Abstract We demonstrate the use of tip-enhanced Raman spectroscopy (TERS) on polymeric microstructures fabricated by two-photon polymerization direct laser writing (TPP-DLW). Compared to the signal intensity obtained in confocal Raman microscopy, a linear enhancement of almost two times is measured when using TERS. Because the probing volume is much smaller in TERS than in confocal Raman microscopy, the effective signal enhancement is estimated to be ca. 104. We obtain chemical maps of TPP microstructures using TERS with relatively short acquisition times and with high spatial resolution as defined by the metallic tip apex radius of curvature. We take advantage of this high resolution to study the homogeneity of the polymer network in TPP microstructures printed in an acrylic-based resin. We find that the polymer degree of conversion varies by about 30% within a distance of only 100 nm. The combination of high resolution topographical and chemical data delivered by TERS provides an effective analytical tool for studying TPP-DLW materials in a non-destructive way.
more »
« less
Thermal post-curing as an efficient strategy to eliminate process parameter sensitivity in the mechanical properties of two-photon polymerized materials
Two-photon polymerization direct laser writing (TPP-DLW) is one of the most versatile technologies to additively manufacture complex parts with nanoscale resolution. However, the wide range of mechanical properties that results from the chosen combination of multiple process parameters imposes an obstacle to its widespread use. Here we introduce a thermal post-curing route as an effective and simple method to increase the mechanical properties of acrylate-based TPP-DLW-derived parts by 20-250% and to largely eliminate the characteristic coupling of processing parameters, material properties and part functionality. We identify the underlying mechanism of the property enhancement as a self-initiated thermal curing reaction, which robustly facilitates the high property reproducibility that is essential for any application of TPP-DLW.
more »
« less
- Award ID(s):
- 1905582
- PAR ID:
- 10164582
- Publisher / Repository:
- Optical Society of America
- Date Published:
- Journal Name:
- Optics Express
- Volume:
- 28
- Issue:
- 14
- ISSN:
- 1094-4087; OPEXFF
- Format(s):
- Medium: X Size: Article No. 20362
- Size(s):
- Article No. 20362
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Abstract The main research goal of this study is to decipher the intercorrelation between process-induced thermal-structure-property relationships of Stainless Steel 316L fabricated by laser powder bed fusion. The objective therein is achieved by explaining and quantifying the effect of processing parameters and part-scale thermal history on microstructure evolution and mechanical properties of these parts. Multiple previous works have correlated the effect of process parameters on flaw formation, microstructural features evolved and functional properties; however, a lack of understanding remains in the underlying effect of the thermal history on part microstructure and mechanical properties. The thermal distribution, or thermal history, of the part as it is being built layer-by-layer is influenced by the processing parameters, material properties and shape of the part. The thermal history influences the microstructure by changing the grain structure evolution, which affects the part properties. Therefore, the novelty of this paper lies in illuminating the process-thermal history-microstructure-property relationship in laser powder bed fusion. Characterization of tensile specimens processed at a variety of conditions reveal a direct influence of the choice of process parameters on the dendritic structure and the grain orientations. A high energy density leads to <100> textured columnar dendritic grains and low energy density leads to randomly oriented equiaxed grains as a result of the shifting heat influx. The tensile properties are correlated with the inherent microstructure. Through future work involving fracture surface analysis, the texture, grain size and porosity is expected to influence the inherent fracture mechanism. This work demonstrates that an understanding of thermal distribution within a printed part can inform the choice of processing conditions to generate the final microstructure as per the specified functional requirements. Thus, this paper lays the foundation for future prediction and control of microstructure and functional properties in laser powder bed fusion by identifying the root fundamental thermal phenomena that influences the microstructure evolution and part properties.more » « less
-
Abstract Two‐photon polymerization (TPP) is widely used to create 3D micro‐ and nanoscale scaffolds for biological and mechanobiological studies, which often require the mechanical characterization of the TPP fabricated structures. To satisfy physiological requirements, most of the mechanical characterizations need to be conducted in liquid. However, previous characterizations of TPP fabricated structures are all conducted in air due to the limitation of conventional micro‐ and nanoscale mechanical testing methods. In this study, a new experimental method is reported for testing the mechanical properties of TPP‐printed microfibers in liquid. The experiments show that the mechanical behaviors of the microfibers tested in liquid are significantly different from those tested in air. By controlling the TPP writing parameters, the mechanical properties of the microfibers can be tailored over a wide range to meet a variety of mechanobiology applications. In addition, it is found that, in water, the plasticly deformed microfibers can return to their predeformed shape after tensile strain is released. The shape recovery time is dependent on the size of microfibers. The experimental method represents a significant advancement in mechanical testing of TPP fabricated structures and may help release the full potential of TPP fabricated 3D tissue scaffolds for mechanobiological studies.more » « less
-
Dynamic Actuation of Soft 3D Micromechanical Structures Using Micro‐Electromechanical Systems (MEMS)Abstract Direct laser writing (DLW) is an advanced fabrication technique that allows users to create complex 3D microstructures from polymer precursors. These microstructures can be integrated with micro‐electromechanical systems (MEMS) actuators. MEMS actuators provide a convenient platform for interacting with the intricate microstructures, either to characterize their mechanical properties or cause them to deform. Structures are fabricated directly onto electrostatic comb drives and chevron thermal actuators that are produced using a commercial foundry process. By applying a voltage to the MEMS actuators, highly controlled deformation of these microstructures is observed. Mechanical behaviors of microstructures produced with different materials and fabrication conditions are compared. MEMS–DLW integration is a convenient approach to characterizing the mechanics of DLW microstructures and may well lead to a new class of dynamic 3D devices for applications ranging from tissue engineering to imaging.more » « less
-
Purpose There is recent emphasis on designing new materials and alloys specifically for metal additive manufacturing (AM) processes, in contrast to AM of existing alloys that were developed for other traditional manufacturing methods involving considerably different physics. Process optimization to determine processing recipes for newly developed materials is expensive and time-consuming. The purpose of the current work is to use a systematic printability assessment framework developed by the co-authors to determine windows of processing parameters to print defect-free parts from a binary nickel-niobium alloy (NiNb5) using laser powder bed fusion (LPBF) metal AM. Design/methodology/approach The printability assessment framework integrates analytical thermal modeling, uncertainty quantification and experimental characterization to determine processing windows for NiNb5 in an accelerated fashion. Test coupons and mechanical test samples were fabricated on a ProX 200 commercial LPBF system. A series of density, microstructure and mechanical property characterization was conducted to validate the proposed framework. Findings Near fully-dense parts with more than 99% density were successfully printed using the proposed framework. Furthermore, the mechanical properties of as-printed parts showed low variability, good tensile strength of up to 662 MPa and tensile ductility 51% higher than what has been reported in the literature. Originality/value Although many literature studies investigate process optimization for metal AM, there is a lack of a systematic printability assessment framework to determine manufacturing process parameters for newly designed AM materials in an accelerated fashion. Moreover, the majority of existing process optimization approaches involve either time- and cost-intensive experimental campaigns or require the use of proprietary computational materials codes. Through the use of a readily accessible analytical thermal model coupled with statistical calibration and uncertainty quantification techniques, the proposed framework achieves both efficiency and accessibility to the user. Furthermore, this study demonstrates that following this framework results in printed parts with low degrees of variability in their mechanical properties.more » « less