Abstract Microbially-induced calcium carbonate precipitation (MICP) is a biological process in which microbially-produced urease enzymes convert urea and calcium into solid calcium carbonate (CaCO3) deposits. MICP has been demonstrated to reduce permeability in shale fractures under elevated pressures, raising the possibility of applying this technology to enhance shale reservoir storage safety. For this and other applications to become a reality, non-invasive tools are needed to determine how effectively MICP seals shale fractures at subsurface temperatures. In this study, two different MICP strategies were tested on 2.54 cm diameter and 5.08 cm long shale cores with a single fracture at 60 ℃. Flow-through, pulsed-flow MICP-treatment was repeatedly applied to Marcellus shale fractures with and without sand (“proppant”) until reaching approximately four orders of magnitude reduction in apparent permeability, while a single application of polymer-based “immersion” MICP-treatment was applied to an Eagle Ford shale fracture with proppant. Low-field nuclear magnetic resonance (LF-NMR) and X-Ray computed microtomography (micro-CT) techniques were used to assess the degree of biomineralization. With the flow-through approach, these tools revealed that while CaCO3precipitation occurred throughout the fracture, there was preferential precipitation around proppant. Without proppant, the same approach led to premature sealing at the inlet side of the core. In contrast, immersion MICP-treatment sealed off the fracture edges and showed less mineral precipitation overall. This study highlights the use of LF-NMR relaxometry in characterizing fracture sealing and can help guide NMR logging tools in subsurface remediation efforts.
more »
« less
Splitting tensile strength of shale cores: intact versus fractured and sealed with ureolysis-induced calcium carbonate precipitation (UICP)
Abstract Ureolysis-induced calcium carbonate precipitation (UICP) is a biomineral solution where the urease enzyme converts urea and calcium into calcium carbonate. The resulting biomineral can bridge gaps in fractured shale, reduce undesired fluid flow, limit fracture propagation, better store carbon dioxide, and potentially enhance well efficiency. The mechanical properties of shale cores were investigated using a modified Brazilian indirect tensile strength test. An investigation of intact shale using Eagle Ford and Wolfcamp cores was conducted at varying temperatures. Results show no significant difference between shale types (average tensile strength = 6.19 MPa). Eagle Ford displayed higher strength at elevated temperature, but temperature did not influence Wolfcamp. Comparatively, cores with a single, lengthwise heterogeneous fracture were sealed with UICP and further tested for tensile strength. UICP was delivered via a flow-through method which injected 20–30 sequential patterns of ureolytic microorganisms and UICP-promoting fluids into the fracture until permeability reduced by three orders of magnitude or with an immersion method which placed cores treated with guar gum and UICP-promoting fluids into a batch reactor, demonstrating that guar gum is a suitable inclusion and may reduce the number of flow-through injections required. Tensile results for both delivery methods were variable (0.15–8 MPa), and in some cores the biomineralized fracture split apart, possibly due to insufficient sealing and/or heterogeneity in the composite UICP-shale cores. Notably in other cores the biomineralized fracture remained intact, demonstrating more cohesion than the surrounding shale, indicating that UICP may produce a strong seal for subsurface application.
more »
« less
- Award ID(s):
- 2125748
- PAR ID:
- 10629412
- Publisher / Repository:
- Springer
- Date Published:
- Journal Name:
- Geomechanics and Geophysics for Geo-Energy and Geo-Resources
- Volume:
- 10
- Issue:
- 1
- ISSN:
- 2363-8419
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Abstract Common adhesives for nonstructural applications are manufactured using petrochemicals and synthetic solvents. These adhesives are associated with environmental and health concerns because of their release of volatile organic compounds (VOCs). Biopolymer adhesives are an attractive alternative because of lower VOC emissions, but their strength is often insufficient. Existing mineral fillers can improve the strength of biopolymer adhesives but require the use of crosslinkers that lower process sustainability. This work introduces a novel approach to strengthen biopolymer adhesives through calcium carbonate biomineralization, which avoids the need for crosslinkers. Biomineral fillers produced by either microbially or enzymatically induced calcium carbonate precipitation (MICP and EICP, respectively) were precipitated within guar gum and soy protein biopolymers. Both, MICP and EICP, increased the strength of the biopolymer adhesives. The strength was further improved by optimizing the concentrations of bacteria, urease enzyme, and calcium. The highest strengths achieved were on par with current commercially available nonstructural adhesives. This study demonstrates the feasibility of using calcium carbonate biomineralization to improve the properties of biopolymer adhesives, which increases their potential viability as more sustainable adhesives.more » « less
-
ABSTRACT:This study investigates the distinction between unreacted shale samples and those exposed to CO2-rich brine under elevated temperature (100°C) and pressure (1800 psi) conditions over 28 days. Samples underwent scratch testing under constant loading to ensure independent penetration depth, circumventing variability associated with load-dependent outcomes prevalent in progressive loading methodologies. Vertical hardness profiles revealed significant variations between reacted and unreacted regions, influenced by differential dissolution and precipitation characteristics, while horizontal hardness provided limited insights, particularly in the reacted region where higher tangential forces and deeper scratches indicated greater material compressibility. Distinct scratch path variations were observed, with fractures absent in the ductile reacted region at lower testing forces. The shale samples were sourced from the Eagle Ford Formation, providing insights into the mechanical response of carbonate-rich shale rocks in extreme environments. This research enhances understanding of shale's mechanical properties and material responses under diverse operational conditions, elucidating interactions with influential environmental factors, particularly in CO2-exposed scenarios. Conducted at a microscale level, this study offers detailed insights into material behavior, crucial for predicting long-term stability of geostructures exposed to reactive brine and potential CO2 leakage in subsurface reservoirs. 1. INTRODUCTIONThe investigation into chemical interactions between carbonate rocks and acidic brine is cruical for understanding complex mechanical and microstructural transformations essential for applications like geostructure stability, CO2 storage, and energy exploitation. Under elevated pressure and temperature conditions, the equilibrium between injected fluids and rocks undergoes alterations, leading to geochemical responses, especially with the presence of CO2 as a supercritical phase or in aqueous form (Prakash et al. 2023a; Prakash et al. 2022). In this context, investigating fracture properties becomes essential, aiming to comprehend the development and propagation of fractures within reacted formations to evaluate structural integrity and potential pathways for fluid migration.Prior geochemical investigations have explored the localized repercussions of CO2 attacks on rock permeability, shedding light on alterations attributed to carbonate precipitation sealing fractures and pores or the dissolution of diverse minerals (Burnside et al. 2013; Minardi et al. 2021). Shale rocks exposed to acidic brine predominantly undergo carbonate reactions, particularly carbonates dissolution and precipitation (Prakash et al., 2022; Prakash et al. 2023b). Experimental studies on fracture mechanics and mechanical properties have utilized conventional methods such as single edge notched bend, chevron notched beam, three-point bending, and semi-circular bending tests, acknowledging their inherent limitations (Smith & Chowdary, 1975; Bazant and Kazemi, 1990; Helmer et al. 2014; Dubey et al., 2020).more » « less
-
The emergence of engineered living materials (ELMs) has led to the development of functional composites by combining living microorganisms with nonliving components, particularly hydrogels. Hydrogels, which mimic the extracellular matrix, support microbial growth by providing essential nutrients and promoting cell adhesion, making them ideal for ELM production. However, hydrogel-based materials often face challenges in three-dimensional printing due to poor structural integrity and limited printability, frequently requiring additional processes, precise control, and/or material modifications to enhance their printing performance. This study focuses on developing a microorganism-laden gelatin microgel and gelatin solution-based composite bioink for self-supported printing of ELMs, enhanced via microbial-induced calcium carbonate precipitation. Gelatin microgels are utilized as rheology modifiers, enabling the yield-stress fluid behavior of the bioink for improved printability and postprinting shape retention, while transglutaminase enzymatically cross-links printed structures completely, resulting in good printability. Furthermore, Sporosarcina pasteurii in the bioink enables calcium carbonate deposition during postprinting culturing, forming robust, biomineralized structures. Fabricated samples are found to have significant successful mineral deposition with over 50 wt% calcium carbonate content, and they exhibit compressive strengths of up to 1.4 MPa. This approach offers a cost-effective, energy-efficient method for creating high-strength, biocompatible biocomposites with potential applications such as bone tissue engineering, coral restoration, and sustainable building development.more » « less
-
In this research study, the fracture strength of flat 10 mm thick annealed glass sheets having an abrasive water-jet cut surface and bearing against a transparent interface material is experimentally investigated. The transparent interface material is necessary to provide axial-compressive force continuity in modular compression-dominant all- glass shell structures. A series of short glass columns were tested in axial compression under a variety of load cases, which included cyclic, creep, and monotonic-to-fracture loading. A target glass fracture bearing stress of 36.6 MPa is identified and represents an upper bound bearing stress for annealed glass compression members failing in a flexural buckling mode. The study concludes the transparent thermoplastic material, known as Surlyn, was able to achieve a fracture strength that exceeds the target value and that the fracture strength is not affected by cyclic or creep loading. Consequently, column-related failure limit states will occur before glass fracture is associated with interface bearing. Glass fracture occurs in Type-I mode, reflecting the presence of interface tensile stress. Furthermore, the monotonic bearing stiffness in the service range of 5 to 15 MPa is increased by 20 % and 16 % for samples subjected to cyclic and creep loading, respectively, relative to monotonic-only samples.more » « less
- Free Publicly Accessible Full Text
-
Accepted Manuscript1.0
- Journal Article:
- https://doi.org/10.1007/s40948-024-00897-0