  • Dynamic Covalent Chemistry at Interfaces: Development of Tougher, Healable Composites through Stress Relaxation at the Resin–Silica Nanoparticles Interface
Title: Dynamic Covalent Chemistry at Interfaces: Development of Tougher, Healable Composites through Stress Relaxation at the Resin–Silica Nanoparticles Interface
Abstract

The interfacial region in composites that incorporate filler materials of dramatically different modulus relative to the resin phase acts as a stress concentrator and becomes a primary locus for composite failure. A novel adaptive interface (AI) platform formed by coupling moieties capable of dynamic covalent chemistry (DCC) is introduced to the resin–filler interface to promote stress relaxation. Specifically, silica nanoparticles (SNP) are functionalized with a silane capable of addition fragmentation chain transfer (AFT), a process by which DCC‐active bonds are reversibly exchanged upon light exposure and concomitant radical generation, and copolymerized with a thiol‐ene resin. At a fixed SNP loading of 25 wt%, the toughness (2.3 MJ m−3) is more than doubled and polymerization shrinkage stress (0.4 MPa) is cut in half in the AI composite relative to otherwise identical composites that possess a passive interface (PI) with similar silane structure, but without the AFT moiety. In situ activation of the AI during mechanical loading results in 70% stress relaxation and three times higher fracture toughness than the PI control. When interfacial DCC was combined with resin‐based DCC, the toughness was improved by 10 times relative to the composite without DCC in either the resin or at the resin–filler interface.

  more » « less
NSF-PAR ID:
10062889
Author(s) / Creator(s):
 ;  ;  ;  ;  ;  
Publisher / Repository:
Wiley Blackwell (John Wiley & Sons)
Date Published:
Journal Name:
Advanced Materials Interfaces
Volume:
5
Issue:
18
ISSN:
2196-7350
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. ; ; ; ; ; ( , Polymer Chemistry)
    null (Ed.)
    Due to a mismatch in mechanical moduli, the interface between constituent materials in a composite is the primary locus for crack nucleation due to stress concentration. Relaxation of interfacial stresses, without modifying the properties of constituent materials, is a potent means of improving composite performance with broad appeal. Herein, we develop a new type of adaptive interface that utilizes thiol–thioester exchange (TTE) at the filler–polymer interface. Specifically, dynamic covalent bonds sequestered at material interfaces are reversibly exchanged in the presence of thioester moieties, excess thiol and a base/nucleophile catalyst. Employing this active interface effectively mitigates deleterious growth of interfacial stresses, thereby enhancing the composite's mechanical performance in terms of reductions in polymerization shrinkage stress and improvement in toughness. Activating interfacial TTE in an otherwise static matrix resulted in 45% reduction in the polymerization stress, more significant post-polymerization stress relaxation and drastically increased toughness relative to control composites incapable of TTE bond exchange but otherwise identical. In particular, the higher fracture toughness in TTE-activated composites is attributed to the alleviation of crack tip strain concentration, as revealed by digital image correlation. 
    more » « less
  2. ; ; ( , Composites science and technology)
    null (Ed.)
    Aramid fiber reinforced polymer composites have been shown to exhibit impressive mechanical properties, including high strength-to-weight ratio, excellent abrasion resistance, and exceptional ballistic performance. For these reasons, aramid composites have been heavily used in high impact loading environments where ballistic properties are vital. In-situ damage monitoring of aramid composites under dynamic loading conditions typically requires externally bonded sensors, which add bulk and are limited by size and space constraints. To overcome these limitations, this work presents a piezoresistive laser induced graphene (LIG) interface for embedded impact sensing in aramid fiber reinforced composites. Through the monitoring of electrical impedance during ballistic impact, information regarding time and severity of the impact is obtained. The impact velocity correlates with the impedance change of the composites, due to delamination between aramid plies and damage to the LIG interface. The delamination length in Mode I specimens also correlates to changes in electrical impedance of the composite. The interlaminar fracture toughness and areal-density-specific V50 of the LIG aramid composites increased relative to untreated aramid composites. This work demonstrates a methodology to form multifunctional aramid-based composites with a LIG interface that provides both improved toughness and imbedded sensing of impact and damage severity during ballistic impact. 
    more » « less
  3. ; ; ; ; ; ; ; ; ( , Wind Energy)
    Abstract

    Resin uptake plays a critical role in the stiffness‐to‐weight ratio of wind turbine blades in which sandwich composites are used extensively. This work examines the flexural properties of nominally half‐inch thick sandwich composites made with polyvinyl chloride (PVC) foam cores (H60 and H80; PSC and GPC) at several resin uptakes. We found that the specific flexural strength and modulus for the H80 GPC sandwich composites increase from 82.04 to 90.70 kN · m/kg and 6.03 to 7.13 MN · m/kg, respectively, with 11.0% resin uptake reduction, which stands out among the four core sandwich composites. Considering reaching a high stiffness‐to‐weight ratio while preventing resin starvation, 32% to 38% and 40% to 45% resin uptakes are adequate ranges for the H80 PSC and GPC sandwich composites, respectively. The H60 GPC sandwich composites have lower debonding toughness than H60 PSC due to stress concentration in the smooth side skin‐core interphase region. The ailure mode of the sandwich composites depends on the core stiffness and surface texture. The H60 GPC sandwich composites exhibit core shearing and bottom skin‐core debonding failure, while the H80 GPC and PSC sandwich composites show top skin cracking and core crushing failure. The findings indicate that an appropriate range of resin uptake exists for each type of core sandwich composite, and that within the range, a low‐resin uptake leads to lighter blades and thus lower cyclic gravitational loads, beneficial for long blades.

     
    more » « less
  4. ; ; ; ( , ACS Applied Materials & Interfaces)
    Compliant sutures surrounded by stiff matrices are present in biological armors and carapaces, providing enhanced mechanical performance. Understanding the mechanisms through which these sutured composites achieve outstanding properties is key to developing engineering materials with improved strength and toughness. This article studies the impact of suture geometry and load direction on the performance of suture joints using a two-stage reactive polymer resin that enables facile photopatterning of mechanical heterogeneity within a single polymer network. Compliant sinusoidal sutures with varying geometries are photopatterned into stiff matrices, generating a modulus contrast of two orders of magnitude. Empirical relationships are developed connecting suture wavelength and amplitude to composite performance under parallel and perpendicular loading conditions. Results indicate that a greater suture interdigitation broadly improves composite performance when loading is applied perpendicular to suture joints, but has deleterious effects when loading is applied parallel to the joint. Investigations into the failure mechanisms under perpendicular loading highlight the interplay between suture geometry and crack growth stability after damage initiation occurs. Our findings could enable a framework for engineering composites and bio-inspired structures in the future. 
    more » « less
  5. ; ; ; ; ; ; ( , Advanced Materials Technologies)
    Abstract

    Developing mechanically flexible composite materials with high electrical conductivity is currently hindered by the need to use high loading of conductive filler, which severely limits flexibility. Here, acoustic focusing is used to control arrangement of conductive particles in photopolymer matrices to create composites with both tunable conductivity and flexibility. Acoustophoresis patterns filler particles into highly efficient percolated networks which utilize up to 97% of the particles in the composite, whereas the inefficient stochastic networks of conventional dispersed‐fiber composites utilize<5%. These patterned materials have conductivity an order of magnitude higher than conventional composites made with the same ink, reaching 48% the conductivity of bulk silver within the assembled silver‐particle networks (at 2.6 vol% loading). They also have low particle loading so that they are flexible, withstanding>500 bending cycles without losses in conductivity and changing conductivity only 5% within cycles on average. In contrast, conventional unpatterned composites with the same conductivity require such high loading that they are prohibitively brittle. Finally, modulating the applied acoustic field controls the anisotropy of the conductive networks and produces materials which are either 2D conductive, 1D conductive, or insulating, using the same nozzle and ink, paving the way for versatile multifunctional 3D printing.

     
    more » « less
  • Citation Formats
  • MLA
  • APA
  • Chicago
  • BibTeX
  • Save / Share this Record
  • Send to Email