Explore Research Products in the PAR
It may take a few hours for recently added research products to appear in PAR search results.


Title: Linking energy loss in soft adhesion to surface roughness
A mechanistic understanding of adhesion in soft materials is critical in the fields of transportation (tires, gaskets, and seals), biomaterials, microcontact printing, and soft robotics. Measurements have long demonstrated that the apparent work of adhesion coming into contact is consistently lower than the intrinsic work of adhesion for the materials, and that there is adhesion hysteresis during separation, commonly explained by viscoelastic dissipation. Still lacking is a quantitative experimentally validated link between adhesion and measured topography. Here, we used in situ measurements of contact size to investigate the adhesion behavior of soft elastic polydimethylsiloxane hemispheres (modulus ranging from 0.7 to 10 MPa) on 4 different polycrystalline diamond substrates with topography characterized across 8 orders of magnitude, including down to the angstrom scale. The results show that the reduction in apparent work of adhesion is equal to the energy required to achieve conformal contact. Further, the energy loss during contact and removal is equal to the product of the intrinsic work of adhesion and the true contact area. These findings provide a simple mechanism to quantitatively link the widely observed adhesion hysteresis to roughness rather than viscoelastic dissipation.  more » « less
Award ID(s):
1727378
PAR ID:
10131443
Author(s) / Creator(s):
; ; ; ; ;
Date Published:
Journal Name:
Proceedings of the National Academy of Sciences
Volume:
116
Issue:
51
ISSN:
0027-8424
Page Range / eLocation ID:
25484 to 25490
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. ; ; ; ; ; (, Science Advances)
    While controlling underwater adhesion is critical for designing biological adhesives and in improving the traction of tires, haptics, or adhesives for health monitoring devices, it is hindered by a lack of fundamental understanding of how the presence of trapped water impedes interfacial bonding. Here, by using well-characterized polycrystal diamond surfaces and soft, nonhysteretic, low–surface energy elastomers, we show a reduction in adhesion during approach and four times higher adhesion during retraction as compared to the thermodynamic work of adhesion. Our findings reveal how the loading phase of contact is governed by the entrapment of water by ultrasmall (10-nanometer-scale) surface features. In contrast, the same nanofeatures that reduce adhesion during approach serve to increase adhesion during separation. The explanation for this counterintuitive result lies in the incompressibility-inextensibility of trapped water and the work needed to deform the polymer around water pockets. Unlike the well-known viscoelastic contribution to adhesion, this science unlocks strategies for tailoring surface topography to enhance underwater adhesion. 
    more » « less
  2. ; ; ; ; ; ; ; (, Journal of the Mechanics and Physics of Solids)
    Energy dissipation around a propagating crack is the primary mechanism for the enhanced fracture toughness in viscoelastic solids. Such dissipation is spatially non-uniform and is highly coupled to the crack propagation process due to the history-dependent nature of viscoelasticity. We present an experimental approach to map the dissipation field during crack propagation in soft viscoelastic solid. Specifically, we track randomly distributed tracer particles to measure the evolving deformation field. The measured deformation field is then put into a nonlinear constitutive model to determine the dissipation field. Our methodology was used to investigate the deformation and dissipation fields around a propagating crack in a Polyampholyte (PA) hydrogel. The deformation field measurements allowed us to assess whether the commonly assumed translational invariance in viscoelastic fracture theories holds true in practical experiments. Furthermore, by combining the obtained deformation fields with a nonlinear viscoelastic model, we captured the complete history of the dissipation field during crack propagation. We found that dissipation occurred even at material points that are a few millimeters away from the crack tip. The mapped dissipation field also enabled the separate determination of the intrinsic and dissipative components of fracture toughness for the viscoelastic hydrogel. 
    more » « less
  3. ; ; ; ; (, Experimental Mechanics)
    null (Ed.)
    Background: Surface topography strongly modifies adhesion of hard-material contacts, yet roughness of real surfaces typically exists over many length scales, and it is not clear which of these scales has the strongest effect. Objective: This investigation aims to determine which scales of topography have the strongest effect on macroscopic adhesion. Methods: Adhesion measurements were performed on technology-relevant diamond coatings of varying roughness using spherical ruby probes that are large enough (0.5-mm-diameter) to sample all length scales of topography. For each material, more than 2000 measurements of pull-off force were performed in order to investigate the magnitude and statistical distribution of adhesion. Using sphere-contact models, the roughness-dependent effective values of work of adhesion were measured, ranging from 0.08 to 7.15 mJ/m^2 across the four surfaces. The data was more accurately fit using numerical analysis, where an interaction potential was integrated over the AFM-measured topography of all contacting surfaces. Results: These calculations revealed that consideration of nanometer-scale plasticity in the materials was crucial for a good quantitative fit of the measurements, and the presence of such plasticity was confirmed with AFM measurements of the probe after testing. This analysis enabled the extraction of geometry-independent material parameters; the intrinsic work of adhesion between ruby and diamond was determined to be 46.3 mJ/m^2. The range of adhesion was 5.6 nm, which is longer than is typically assumed for atomic interactions, but is in agreement with other recent investigations. Finally, the numerical analysis was repeated for the same surfaces but this time with different length-scales of roughness included or filtered out. Conclusions: The results demonstrate a critical band of length-scales—between 43 nm and 1.8 µm in lateral size—that has the strongest effect on the total adhesive force for these hard, rough contacts. 
    more » « less
  4. ; ; ; ; ; (, Soft Matter)
    Lubricated contacts are present in many engineering and biological systems involving soft solids. Typical mechanisms considered for controlling the sliding friction in such lubricated conditions involve bulk material compliance, fluid viscosity, viscoelastic response of the material (hysteretic friction), and breaking of the fluid film where dry contact occurs (adhesive friction). In this work we show that a two-phase periodic structure (TPPS), with a varying modulus across the sliding surface, provides significant enhancement of lubricated sliding friction when the system is in the elastohydrodynamic lubrication (EHL) regime. We propose that the enhanced friction is due to extra energy loss during periodic transitions of the sliding indenter between the compliant and stiff regions during which excess energy is dissipated through the fluid layer. This is a form of elastic hysteresis that provides a novel mechanism for friction enhancement in soft solids under lubricated conditions. 
    more » « less
  5. ; ; ; (, Soft Matter)
    null (Ed.)
    In this work, we revisit experimentally and theoretically the mechanics of a tape loop. Using primarily elastic materials (polydimethylsiloxane, PDMS, or polycarbonate, PC) and confocal microscopy, we monitor the shape as well as the applied forces during an entire cycle of compression and retraction of a half-loop compressed between parallel glass plates. We observe distinct differences in film shape during the cycle; points of equal applied force or equal plate separation differ in shape upon compression or retraction. To model the adhesion cycle in its entirety, we adapt the ‘Sticky Elastica’ of [T. J. W. Wagner et al., Soft Matter , 2013, 9 , 1025–1030] to the tape loop geometry, which allows a complete analytical description of both the force balance and the film shape. We show that under compression the system is generally not sensitive to interfacial interactions, whereas in the limit of large separation of the confining parallel plates during retraction the system is well described by the peel model. Ultimately, we apply this understanding to the measurement of the energy release rate of a wide range of different cross-linker ratio PDMS elastomer half-loops in contact with glass. Finally, we show how the model illuminates an incredibly simple adhesion measurement technique, which only requires a ruler to perform. 
    more » « less
  • Citation Formats
  • MLA
  • APA
  • Chicago
  • BibTeX
  • Save / Share this Record
  • Send to Email