skip to main content
US FlagAn official website of the United States government
dot gov icon
Official websites use .gov
A .gov website belongs to an official government organization in the United States.
https lock icon
Secure .gov websites use HTTPS
A lock ( lock ) or https:// means you've safely connected to the .gov website. Share sensitive information only on official, secure websites.

Explore Research Products in the PAR
It may take a few hours for recently added research products to appear in PAR search results.


Title: Magnetic Properties of Proton Irradiated Fe 2.7 GeTe 2 Bulk Crystals
van der Waals (vdW) magnetic materials show promise in being the foundation for future spintronic technology. The magnetic behavior of Fe2.7GeTe2 (FGT), a vdW itinerant ferromagnet, was investigated before and after proton irradiation. Proton irradiation of the sample was carried out at a fluence of 1×1018 cm-2. The magnetization measurements revealed a small increase of saturation magnetization (Ms) of about 4% upon proton irradiation of the sample, in which, the magnetic field was applied parallel to the c-axis. X-ray photoelectron spectroscopy for pristine and irradiated FGT revealed a general decrease in intensity after irradiation for Ge and Te and an increase in peak intensity of unavoidable surface iron oxide. Furthermore, no noticeable change in the Curie temperature (TC =152 K) is observed in temperature dependent magnetization variation. This work signifies the importance of employing protons in tuning the magnetic properties of vdW materials.  more » « less
Award ID(s):
1855377
PAR ID:
10113332
Author(s) / Creator(s):
; ; ; ; ; ;
Date Published:
Journal Name:
MRS Advances
ISSN:
2059-8521
Page Range / eLocation ID:
1 to 6
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. ; ; ; ; ; ; ; ; (, Journal of Physics: Condensed Matter)
    Abstract The discovery of long-range magnetic ordering in atomically thin materials catapulted the van der Waals (vdW) family of compounds into an unprecedented popularity, leading to potentially important technological applications in magnetic storage and magneto-transport devices, as well as photoelectric sensors. With the potential for the use of vdW materials in space exploration technologies it is critical to understand how the properties of such materials are affected by ionizing proton irradiation. Owing to their robust intra-layer stability and sensitivity to external perturbations, these materials also provide excellent opportunities for studying proton irradiation as a non-destructive tool for controlling their magnetic properties. Specifically, the exfoliable Cr2Si2Te6(CST) is a ferromagnetic semiconductor with the Curie temperature (TC) of ∼32 K. Here, we have investigated the magnetic properties of CST upon proton irradiation as a function of fluence (1 × 1015, 5 × 1015, 1 × 1016, 5 × 1016, and 1 × 1018H+/cm−2) by employing variable-temperature, variable-field magnetization measurements, and detail how the magnetization, magnetic anisotropy vary as a function of proton fluence across the magnetic phase transition. While theTCremains constant as a function of proton fluence, we observed that the saturation magnetization and magnetic anisotropy diverge at the proton fluence of 5 × 1016H+/cm−2, which is prominent in the ferromagnetic phase, in particular.This work demonstrates that proton irradiation is a feasible method for modifying the magnetic properties and local magnetic interactions of vdWs crystals, which represents a significant step forward in the design of future spintronic and magneto-electronic applications. 
    more » « less
  2. ; ; ; ; ; (, Angewandte Chemie International Edition)
    Abstract Ferromagnetic metal Fe3GeTe2(FGT), whose structure exhibits weak van‐der‐Waals interactions between 5‐atom thick layers, was subjected to liquid‐phase exfoliation (LPE) in N‐methyl pyrrolidone (NMP) to yield a suspension of nanosheets that were separated into several fractions by successive centrifugation at different speeds. Electron microscopy confirmed successful exfoliation of bulk FGT to nanosheets as thin as 6 nm. The ferromagnetic ordering temperature for the nanosheets gradually decreased with the increase in the centrifugation speed used to isolate the 2D material. These nanosheets were resuspended in NMP and treated with an organic acceptor, 7,7,8,8‐tetracyano‐quinodimethane (TCNQ), which led to precipitation of FGT‐TCNQ composite. The formation of the composite material is accompanied by charge transfer from the FGT nanosheets to TCNQ molecules, generating TCNQ⋅−radical anions, as revealed by experimental vibrational spectra and supported by first principles calculations. Remarkably, a substantial increase in magnetic anisotropy was observed, as manifested by the increase in the coercive field from nearly zero in bulk FGT to 1.0 kOe in the exfoliated nanosheets and then to 5.4 kOe in the FGT‐TCNQ composite. The dramatic increase in coercivity of the composite suggests that functionalization with redox‐active molecules provides an appealing pathway to enhancing magnetic properties of 2D materials. 
    more » « less
  3. ; ; ; ; ; ; (, MRS Advances)
    The bulk van der Waals crystal Mn3Si2Te6 (MST) has been irradiated with a proton beam of 2 MeV at a fluence of 1×1018 H+ cm-2. The temperature dependent magnetization measurements show a drastic decrease in the magnetization of 49.2% in the H//c direction observed in ferrimagnetic state. This decrease in magnetization is also reflected in the isothermal magnetization curves. No significant change in the ferrimagnetic transition temperature (75 K) was reflected after irradiation. Electron paramagnetic resonance (EPR) spectroscopy shows no magnetically active defects present after irradiation. Here, experimental findings gathered from MST bulk crystals via magnetic measurements, magnetocaloric effect, and heat capacity are discussed. 
    more » « less
  4. ; ; ; ; ; ; ; ; ; ; et al (, npj 2D Materials and Applications)
    Abstract Among several well-known transition metal-based compounds, cleavable van der Waals (vdW) Fe3-xGeTe2(FGT) magnet is a strong candidate for use in two-dimensional (2D) magnetic devices due to its strong perpendicular magnetic anisotropy, sizeable Curie temperature (TC~154 K), and versatile magnetic character that is retained in the low-dimensional limit. While the TCremains far too low for practical applications, there has been a successful push toward improving it via external driving forces such as pressure, irradiation, and doping. Here we present experimental evidence of a room temperature (RT) ferromagnetic phase induced by the electrochemical intercalation of common tetrabutylammonium cations (TBA+) into quasi-2D FGT. We obtained Curie temperatures as high as 350 K with chemical and physical stability of the intercalated compound. The temperature-dependent Raman measurements, in combination with vdW-corrected ab initio calculations, suggest that charge transfer (electron doping) upon intercalation could lead to the observation of RT ferromagnetism. This work demonstrates that molecular intercalation is a viable route in realizing high-temperature vdW magnets in an inexpensive and reliable manner, and has the potential to be extended to bilayer and few-layer vdW magnets. 
    more » « less
  5. (, 52th IEEE Semiconductor Interface Specialists Conference)
    The developing material class of van der Waals (vdW) magnets has attracted great interest due to their novel properties such as gate and strain tunable magnetism. Magnetism at the atomic limit remains difficult to explore however due to the air instability of most vdW ferromagnets. In this work, we demonstrate that pre-fabricated Hall bar electrodes can be used to probe magnetism in Fe3GeTe2 (FGT) flakes via the anomalous Hall effect. Utilizing this device structure, we systematically investigated the magnetic properties of FGT. Clear ferromagnetic hysteresis windows were clearly observed at temperatures up to 200 K. These vdW Hall bar structures provides a highly efficient and damage-free strategy for metal integration, which could be used in many other 2D magnetic materials. 
    more » « less