Magnetic nanocomposites with 0-3 connectivity, whereby a 0D magnetic nanoparticle phase is embedded into a 3D magnetic metal matrix phase, have gained increased interest for use in applications ranging from integrated power inductor cores to exchange-spring magnets. The electro-infiltration process, in which a metal phase is electroplated through a nanoparticle film phase, is an inexpensive approach compatible with semiconductor fabrication methods for the formation of these nanocomposites. Past demonstrations of electro-infiltrated nanocomposites have relied on scanning electron microscopy and energy dispersive x-ray spectroscopy to evaluate the 0-3 composite structure. However, a detailed investigation of the boundary between the particle and metal matrix phases cannot be performed with these tools, and it is unknown whether the particle/matrix interfaces are dense and void-free. This detail is critical, as the presence of even nanoscale voids would affect any potential magnetic exchange coupling and hence the overall electromagnetic properties of the material. This work seeks to explore the phase boundary of 0-3 magnetic nanocomposite fabricated by electro-infiltration by using scanning transmission electron microscopy and energy-dispersive x-ray spectroscopy to analyze the nanostructure of two different composites—a nickel/iron-oxide composite and a permalloy/iron-oxide composite. High-resolution imaging indicates that the interface between the particle phase and matrix phase is dense and void-free. These results will help guide future studies on the design and implementation of these magnetic nanocomposites for end applications.
more »
« less
Electrophoretic deposition of iron oxide nanoparticles to achieve thick nickel/iron oxide magnetic nanocomposite films
For modern switching power supplies, current bulk magnetic materials, such as ferrites or magnetic metal alloys, cannot provide both low loss and high magnetic saturation to function with both high power density and high efficiency at high frequencies (10-100 MHz). Magnetic nanocomposites comprised of a ferrite and magnetic metal alloy provide the opportunity to achieve these desired magnetic properties, but previously investigated thin-film fabrication techniques have difficulty achieving multi-micrometer film thicknesses which are necessary to provide practical magnetic energy storage and power handling. Here, we present a versatile technique to fabricate thick magnetic nanocomposites via a two-step process, consisting of the electrophoretic deposition of an iron oxide nanoparticle phase into a mold on a substrate, followed by electro-infiltration of a nickel matrix. The deposited films are imaged via scanning electron microscopy and energy dispersive X-ray spectroscopy to identify the presence of iron and nickel, confirming the infiltration of the nickel between the iron oxide nanoparticles. A film thickness of ∼7 μm was measured via stylus profilometry. Further confirmation of successful composite formation is obtained with vibrating sample magnetometry, showing the saturation magnetization value of the composite (473 kA/m) falls between that of the iron oxide nanoparticles (280 kA/m) and the nickel matrix (555 kA/m). These results demonstrate the potential of electrophoretic deposition coupled with electro-infiltration to fabricate magnetic nanocomposite films.
more »
« less
- Award ID(s):
- 1727930
- PAR ID:
- 10597487
- Publisher / Repository:
- American Institute of Physics
- Date Published:
- Journal Name:
- AIP Advances
- Volume:
- 10
- Issue:
- 1
- ISSN:
- 2158-3226
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
null (Ed.)Incorporating nanoparticles into devices for a wide range of applications often requires the formation of thick films, which is particularly necessary for improving magnetic power storage, microwave properties, and sensor performance. One approach to assembling nanoparticles into films is the use of electrophoretic deposition (EPD). This work seeks to develop methods to increase film thickness and stability in EPD by increasing film-substrate interactions via functionalizing conductive substrates with various chelating agents. Here, we deposited iron oxide nanoparticles onto conductive substrates functionalized with three chelating agents with different functional moieties and differing chelating strengths. We show that increasing chelating strength can increase film-substrate interactions, resulting in thicker films when compared to traditional EPD. Results will also be presented on how the chelating strength relates to film formation as a function of deposition conditions. Yield for EPD is influenced by deposition conditions including applied electric field, particle concentration, and deposition time. This work shows that the functionalization of substrates with chelating agents that coordinate strongly with nanoparticles (phosphonic acid and dopamine) overcome parameters that traditionally hinder the deposition of thicker and more stable films, such as applied electric field and high particle concentration. We show that functionalizing substrates with chelating agents is a promising method to fabricate thick, stable films of nanoparticles deposited via EPD over a larger processing space by increasing film-substrate interactions.more » « less
-
Abstract Flexible nanocomposite films, with cobalt ferrite nanoparticles (CFN) as the ferromagnetic component and polyvinylidene fluoride–trifluoroethylene (PVDF-TrFE) copolymer as the ferroelectric matrix, were fabricated using a blade coating technique. Nanocomposite films were prepared using a two-step process; the first process involves the synthesis of cobalt ferrite (CoFe2O4) nanoparticles using a sonochemical method, and then incorporation of various weight percentages (0, 2.5, 5, and 10%) of cobalt ferrite nanoparticles into the PVDF-TrFE to form nanocomposites. The ferroelectric polarβphase of PVDF-TrFE was confirmed by x-ray diffraction (XRD). Thermal studies of films showed notable improvement in the thermal properties of the nanocomposite films with the incorporation of nanoparticles. The ferroelectric properties of the pure polymer/composite films were studied, showing a significant improvement of maximum polarization upon 5wt% CFN loading in PVDF-TrFE composite films compared to the PVDF-TrFE film. The magnetic properties of as-synthesized CFN and the polymer nanocomposites were studied, showing a magnetic saturation of 53.7 emu g−1at room temperature, while 10% cobalt ferrite-(PVDF-TrFE) nanocomposite shows 27.6 emu/g. We also describe a process for fabricating high optical quality pure PVDF-TrFE and pinhole-free nanocomposite films. Finally, the mechanical studies revealed that the mechanical strength of the films increases up to 5 wt% loading of the nanoparticles in the copolymer matrix and then decreases. This signifies that the obtained films could be suited for flexible electronics.more » « less
-
Bacterial cellulose nanocrystals (BCNCs) are biocompatible cellulose nanomaterials that can host guest nanoparticles to form hybrid nanocomposites with a wide range of applications. Herein, we report the synthesis of a hybrid nanocomposite that consists of plasmonic gold nanoparticles (AuNPs) and superparamagnetic iron oxide (Fe 3 O 4 ) nanoparticles supported on BCNCs. As a proof of concept, the hybrid nanocomposites were employed to isolate and detect malachite green isothiocyanate (MGITC) via magnetic separation and surface-enhanced Raman scattering (SERS). Different initial gold precursor (Au 3+ ) concentrations altered the size and morphology of the AuNPs formed on the nanocomposites. The use of 5 and 10 mM Au 3+ led to a heterogenous mix of spherical and nanoplate AuNPs with increased SERS enhancements, as compared to the more uniform AuNPs formed using 1 mM Au 3+ . Rapid and sensitive detection of MGITC at concentrations as low as 10 −10 M was achieved. The SERS intensity of the normalized Raman peak at 1175 cm −1 exhibited a log-linear relationship for MGITC concentrations between 2 × 10 −10 and 2 × 10 −5 M for Au@Fe 3 O 4 @BCNCs. These results suggest the potential of these hybrid nanocomposites for application in a broad range of analyte detection strategies.more » « less
-
Iron oxide nanomaterials participate in redox processes that give them ideal properties for their use as earth-abundant catalysts. Fabricating nanocatalysts for such applications requires detailed knowledge of the deposition and growth. We report the spontaneous deposition of iron oxide nanoparticles on HOPG in defect areas and on step edges from a metal precursor solution. To study the nucleation and growth of iron oxide nanoparticles, tailored defects were created on the surface of HOPG using various ion sources that serve as the target sites for iron oxide nucleation. After solution deposition and annealing, the iron oxide nanoparticles were found to nucleate and coalesce at 400 °C. AFM revealed that the particles on the sp 3 carbon sites enabled the nanoparticles to aggregate into larger particles. The iron oxide nanoparticles were characterized as having an Fe 3+ oxidation state and two different oxygen species, Fe–O and Fe–OH/Fe–OOH, as determined by XPS. STEM imaging and EDS mapping confirmed that the majority of the nanoparticles grown were converted to hematite after annealing at 400 °C. A mechanism of spontaneous and selective deposition on the HOPG surface and transformation of the iron oxide nanoparticles is proposed. These results suggest a simple method for growing nanoparticles as a model catalyst.more » « less