Abstract This study focuses on fabrication of aerogel-coated macroporous polyester fabrics for the purposes of filtration of nanometric airborne particles and potential application in facemasks. Syndiotactic polystyrene (sPS) and polyimide (PI) gels that provide respectively majority macropores (diameter > 50 nm) and mesopores (diameter 2 to 50 nm) are coated onto woven polyester fabrics via a dip coating process. The resultant materials are supercritically dried to obtain aerogelcoated fabrics. The results show that sPS is more suitable for the dip coating process. However, evaporation of the solvent during handling of gel-coated fabrics leads to closure of the surface pores that are later recovered via solvent annealing. The resultant aerogel-coated fabrics offer high air permeability (∼10 –10 m 2 ) and high filtration efficiency (> 99.95%) of airborne sodium chloride test particles of size 25 to 150 nm.
more »
« less
This content will become publicly available on March 1, 2026
Nanoparticle Air Filtration Using MXene-Coated Textiles
Nanoparticles with aerodynamic diameters of less than 100 nm pose serious problems to human health due to their small size and large surface area. Despite continuous progress in materials science to develop air remediation technologies, efficient nanoparticle filtration has appeared to be challenging. This study showcases the great promise of MXene-coated polyester textiles to efficiently filter nanoparticles, achieving a high efficiency of ~90% within the 15–30 nm range. Using alkaline earth metal ions to assist textile coating drastically improves the filter performance by ca. 25%, with the structure–property relationship thoroughly assessed by electron microscopy and X-ray computed tomography. Such techniques confirm metal ions’ crucial role in obtaining fully coated and impregnated textiles, which increases tortuosity and structural features that boost the ultimate filtration efficiency. Our work provides a novel perspective on using MXene textiles for nanoparticle filtration, presenting a viable alternative to produce high-performance air filters for real-world applications.
more »
« less
- Award ID(s):
- 2216175
- PAR ID:
- 10638498
- Publisher / Repository:
- MDPI Journal of Carbon Research
- Date Published:
- Journal Name:
- C
- Volume:
- 11
- Issue:
- 1
- ISSN:
- 2311-5629
- Page Range / eLocation ID:
- 13
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
null (Ed.)With the increased bacteria-induced hospital-acquired infections (HAIs) caused by bio-contaminated surfaces, the requirement for a safer and more efficient antibacterial strategy in designing personal protective equipment (PPE) such as N95 respirators is rising with urgency. Herein, a self-decontaminating nanofibrous filter with a high particulate matter (PM) filtration efficiency was designed and fabricated via a facile electrospinning method. The fillers implemented in the electrospun nanofibers were constructed by grafting a layer of antibacterial polymeric quaternary ammonium compound (QAC), that is, poly[2-(dimethyl decyl ammonium) ethyl methacrylate] (PQDMAEMA), onto the surface of metal–organic framework (MOF, UiO-66-NH 2 as a model) to form the active composite UiO-PQDMAEMA. The UiO-PQDMAEMA filter demonstrates an excellent PM filtration efficiency (>95%) at the most penetrating particle size (MPPS) of 80 nm, which is comparable to that of the commercial N95 respirators. Besides, the UiO-PQDMAEMA filter is capable of efficiently killing both Gram-positive ( S. epidermidis ) and Gram-negative ( E. coli ) airborne bacteria. The strong electrostatic interactions between the anionic cell wall of the bacteria and positively charged nitrogen of UiO-PQDMAEMA are the main reasons for severe cell membrane disruption, which leads to the death of bacteria. The present work provides a new avenue for combating air contamination by using the QAC-modified MOF-based active filters.more » « less
-
RationaleA two‐component matrix of 2‐nitrophloroglucinol (2‐NPG) and silica nanoparticles was used for matrix‐assisted laser desorption ionization (MALDI) mass spectrometry imaging of high‐charge‐state biomolecules in tissue. Potential advantages include increased effective mass range and efficiency of fragmentation. MethodsA mixture of 2‐NPG matrix and silica nanoparticles was applied to cyrosectioned 10 μm thick mouse brain tissue. The mixture was pipetted onto the tissue for profiling and sprayed for tissue imaging. MALDI images were obtained under high vacuum in a commercial time‐of‐flight mass spectrometer. ResultsThe combined 2‐NPG and nanoparticle matrix produced highly charged ions from tissue with high‐vacuum MALDI. Nanoparticles of 20, 70, 400, and 1000 nm in diameter were tested, the 20 nm particles producing the highest charge states. Images of mouse brain tissue obtained from highly charged ions show similar spatial localization. ConclusionsThe combined 2‐NPG and nanoparticle matrix produces highly charged ions from tissue through a mechanism that may rely on the high surface area of the particles which can dry the tissue, and their ability to bind analyte molecules thereby assisting in crystal formation and production of multiply charged ions on laser irradiation.more » « less
-
Abstract The emergence of the SARS‐CoV‐2 pandemic and airborne particulate matter (PM) pollution has led to remarkably high demand for face masks. However, conventional respirators are intended for single use and made from nondegradable materials, causing serious concern for a plastic‐waste environmental crisis. Furthermore, these facemasks are weakened in humid conditions and difficult to decontaminate. Herein, a reusable, self‐sustaining, highly effective, and humidity‐resistant air filtration membrane with excellent particle‐removal efficiency is reported, based on highly controllable and stable piezoelectric electrospun poly (l‐lactic acid) (PLLA) nanofibers. The PLLA filter possesses a high filtration efficiency (>99% for PM 2.5 and>91% for PM 1.0) while providing a favorable pressure drop (≈91 Pa at normal breathing rate) for human breathing due to the piezoelectric charge naturally activated by respiration through the mask. The filter has a long, stable filtration performance and good humidity resistance, demonstrated by a minimal declination in the filtration performance of the nanofiber membrane after moisture exposure. The PLLA filter is reusable via common sterilization tools (i.e., an ultrasonic cleaning bath, autoclave, or microwave). Moreover, a prototype of a completely biodegradable PLLA nanofiber‐based facemask is fabricated and shown to decompose within 5 weeks in an accelerated degradation environment.more » « less
-
One major challenge in the development of nanoparticle-based therapeutics, including viral vectors for the delivery of gene therapies, is the development of cost-effective purification technologies. The objective of this study was to examine fouling and retention behaviors during the filtration of model nanoparticles through membranes of different pore sizes and the effect of solution conditions. Data were obtained with 30 nm fluorescently labeled polystyrene latex nanoparticles using both cellulosic and polyethersulfone membranes at a constant filtrate flux, and both pressure and nanoparticle transmission were evaluated as a function of cumulative filtrate volume. The addition of NaCl caused a delay in nanoparticle transmission and an increase in fouling. Nanoparticle transmission was also a function of particle hydrophobicity. These results provide important insights into the factors controlling transmission and fouling during nanoparticle filtration as well as a framework for the development of membrane processes for the purification of nanoparticle-based therapeutics.more » « less