBi (Mn50Bi25Sn25) changes the magnetocrystalline anisotropy constant (Ku) from −0.202 MJ/m3 (the in-plane magnetization) for LTP MnBi to 1.711 MJ/m3 (the out-of-plane magnetization). In comparison, the Ku remains negative but slightly decreases to −0.043 MJ/m3 when Sn is interstitially doped in MnBi [(Mn0.5Bi0.5)66.7Sn33.3]. The Curie temperature (TC) decreases from 716 K for LTP Mn50Bi50 to 445 K for Mn50Bi25Sn25 and 285 K for (Mn0.5Bi0.5)66.7Sn33.3. Mn50Bi25Sn25 has a lower magnetic moment of 5.034 μB/f.u. but a higher saturation magnetization of 64.2 emu/g than (Mn0.5Bi0.5)66.7Sn33.3 with a magnetic moment of 6.609 μB/f.u. and a saturation magnetization of 48.2 emu/g because the weight and volume of the substitutionally Sn-doped MnBi are smaller than the interstitially Sn-doped MnBi. The low Curie temperature and magnetization for Sn-doped MnBi are attributed to the high concentration of Sn. Thus, future study needs to focus on low Sn-concentrated MnBi.
more »
« less
- Award ID(s):
- 2137275
- PAR ID:
- 10597217
- Publisher / Repository:
- American Institute of Physics
- Date Published:
- Journal Name:
- AIP Advances
- Volume:
- 13
- Issue:
- 10
- ISSN:
- 2158-3226
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
We have carried out a combined theoretical and experimental investigation of both stoichiometric and nonstoichiometric CoFeVGe alloys. In particular, we have investigated CoFeVGe, Co1.25Fe0.75VGe, Co0.75Fe1.25VGe, and CoFe0.75VGe bulk alloys. Our first principles calculations suggest that all four alloys show ferromagnetic order, where CoFeVGe, Co1.25Fe0.75VGe, and Co0.75Fe1.25VGe are highly spin polarized with spin polarization values of over 80%. However, the spin polarization value of CoFe0.75VGe is only about 60%. We have synthesized all four samples using arc melting and high-vacuum annealing at 600 °C for 48 hours. The room temperature x-ray diffraction of these samples exhibits a cubic crystal structure with disorder. All the samples show single magnetic transitions at their Curie temperatures, where the Curie temperature and high field (3T) magnetization are 288 K and 42 emu/g; 305 K and 1.5 emu/g; 238 K and 39 emu/g; and 306 K and 35 emu/g for CoFeVGe, Co1.25Fe0.75VGe, Co0.75Fe1.25VGe, and CoFe0.75VGe, respectively.more » « less
-
We have stabilized epitaxial oxide thin films of transparent, magnetic Ru-doped BaSnO3. Films were grown by pulsed laser deposition and exhibited excellent epitaxy and crystallinity as determined by x-ray diffraction. Epitaxial films of Ru doped BaSnO3 were grown with a ceramic target of nominally 4% Ru doping on the Sn site but resulted in 3% Ru doping in the lms. Paramagnetic behavior is observed in all lms with a Curie law dependence on temperature. The field dependence of the magnetization shows a paramagnetic moment that saturates at a value consistent with low spin Ru. Films are also found to be transparent in the visible regime. Together these results demonstrate the realization of highly crystalline, transparent, paramagnetic,epitaxial doped BaSnO3 films.more » « less
-
The intermetallic compound LiMnBi was synthesized by the two-step solid-state reaction from the elements. A synthesis temperature of 850 K was selected based on in situ high-temperature powder X-ray diffraction data. LiMnBi crystalizes in the layered-like PbClF structure type (a = 4.3131(7) Å, c = 7.096(1) Å at 100 K, P4/nmm space group, Z = 2). The LiMnBi structure is built of alternating [MnBi] and Li layers, as determined from single-crystal X-ray diffraction data. Magnetic property measurements and solid-state 7Li nuclear magnetic resonance data collected for polycrystalline LiMnBi samples indicate the long-range antiferromagnetic ordering of the Mn sublattice at ∼340 K, with no superconductivity detected down to 5 K. LiMnBi is air- and water-sensitive. Under aerobic conditions, Li can be extracted from the LiMnBi structure to form Li2O/LiOH and MnBi (NiAs structure type, P63/mmc). The obtained MnBi polymorph was previously reported to be one of the strongest rare-earth-free ferromagnets, yet its bulk synthesis in powder form is cumbersome. The proposed magneto-structural transformation from ternary LiMnBi to ferromagnetic MnBi involves condensation of the MnBi4 tetrahedra upon Li deintercalation and is exclusive to LiMnBi. In contrast, ferromagnetic MnBi cannot be obtained from either isostructural NaMnBi and KMnBi or from the structurally related CaMn2Bi2. Such a distinctive transformation in the case of LiMnBi is presumed to be due to its fitting reactivity to yield MnBi and a favorable interlayer distance between [MnBi] layers, while the interlayer distance in NaMnBi and KMnBi structural analogues is unfavorably long. The studies of delithiation from layered-like LiMnBi under different chemical environments indicate that the yield of MnBi depends on the type of solvent used and the kinetics of the reaction. A slow rate and mild reaction media lead to a high fraction of the MnBi product. The saturation magnetization of the “as-prepared” MnBi is ∼50% of the expected value of 81.3 emu/g. Overall, this study adds a missing member to the family of ternary pnictides and illustrates how soft-chemistry methods can be used to obtain “difficult-to-synthesize” compounds.more » « less
-
Because of the importance of ferromagnetism at room temperature, we search for new materials that can exhibit a non-vanishing magnetic moment at room temperature and at the same time can be used in spintronics. The experimental results indicate that d 0 ferromagnetism without any magnetic impurities takes place in PbS films made of close-packed lead sulfide nanoparticles of 30 nm. To explain the existence of the d 0 ferromagnetism, we propose a model where various PbS bulk and surface configurations of Pb-vacancies are analyzed. The bulk configurations have a zero magnetic moment while the two surface configurations with Pb vacancies with the same non-vanishing magnetic moments and lowest ground state energies contribute to the total magnetization. Based on the experimental value of the saturation magnetization, 0.2 emu g −1 , we have found that the calculated Pb vacancy concentration should be about 3.5%, which is close to typical experimental values. Besides being very important for applications, there is one feature of PbS d 0 ferromagnetism that makes this material special for fundamental research: PbS ferromagnetism can exhibit topologically driven spatial magnetic moment distributions ( e.g. , magnetic skyrmions) due to large spin–orbit coupling.more » « less