Abstract Recent development of dopant induced solubility control (DISC) patterning of polymer semiconductors has enabled direct‐write optical patterning of poly‐3‐hexylthiophene (P3HT) with diffraction limited resolution. Here, the optical DISC patterning technique to the most simple circuit element, a wire, is applied. Optical patterning of P3HT and P3HT doped with the molecular dopant 2,3,5,6‐tetrafluoro‐7,7,8,8‐tetracyanoquinodimethane (F4TCNQ) wires with dimensions of 20–70 nm thickness, 200–900 nm width, and 40 μm length is demonstrated. In addition, optical patterning of wire patterns like “L” bends and “T” junctions without changing the diameter or thickness of the wires at the junctions is demonstrated. The wires themselves show up to 0.034 S cm‐1conductance when sequentially doped. It is also demonstrated that a P3HT nanowire can be doped, de‐doped, and re‐doped from solution without changing the dimension of the wire. The combined abilities to optically pattern and reversibly dope a polymer semiconductor represents a full suite of patterning steps equivalent to photolithography for inorganic semiconductors.
more »
« less
Effect of processing conditions on additive DISC patterning of P3HT films
There is a critical need to develop a method to pattern semiconducting polymers for device applications on the sub-micrometer scale. Dopant induced solubility control (DISC) patterning is a recently published method for patterning semiconductor polymers that has demonstrated sub-micron resolution. DISC relies on the sequential addition of molecular dopants (here 2,3,5,6-tetrafluoro-7,7,8,8-tetracyanoquinodimethane (F4TCNQ)) to the conjugated polymer. In doped areas, the conjugated polymer is protected from dissolution while in undoped areas, the polymer dissolves into solution. Here we examine factors that affect the resolution of the developed pattern. Two factors are determined to be critical to pattern resolution, the initial crystallinity of the polymer, here poly(3-hexylthiophene) (P3HT), and the quality of the development solvent. We find that dopants diffuse more readily in highly crystalline films than in amorphous films of P3HT and that dopant diffusion reduces the fidelity of the resulting pattern. We also find that the choice of development solvent affects both the fidelity of the pattern and dopant distribution within the patterned polymer domains. Finally, we show that a dopant that diffuses more slowly than F4TCNQ in the P3HT film can be used to pattern the film with higher fidelity. These results together provide a road map for optimizing additive DISC patterning for any polymer/dopant pair.
more »
« less
- Award ID(s):
- 1636385
- PAR ID:
- 10111934
- Date Published:
- Journal Name:
- Journal of Materials Chemistry C
- Volume:
- 7
- Issue:
- 2
- ISSN:
- 2050-7526
- Page Range / eLocation ID:
- 302 to 313
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
The mechanism and the nature of the species formed by molecular doping of the model polymer poly(3-hexylthiophene) (P3HT) in its regioregular (rre-) and regiorandom (rra-) forms in solution are investigated for three different dopants: the prototypical π-electron acceptor 2,3,5,6-tetrafluoro-7,7,8,8-tetracyanoquinodimethane (F4TCNQ), the strong Lewis acid tris(pentafluorophenyl)borane (BCF), and the strongly oxidizing complex molybdenum tris[1-(methoxycarbonyl)-2-(trifluoromethyl)-ethane-1,2-dithiolene] (Mo(tfd-CO2Me)3). In a combined optical and electron paramagnetic resonance study, we show that the doping of rreP3HT in solution occurs by integer charge transfer, resulting in the formation of P3HT radical cations (polarons) for all the dopants considered here. Remarkably, despite the different chemical nature of the dopants and dopant-polymer interaction, the formed polarons exhibit essentially identical optical absorption spectra. The situation is very different for the doping of rraP3HT, where we observe the formation of a charge-transfer complex with F4TCNQ and formation of a “localized” P3HT polaron on non-aggregated chains upon doping with BCF, while there is no indication of dopant-induced species in case of Mo(tfd-CO2Me)3. We estimate the ionization efficiency of the respective dopants for the two polymers in solution and report the molar extinction coefficient spectra of the three different species. Finally, we observe increased spin delocalization in regioregular compared to regiorandom P3HT by electron nuclear double resonance, suggesting that the ability of the charge to delocalize on aggregates of planarized polymer backbones plays a significant role in determining the doping mechanism.more » « less
-
Abstract Carrier mobility in doped conjugated polymers is limited by Coulomb interactions with dopant counterions. This complicates studying the effect of the dopant's oxidation potential on carrier generation because different dopants have different Coulomb interactions with polarons on the polymer backbone. Here, dodecaborane (DDB)‐based dopants are used, which electrostatically shield counterions from carriers and have tunable redox potentials at constant size and shape. DDB dopants produce mobile carriers due to spatial separation of the counterion, and those with greater energetic offsets produce more carriers. Neutron reflectometry indicates that dopant infiltration into conjugated polymer films is redox‐potential‐driven. Remarkably, X‐ray scattering shows that despite their large 2‐nm size, DDBs intercalate into the crystalline polymer lamellae like small molecules, indicating that this is the preferred location for dopants of any size. These findings elucidate why doping conjugated polymers usually produces integer, rather than partial charge transfer: dopant counterions effectively intercalate into the lamellae, far from the polarons on the polymer backbone. Finally, it is shown that the IR spectrum provides a simple way to determine polaron mobility. Overall, higher oxidation potentials lead to higher doping efficiencies, with values reaching 100% for driving forces sufficient to dope poorly crystalline regions of the film.more » « less
-
Doping is required to increase the electrical conductivity of organic semiconductors for uses in electronic and energy conversion devices. The limited number of commonly used p-type dopants suggests that new dopants or doping mechanisms could improve the efficiency of doping and provide new means for processing doped polymers. Drawing on Lewis acid–base pair chemistry, we combined Lewis acid dopant B(C 6 F 5 ) 3 (BCF) with the weak Lewis base benzoyl peroxide (BPO). The detailed behavior of p-type doping of the model polymer poly(3-hexylthiophene) (P3HT) with this Lewis acid–base pair in solution was examined. Solution 19 F-NMR spectra confirmed the formation of the expected counterion, as well as side products from reactions with solvent. BCF : BPO was also found to efficiently dope a range of semiconducting polymers with varying chemical structures demonstrating that the BCF : BPO combination has an effective electron affinity of at least 5.3 eV. In thin films of regioregular P3HT cast from the doped solutions, delocalized polarons formed due to the large counterions leading to a large polaron-counterion distance. At and above 0.2 eq. BCF : BPO doping, amorphous areas of the film became doped, disrupting the structural order of the films. Despite the change in structural order, thin films of regioregular P3HT doped with 0.2 eq. BCF : BPO had a conductivity of 25 S cm −1 . This study demonstrates the effectiveness of a two-component Lewis acid–base doping mechanism and suggests additional two-component Lewis acid–base chemistries should be explored.more » « less
-
Abstract Conjugated polymer brush (CPB) films are more robust and exhibit more vertically aligned polymer chains than their spun‐cast analogs. We prepare CPB films of poly(3‐hexylthiophene) (P3HT) by coupling an amine‐terminated surface (ATS) formed from (3‐aminopropyl)triethoxysilane (APTES) on Si/SiO2to 4‐bromobenzoic acid using standard, inexpensive peptide coupling reagents. The resulting terminal bromobenzene is reacted with Pd(PtBu3)2and immersed in the monomer solution. X‐ray photoelectron spectroscopy, spectroscopic ellipsometry and static water contact angle measurements confirm the surface chemistry at each stage of P3HT CPB preparation. Atomic force microscopy(AFM) and UV–vis spectrophotometry indicate that the CPB films prepared by this method exhibit similar morphology and optical properties to those produced from other methods of poly(3‐alkylthiophene) CPB film preparation. Variations of the standard approach, such as using a pre‐synthesized silane counterpart or with (11‐aminoundecyl)triethoxysilane, show comparable film morphologies by AFM. This method is used to produce the first CPB film of poly(3‐dodecylthiophene), showing its utility for exploring CPB films of more sterically demanding polymers. Peptide coupling is used to prepare an analogous functionalized thiol for initiating P3HT CPB film growth from Au surfaces, and microcontact printing with this thiol allows preparation of the first patterned CPB film of P3HT.more » « less
An official website of the United States government