Abstract Alkali‐activated mortar (AAM) is an emerging eco‐friendly construction material, which can complement ordinary Portland cement (OPC) mortars. Prediction of properties of AAMs—albeit much needed to complement experiments—is difficult, owing to substantive batch‐to‐batch variations in physicochemical properties of their precursors (i.e., aluminosilicate and activator solution). In this study, a machine learning (ML) model is employed; and it is shown that the model—once trained and optimized—can reliably predict compressive strength of AAMs solely from their initial physicochemical attributes. Prediction performance of the model improves when multiple compositional descriptors of the aluminosilicate are combined into a singular, composite chemostructural descriptor (i.e.,network ratioandnumber of constraints); thus, reducing the degrees of freedom. Through interpretation of the ML model's outcomes—specifically the variable importance for the AAMs’ compressive strength—a simple, easy‐to‐use, closed‐form analytical model is developed. Results demonstrate that the analytical model yields predictions of compressive strength of AAMs without scarifying much accuracy compared to the ML model. Overall, this study's outcomes demonstrate a roadmap—incorporates composite chemostructural descriptors in ML models—that can be employed to design AAMs to achieve targeted compressive strength.
more »
« less
This content will become publicly available on January 2, 2027
Effects of shear on the rheological property development of alkali-activated metakaolin geopolymers with implications for ISRU in lunar construction
Alkali-activated materials (AAMs) are candidates for high-strength lunar construction materials via in- situ resource utilization (ISRU) of aluminosilicate lunar regolith. To inform processing strategies for lunar AAMs, the shear-dependent rheological properties of a model AAM comprised of a sodium silicate activated metakaolin are measured from synthesis through gelation along with the compressive strength at longer reaction times. A combination of steady-shear, small amplitude oscillatory shear (SAOS), and Optimally Windowed Chirp (OWCh) techniques characterize the viscosity and shear moduli from initial slurry through the critical gel time. The critical gel point defines the processing time window regardless of the applied shear duration. Shearing prior to the critical gel point does not affect the critical gel time or viscoelastic properties of the material after the set point, or the 7-day compressive strength. However, the dynamic moduli prior to the critical gel time vary significantly based on the shear duration, and the critical gel exponent (n) increases with the duration of applied shear. These results demonstrate how to process without compromising final material properties. Metakaolin geopolymers exposed to low earth orbit (LEO) conditions on the Multi-purpose International Space Station Experiment Flight Facility (MISSE-FF) test station on the International Space Station (ISS) for six months of durability testing retain their compressive strength, furthering the technology readiness of aluminosilicate-derived construction material for future lunar construction. This study provides practical guidance for AAM processing protocols and insight into the effect of shear on the binder structural network valuable for both terrestrial and lunar ISRU
more »
« less
- Award ID(s):
- 2118944
- PAR ID:
- 10657237
- Publisher / Repository:
- Journal of rheology
- Date Published:
- Journal Name:
- Journal of Rheology
- ISSN:
- 0148-6055
- Subject(s) / Keyword(s):
- geopolymer
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
null (Ed.)Alkali-activated materials (AAMs) are one type of sustainable alternative for ordinary Portland cement (OPC), providing significant reductions in CO2 emissions. AAMs based on fly ash or metakaolin are found to possess good fire performance, where the binder gels crystallize and form ceramic phases on heating. However, the ambient temperature setting properties and short-term strength development of select low-calcium AAMs are unfavorable, requiring the optimization of the mix design and a re-evaluation of the chemical, mechanical and physical properties at elevated temperatures (i.e., fire conditions). In this investigation, the influence of calcium hydroxide on the thermal evolution of alkali-activated metakaolin has been assessed, where gel crystallization and restructuring have been evaluated using X-ray diffraction and Fourier transform infrared spectroscopy. It is found that the 10 wt. % replacement of metakaolin with calcium hydroxide, together with a reduction in silicate activator concentration from 10 to 5M, does not adversely impact the phase evolution on heating since similar crystalline phases are seen to emerge. However, the exact location of calcium in the high temperature phases of silicate-activated metakaolin remains unknown.more » « less
-
Abstract Geopolymers, a class of alkali‐activated binders, are studied as sustainable alternatives to Ordinary Portland Cement due to their potential for CO2emission reduction. However, the critical relationship between early‐age reaction kinetics, the development of material properties, and evolving chemical structure remains insufficiently explored, primarily because of the complexity of the underlying chemical reactions and the wide variety of geopolymer chemistries. To address this, we investigate the mechanism of early‐age (<72 h) strength development of a model metakaolin geopolymer by measuring curing kinetics using isothermal calorimetry, material property development via rheology, and chemical coordination at distinct extents of reaction via29Si and27Al NMR. A novel approach of collecting solid‐state29Si and27Al NMR spectra at low temperature (−17°C) successfully quenches the geopolymer reaction, allowing for spectrum collection at a desired extent of reaction despite long29Si NMR spectrum collection times. Applying the Avrami kinetic model to deconvoluted calorimetry data enables independent analysis of dissolution and polycondensation/crosslinking reactions. From these data, the gel reaction product mass fraction is estimated, revealing an exponential relationship with the storage modulus in the activated metakaolin slurry. This study provides new insights into the interconnected dynamics of molecular chemistry, reaction kinetics, rheology, and strength development, offering a semi‐empirical framework for understanding property evolution in geopolymers more broadly.more » « less
-
This study investigates a neoteric approach in manufacturing lunar regolith-filled shape memory vitrimer (SMV) composites for extraterrestrial applications. A SMV with robust mechanical properties was combined with locally available lunar regolith to form a composite material. Fourier Transfer Infrared Spectroscopy (FTIR), Scanning Electron Microscope (SEM), Thermogravimetric Analysis (TGA), and X-ray fluorescence (XRF) were used to characterize the resin, the regolith simulant, and the prepared SMV-regolith composites. We explored conventional synthesis as well as 3D printing methods for manufacturing the composite. Glass fabric-reinforced laminated composites were also prepared to evaluate the impact tolerance and damage healing efficiency. Compressive strength, flexural strength, and impact resistance of the composite were tested at both room and elevated temperatures. A compressive strength of 96.0 MPa and 5.4 MPa were recorded for composite with 40 wt% regolith ratio at room and elevated temperatures, respectively. The glass fabric reinforced SMV-regolith laminate exhibited a bending strength of 232.7 MPa, good impact tolerance under low-velocity impact test, and good healing efficiency up to two damage healing cycles. The 3D printed SMV-regolith composite using a liquid crystal display (LCD)-based printer exhibited a good thermomechanical property with a compressive and tensile strength of 139.16 MPa and 13.99 MPa, respectively, and a good shape memory effect. However, the LCD-based printing using vat-photopolymerization limits the size of the printed samples. Nonetheless, this study shows that utilization of regolith to form advanced composite is possible. SMV regolith composite is a promising material for lunar base applications due to its simple manufacturing process, excellent mechanical properties, and low energy consumption.more » « less
-
As a next generation composite material, carbon fiber reinforced polymer (CFRP) has great potential to be widely used in manufacturing industries due to its outstanding mechanical properties. The high strength to weight ratio, and high stiffness inherent to CFRPs make them a desired material in various kinds of applications. CFRPs frequently experience bending loads while in use for such things as aircraft, automobiles, bridges, etc. Anisotropic behavior and limited in through thickness properties are major concerns which affect the performance of CFRPs. Moreover, in the interlaminar region, traditional CFRPs are often vulnerable to matrix sensitive damage such as compressive failure, delamination, and shear failure due to the absence of enough strength in through thickness direction. The tensile and compressive stress generated by the bending loads can weaken the interlaminar shear properties due to the absence of fibers in through thickness and ultimately can lead to catastrophic failure. This study introduces a novel approach with z-threaded CFRP (ZT-CFRP), which incorporates electrically aligned z-threaded carbon nanofibers (CNFs) as reinforcement. Flexural test using 3-point bending was performed on both control CFRP and ZT-CFRP samples reinforced with 1.0 wt.% carbon nanofiber z-threads. The results showed a 15% improvement in the flexural strength and about 36% linear elastic range increase for the ZT-CFRP laminates compared to the unmodified CFRP laminates, and validated the effectiveness of nanofiber Z-threading strategy in strengthening composite materials against flexural loading.more » « less