An overview of the mechanical bonding of dissimilar bulk engineering metals through high‐pressure torsion (HPT) processing at room temperature is described in this Review. A recently developed procedure of mechanical bonding involves the application of conventional HPT processing to alternately stacked two or more disks of dissimilar metals. A macroscale microstructural evolution involves the concept of making tribomaterials and, for some dissimilar metal combinations, microscale microstructural changes demonstrate the synthesis of metal matrix nanocomposites (MMNCs) through the nucleation of nanoscale intermetallic compounds within the nanostructured metal matrix. Further straining by HPT during mechanical bonding provides an opportunity to introduce limited amorphous phases and a bulk metastable state. The mechanically bonded nanostructured hybrid alloys exhibit an exceptionally high specific strength and an enhanced plasticity. These experimental findings suggest a potential for using mechanical bonding for simply and expeditiously fabricating a wide range of new alloy systems by HPT processing.
more »
« less
Size Effect on Microstructural Evolution and Micromechanical Responses of Mechanically Bonded Aluminum and Magnesium by High‐Pressure Torsion
The mechanical bonding of dissimilar metals though the application of high‐pressure torsion (HPT) processing is developed recently for introducing unique ultrafine‐grained alloy systems involving microstructural heterogeneity leading to excellent mechanical properties. Considering further developments of the processing approach and the produced hybrid materials, the size effect on microstructural evolution and micromechanical responses of the mechanically bonded Al–Mg systems is evaluated. In practice, processing by HPT is conducted at room temperature on the separate Al and Mg disks having 25 mm diameter under 1.0 GPa at 0.4 rpm, and the results are compared with the mechanically bonded Al–Mg system having 10 mm diameter. The Al–Mg disks having 25 mm diameter show a general hardness distribution where low hardness appears around the disk centers, and it increases at the disk peripheries. Nanoindentation measurements demonstrate that there is excellent plasticity at the edges of the Al–Mg system with 25 mm diameter. The Al–Mg system with both 10 and 25 mm diameters show a consistent trend of hardness evolution outlining an exponential increase of hardness with increasing equivalent strain. The results are anticipated to provide a conceptual framework for the development and scale‐up of the HPT‐induced mechanical bonding technique.
more »
« less
- Award ID(s):
- 1810343
- PAR ID:
- 10123628
- Publisher / Repository:
- Wiley Blackwell (John Wiley & Sons)
- Date Published:
- Journal Name:
- Advanced Engineering Materials
- Volume:
- 22
- Issue:
- 10
- ISSN:
- 1438-1656
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
null (Ed.)Processing through the application of high-pressure torsion (HPT) provides significant grain refinement in bulk metals at room temperature. These ultrafine-grained (UFG) materials after HPT generally demonstrate exceptional mechanical properties. Recent reports demonstrated the bulk-state reactions for mechanical bonding of dissimilar lightweight metal disks to synthesize hybrid alloy systems by utilizing conventional HPT processing. Accordingly, the present report provides a comprehensive summary of the recent work on processing of several UFG hybrid alloy systems including Al-Mg and Al-Cu by HPT under 6.0 GPa at room temperature and a special emphasis was placed on understanding the evolution of hardness. This study demonstrates a significant opportunity for the application of HPT for a possible contribution to current enhancements in diffusion bonding, welding and mechanical joining technologies as well as to an introduction of hybrid engineering nanomaterials.more » « less
-
Al-Mg alloy disks were produced from Mg sandwiched between Al through 100 turns of high-pressure torsion (HPT) at 6.0 GPa at room temperature, resulting in high microhardness of Hv 300–350 in regions experiencing a nominal shear strain > ~ 390. While compositional mapping using scanning electron microscopy energy-dispersive spectroscopy (EDS) showed a uniform distribution of Mg through the disk thickness at 1.5 mm and 3.0 mm from the disk center, transmission electron microscopy EDS showed a heterogeneous distribution of Mg remained on the nanoscale. Although HPT induces enough mixing to result in face-center-cubic Al with supersaturations of Mg of up to ~ 20 at.% near the disk surfaces, β-Al3Mg2, γ-Al12Mg17 and Al2Mg intermetallic phases were identified by electron diffraction throughout the disk thickness even in regions experiencing high shear strain. This study visually captures detailed compositional heterogeneity throughout the sample thickness following intense mechanical alloying, nanoscale re-structuring and phase transformations.more » « less
-
This work presents a multi-scale microstructural characterization of aluminum alloys processed by high-pressure torsion (HPT) and cold angular rolling process (CARP) to improve their mechanical properties. Mechanical properties such as microhardness and tensile strength were correlated with microstructural features. To understand the processing-structure-property relationships, characterization methods spanning nano- to millimeter scales were used, including X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), electron backscatter diffraction (EBSD), transmission electron microscopy (TEM), and scanning transmission electron microscopy (STEM) EDS. TEM and STEM EDS were used to show that HPT of a Mg sheet sandwiched between Al sheets successfully produced a supersaturated solid solution (SSSS) of Mg in Al and several Al-Mg intermetallic phases, leading to significant grain refinement and increases in microhardness over pure Al. Although CARP has potential to induce the severe plastic deformation (SPD), the CARP system used in this work was not able to achieve SPD aluminum alloys. However, SEM EBSD characterization shows that CARP achieves an increase of the low-angle grain boundaries (LAGBs) and geometrically necessary dislocation (GND) density in Al-1043,which improves the mechanical properties. Moreover, a preliminary study was conducted on CAPR processed Al-6061 alloys to understand the synergistic effects precipitation and CARP-processing on the microstructure and properties. This research provides the critical insights into the capabilities and current limitations of CARP as a continuous SPD technique for aluminum alloys, and demonstrate the importance of integrated multi-scale characterization in understanding advanced materials processing.more » « less
-
null (Ed.)The processing of bulk metals through the application of severe plastic deformation (SPD), using procedures such as equal-channel angular pressing (ECAP) and high-pressure torsion (HPT), is now well established for the fabrication of materials with exceptionally small grain sizes, usually in the submicrometer range and often having grain sizes at the nanometer level. These grain sizes cannot be achieved using thermo-mechanical processing or any conventional processing techniques. Recently, these procedures have been further developed to process alternative advanced materials. For example, by stacking separate disks within the HPT facility for the synthesis of bulk nanocrystalline metastable alloys where it is possible to achieve exceptionally high hardness, or by pressing powders or metallic particles in order to obtain new and novel nanocomposites exhibiting unusual properties.more » « less