skip to main content
US FlagAn official website of the United States government
dot gov icon
Official websites use .gov
A .gov website belongs to an official government organization in the United States.
https lock icon
Secure .gov websites use HTTPS
A lock ( lock ) or https:// means you've safely connected to the .gov website. Share sensitive information only on official, secure websites.

Explore Research Products in the PAR
It may take a few hours for recently added research products to appear in PAR search results.


This content will become publicly available on May 25, 2026

Title: Powder spreading behavior of bimodal ceramics in the binder jetting process
Binder jetting (BJT) has been extensively explored for additive manufacturing of ceramics due to its ability to create complex structures by processing refractory and hard-to-machine materials. However, achieving a uniform powder bed with high packing density while processing ceramics in BJT remains a challenge. This study systematically examines the role of powder size, powder temperature, flow behavior, and powder size distribution on powder bed formation and resulting part properties. Four different alumina powder sizes (1 μm, 5 μm, 10 μm, and 20 μm) were investigated. Flowability characterizations reveal that 1 μm powder remains poorly flowable at both room and elevated temperatures, while 20 μm powder demonstrates excellent flowability at both temperatures. Smaller powders, especially 1 μm, exhibit around 25% loss in moisture, which results in pronounced agglomeration at room temperature. Discrete element method simulations were used to identify the ideal mixing ratio of the bimodal powder using 5 μm and 20 μm powders. For bimodal powder, both the simulation and the experiments exhibited a preferential deposition of smaller powders in the spreading direction. However, the 5 μm and 20 μm powders did not show any preferential deposition in the simulation, but experiments showed preferential deposition behavior. When using bimodal powder, packing density decreases by 7.65% along the spreading direction, which aligns with an 8.19% drop in part relative density. These findings offer valuable insights into the effects of bimodal powder distribution for controlling powder bed packing density and potentially leveraging spatial density variations for functional applications such as biomedical implants, heat exchangers, and gas filtration.  more » « less
Award ID(s):
1944120
PAR ID:
10623682
Author(s) / Creator(s):
; ; ; ;
Publisher / Repository:
AccScience Publishing
Date Published:
Journal Name:
Materials Science in Additive Manufacturing
Volume:
4
Issue:
2
ISSN:
2810-9635
Page Range / eLocation ID:
025110016
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. ; (, Discrete-Element Simulation of Powder Spreading Process in Binder Jetting, and the Effects of Powder Size)
    null (Ed.)
    Binder Jetting has gained particular interest amongst Additive Manufacturing (AM) techniques because of its wide range of applications, broader feasible material systems, and absence of rapid melting-solidification issues present in other AM processes. Understanding and optimizing printing parameters during the powder spreading process is essential to improve the quality of the final part. In this study, a Discrete Element Method (DEM) simulation is employed to evaluate the powder packing density, flowability, and porosity during powder spreading process utilizing three different powder groups. Two groups are formed with monoidal size distributions (75–84 μm and 100–109 μm), and the third one consisting of a bimodal distribution (50 μm + 100 μm). A thorough investigation into the effects of powder size distribution during the powder spreading step in a binder jetting process is conducted using ceramic foundry sand. It was observed that coarser particles result in higher flowability (62% decrease in repose angle) than finer ones due to the cohesion effect present in the latter. A bimodal size distribution yields the highest packing density (8% increase) and lowest porosity (∼12% reduction) in the powder bed, as the finer particles fill in the voids created between the coarser ones. Findings from this study are directly applicable to binder-jetting AM process, and also offer new insights for AM powder manufacturers. 
    more » « less
  2. ; ; ; ; ; (, Journal of Manufacturing Science and Engineering)
    null (Ed.)
    Abstract This paper reports a study on the effects of particle size distribution (tuned by mixing different-sized powders) on density of a densely packed powder, powder bed density, and sintered density in binder jetting additive manufacturing. An analytical model was used first to study the mixture packing density. Analytical results showed that multimodal (bimodal or trimodal) mixtures could achieve a higher packing density than their component powders and there existed an optimal mixing fraction to achieve the maximum mixture packing density. Both a lower component particle size ratio (fine to coarse) and a larger component packing density ratio (fine to coarse) led to a larger maximum mixture packing density. A threshold existed for the component packing density ratio, below which the mixing method was not effective for density improvement. Its relationship to the component particle size ratio was calculated and plotted. In addition, the dependence of the optimal mixing fraction and maximum mixture packing density on the component particle size ratio and component packing density ratio was calculated and plotted. These plots can be used as theoretical tools to select parameters for the mixing method. Experimental results of tap density were consistent with the above-mentioned analytical predictions. Also, experimental measurements showed that powders with multimodal particle size distributions achieved a higher tap density, powder bed density, and sintered density in most cases. 
    more » « less
  3. ; ; ; ; (, Journal of Manufacturing Science and Engineering)
    Abstract Binder jetting is an additive manufacturing process utilizing a liquid-based binding agent to selectively join the material in a powder bed. It is capable of manufacturing complex-shaped parts from a variety of materials including metals, ceramics, and polymers. This paper provides a comprehensive review on currently available reports on metal binder jetting from both academia and industry. Critical factors and their effects in metal binder jetting are reviewed and divided into two categories, namely material-related factors and process-related parameters. The reported data on density, dimensional and geometric accuracy, and mechanical properties achieved by metal binder jetting are summarized. With parameter optimization and a suitable sintering process, ten materials have been proven to achieve a relative density of higher than 90%. Indepth discussion is provided regarding densification as a function of various attributes of powder packing, printing, and post-processing. A few grades of stainless steel obtained equivalent or superior mechanical properties compared to cold working. Although binder jetting has gained its popularity in the past several years, it has not been sufficiently studied compared with other metal additive manufacturing (AM) processes such as powder bed fusion and directed energy deposition. Some aspects that need further research include the understanding of powder spreading process, binder-powder interaction, and part shrinkage. 
    more » « less
  4. ; ; ; (, Journal of Micro and Nano-Manufacturing)
    Abstract Feedstock powders used in binder jetting additive manufacturing include nanopowder, micropowder, and granulated powder. Two important characteristics of the feedstock powders are flowability and sinterability. This paper aims to compare the flowability and sinterability of different feedstock powders. Three powders were compared: nanopowder (with a particle size of ∼100 nm), micropowder (with a particle size of 70 μm), and granulated powder (with a granule size of ∼70 μm) made from the nanopowder by spray freeze drying. Flowability metrics employed included apparent density (AD), tap density (TD), volumetric flow rate (VFR), mass flow rate (MFR), Hausner ratio (HR), Carr index (CI), and repose angle (RA). Sinterability metrics employed included sintered bulk density (SBD), volumetric shrinkage (VS), and densification ratio (DR). Results show that the granulated powder has a higher flowability than the nanopowder and a higher sinterability than the micropowder. Moreover, different flowability metric values of the granulated powder are close to those of the micropowder, indicating that these two powers have a comparably high flowability. Similarly, different sinterability metric values of the granulated powder are close to those of the nanopowder, indicating that these two powders have a comparably high sinterability. 
    more » « less
  5. ; ; ; ; ; (, Powder Metallurgy)
    In the binder jetting (BJ) process, as in most of powder bed additive manufacturing technologies, the powder is periodically recoated onto the substrate layer-by-layer. The elements of the current deposited layer corresponding to the part being manufactured are bonded together using a polymeric binder. In all cases that require a thermal process for sintering, the internal structure of the finished part is defined by the internal structure of the powder bed. This article focuses on the discrete element modelling (DEM) of various powder spreading methods during recoating and their impact on the powder bed structure particularly applied to binder jetting technology. The article demonstrates that despite the thinness of the deposited layers, they typically exhibit porosity and particle and pore size non-uniformities along the build-up direction. These irregularities contribute to the anisotropic sintering shrinkage observed in green BJ bodies during experiments. However, the experiments presented confirmed by modelling show that without binder deposition, the powder bed – except for a narrow surface layer – remains relatively uniform, regardless of the recoating method used. It is the binder injection into the porous structure of the powder bed that disrupts this homogeneity, locks in large surface pores, and exacerbates the effects of powder segregation during spreading. Finally, several strategies, explored via simulation, are proposed to reduce porosity variations during BJ: using a combined roller-wide blade method for powder spreading and a two-hopper approach, where each layer consists of small particles deposited over larger ones. 
    more » « less
  • Citation Formats
  • MLA
  • APA
  • Chicago
  • BibTeX
  • Save / Share this Record
  • Send to Email