Cadmium telluride (CdTe) solar cells are a promising photovoltaic (PV) technology for producing power in space owing to their high-efficiency (> 22.1 %), potential for specific power, and cost-effective manufacturing processes. In contrast to traditional space PVs, the high-Z (atomic number) CdTe absorbers can be intrinsically robust under extreme space radiation, offering long-term stability. Despite these advantages, the performance assessment of CdTe solar cells under high-energy particle irradiation (e.g., photons, neutrons, charged particles) is limited in the literature, and their stability is not comprehensively studied. In this work, we present the PV response of n-CdS / p-CdTe PVs under accelerated neutron irradiation. We measure PV properties of the devices at different neutron/photon doses. The equivalent dose deposited in the CdTe samples is simulated with deterministic and Monte Carlo radiation transport methods.
Thin-film CdTe solar cells were synthesized on a fluorine-doped tin oxide (FTO) coated glass substrate (≈ 4 cm × 4 cm). CdS:O (≈ 100 nm) was reactively RF sputtered in an oxygen/argon ambient followed by a close-spaced sublimation deposition of CdTe (≈ 3.5 μm) in an oxygen/helium ambient. The sample was exposed to a 10 min vapor CdCl2 in oxygen/helium ambient at 430˚C. The samples were exposed to a wet CuCl2 solution prior to anneal 200ºC. A gold back-contact was formed on CdTe via thermal evaporation. The final sample contains 16 CdTe devices. For neutron irradiation, we cleaved the CdTe substrate into four samples and exposed two samples to ≈ 90 kW reactor power neutron radiation for 5.5 hours and 8.2 hours, respectively, in our TRIGA (Training, Research, Isotopes, General Atomics) reactor.
We observed a noticeable color change of the glass substrates to brown after the neutron/gamma reactor exposure. Presumably, the injected high-energy neutrons caused the breaking of chemical bonds and the displacement of atoms in the glass substrates, creating point defects and color centers. The I-V characteristics showed noticeable deterioration with over 8 hour radiations. Specifically, the saturation current of the control devices was ≈ 25 nA increasing to 1 μA and 10 μA for the 5.5-hour and 8.2-hour radiated samples, respectively. The turn-on voltage of the control devices (≈ 0.85 V) decreased with the irradiated sample (≈ 0.75 V for 5.5-hour and ≈ 0.5 V for 8.2-hour exposures), implying noticeable radiation damage occurred at the heterojunction. The higher values of the ideality factor for irradiated devices (n > 2.2) compared to that of the control devices (n ≈ 1.3) also support the deterioration of the p-n junction. We observed the notable decrease in shunt resistance (RSH) and the increase in series resistance (Rs) with the neutron dose. It is possible that Cu ions introduced during the CuCl2 treatment may migrate into CdTe grain boundaries (GBs). The presence of Cu ions at GBs can create additional leakage paths for photocarrier transport, deteriorating the overall PV performance.
We estimated the radiation dose of CdTe in comparison to Si (conventional PV) using a UUTR model (e.g., MCNP6 2D UTR Reactor simulations). In this model, we simulated Si and CdTe at the center point of the triangular fuel lattice and used an “unperturbed flux” tally in the water. Our simulations yielded a dose rate of 6916 Gy/s of neutrons and 16 Gy/s of photons for CdTe, and 1 Gy/s of neutrons and 21 Gy/s of photons for Si (doses +/- <1%). The large dose rate of neutrons in CdTe is mainly attributed to the large thermal neutron absorption cross-section of 113Cd. Based on this estimation, we calculate that the exposure of our CdTe PVs is equivalent to several million years in LEO (Low-Earth Orbit), or about 10,000 years for Si in LEO. Currently, we are working on a low-dose neutron/photon radiation on CdTe PVs and their light I-Vs and microstructural characterizations to gain better understanding on the degradation of CdTe PVs.
more »
« less
Analysis of CdTe photovoltaic cells for ambient light energy harvesting
This paper investigates the suitability of CdTe photovoltaic cells to be used as power sources for wireless sensors located in buildings. We fabricate and test a CdTe photovoltaic cell with a transparent conducting oxide front contact that provides for high photocurrents and low series resistance at low light intensities - and measure the photovoltaic response of this cell across five orders of magnitude of AM1.5G light intensity. Efficiencies of 10% and 17.1% are measured under ~1 W/m2 AM1.5G and LED irradiance respectively, the highest values for a CdTe device under ambient lighting measured to date. We use our results to assess the potential of CdTe for internet of things devices from an optoelectronic, as well as a techno-economic perspective, considering its established manufacturing know-how, potential for low-cost, proven long-term stability and issues around the use of cadmium.
more »
« less
- NSF-PAR ID:
- 10173553
- Date Published:
- Journal Name:
- Journal of Physics D: Applied Physics
- ISSN:
- 0022-3727
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Cadmium telluride and silicon are among the widely used absorber materials in photovoltaic industry. A tandem solar cell of these two can absorb significant portion of solar spectrum to yield high efficiency due to the added voltage of the two solar cells. On basis of low-cost production, a CdTe/Si cell has the potential to produce low-cost and high efficiency tandem PV. The CdTe top cell in a substrate configuration is essential to achieve a tandem between CdTe and Si. A functional CdS/CdTe solar cell in the substrate configuration was fabricated on a Si wafer. Current -Voltage measurements show a diode-like curve with lower J-V parameters compared to standard CdS/CdTe cells. SCAPS simulations were performed to identify possible reasons for poor performance and help improve the device performance.more » « less
-
Low-cost materials, scalable manufacturing, and high power conversion efficiency are critical enablers for large-scale applications of photovoltaic (PV) cells. Cu 2 ZnSn(S,Se) 4 (CZTSSe) has emerged as a promising PV material due to its low-cost earth-abundant nature and the low toxicity of its constituents. We present a compact and environmentally friendly route for preparing metal sulfide (metals are Cu, Zn, and Sn) nanoparticles (NPs) and optimize their annealing conditions to obtain uniform carbon-free CZTSSe thin films with large grain sizes. Further, the solution-stable binary NP inks synthesized in an aqueous solution with additives are shown to inhibit the formation of secondary phases during annealing. A laboratory-scale PV cell with a Al/AZO/ZnO/CdS/CZTSSe/Mo-glass structure is fabricated without anti-reflective coatings, and a 9.08% efficiency under AM1.5G illumination is demonstrated for the first time. The developed scalable, energy-efficient, and environmentally sustainable NP synthesis approach can enable integration of NP synthesis with emerging large-area deposition and annealing methods for scalable fabrication of CZTSSe PV cells.more » « less
-
Cadmium telluride (CdTe) thin-film semiconductors exhibit many desirable properties for low-cost and high-efficiency photovoltaic (PV) technology, including inherent robustness of inorganic absorber, a direct bandgap that allows full absorption of the solar spectrum with thicknesses of only few microns, and inexpensive and high-throughput manufacturing processes. At the best efficiency of 22 %, the power conversion efficiency of CdTe PVs is still well below the maximum theoretical limit (approximately 30 %). It has been suggested that the inferior efficiency is mainly attributed to the inherent polycrystalline nature of CdTe absorber (e.g., grains, grain boundaries). Understanding local photocarrier dynamics is vital to overcoming roadblocks toward higher efficiency CdTe PVs. However, conventional cell-level PV measurements often limit the microstructural analysis. In this work, we present a local PV characterization technique using point back-contacts. The thin-film CdTe solar cells used in this work were prepared by CSS (close-spaced sublimation) on a stack of n-type window layer (e.g., CdS) / transparent conductive layer (TCO; e.g., SnO2) / glass substrate.more » « less
-
Wearable devices with sensing, processing and communication capabilities have become feasible with the advances in internet-of-things (IoT) and low power design technologies. Energy harvesting is extremely important for wearable IoT devices due to size and weight limitations of batteries. One of the most widely used energy harvesting sources is photovoltaic cell (PV-cell) owing to its simplicity and high output power. In particular, flexible PV-cells offer great potential for wearable applications. This paper models, for the first time, how bending a PV-cell significantly impacts the harvested energy. Furthermore, we derive an analytical model to quantify the harvested energy as a function of the radius of curvature. We validate the proposed model empirically using a commercial PV-cell under a wide range of bending scenarios, light intensities and elevation angles. Finally, we show that the proposed model can accelerate maximum power point tracking algorithms and increase the harvested energy by up to 25.0%.more » « less
- Free Publicly Accessible Full Text
-
Accepted Manuscript1.0
- Journal Article:
- https://doi.org/10.1088/1361-6463/ab94e6