Functional polymers or copolymers have been added to separations membranes by incorporating them in the membrane dope prior to casting, by
Increasing Salt Rejection of Polybenzimidazole Nanofiltration Membranes via the Addition of Immobilized and Aligned Aquaporins
Aquaporins are water channel proteins in cell membrane, highly specific for water molecules while restricting the passage of contaminants and small molecules, such as urea and boric acid. Cysteine functional groups were installed on aquaporin Z for covalent attachment to the polymer membrane matrix so that the proteins could be immobilized to the membranes and aligned in the direction of the flow. Depth profiling using x-ray photoelectron spectrometer (XPS) analysis showed the presence of functional groups corresponding to aquaporin Z modified with cysteine (Aqp-SH). Aqp-SH modified membranes showed a higher salt rejection as compared to unmodified membranes. For 2 M NaCl and CaCl2 solutions, the rejection obtained from Aqp-SH membranes was 49.3 ± 7.5% and 59.1 ± 5.1%. On the other hand, the rejections obtained for 2 M NaCl and CaCl2 solutions from unmodified membranes were 0.8 ± 0.4% and 1.3 ± 0.2% respectively. Furthermore, Aqp-SH membranes did not show a significant decrease in salt rejection with increasing feed concentrations, as was observed with other membranes. Through simulation studies, it was determined that there was approximately 24% capping of membrane pores by dispersed aquaporins.
more »
« less
- Award ID(s):
- 1709381
- PAR ID:
- 10182386
- Date Published:
- Journal Name:
- Processes
- Volume:
- 7
- Issue:
- 2
- ISSN:
- 2227-9717
- Page Range / eLocation ID:
- 76
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
more » « less
ABSTRACT in situ polymerization, and by postsynthesis surface modification of existing membranes. Here, a postsynthesis membrane functionalization that targeted decreasing the molecular weight cutoff (MWCO) and increasing the hydrophilicity without significantly decreasing the operating flux was studied. Hybrid bisamide molecules with added amine and carboxylic acid functionalities as end groups were synthesized to form a selective layer on membrane surface via covalent attachment to the membrane. Fourier transform infrared spectroscopy analysis showed the functional groups corresponding to bisamide molecules were present on modified membranes. Furthermore, modified membranes displayed MWCO of 400 Da as compared to 1000 Da MWCO of unmodified membranes, along with an increase in the hydrophilicity of modified membranes. Modified membranes showed an improvement in divalent salt rejection and percent flux recovered after reverse‐flow filtration as compared to unmodified membranes. © 2019 Wiley Periodicals, Inc. J. Appl. Polym. Sci.2020 ,137 , 48327. -
null (Ed.)In the textile industry, a high-efficiency dye removal and low-retention of salt is demanded for recycling wastewater. In this study, polyvinylidene fluoride (PVDF) ultrafiltration membrane was transformed to a negatively charged loose nanofiltration (NF) membrane through UV-grafting of acrylic acid. At the optimal exposure of PVDF membrane in UV light for 5 min, the membrane had a high dye recovery above 99% (Congo red and Eriochrome® Black T) and a low sodium chloride (NaCl) rejection of less than 15% along with pure water flux of 26 L∙m−2∙h−1∙bar−1. Its antifouling and oleophobicity surface properties were verified using fluorescent- bovine serum albumin (BSA) and underwater mineral oil contact angle, respectively. According to the fluorescent microscopic images, the modified membrane had ten times lower adhesion of protein on the surface than the unmodified membrane. The underwater oil contact angle was raised from 110° to 155°. Moreover, the salt rejection followed this sequence: Na2SO4 > MgSO4 > NaCl > MgCl2, which agreed with the typical negatively charged NF membrane. In addition, the physicochemical characterization of membranes was further investigated to understand and link to the membrane performance, such as surface functional group, surface elements analysis, surface roughness/morphology, and surface hydrophilicity.more » « less
-
more » « less
Abstract Monodispersed angstrom-size pores embedded in a suitable matrix are promising for highly selective membrane-based separations. They can provide substantial energy savings in water treatment and small molecule bioseparations. Such pores present as membrane proteins (chiefly aquaporin-based) are commonplace in biological membranes but difficult to implement in synthetic industrial membranes and have modest selectivity without tunable selectivity. Here we present PoreDesigner, a design workflow to redesign the robust beta-barrel Outer Membrane Protein F as a scaffold to access three specific pore designs that exclude solutes larger than sucrose (>360 Da), glucose (>180 Da), and salt (>58 Da) respectively. PoreDesigner also enables us to design any specified pore size (spanning 3–10 Å), engineer its pore profile, and chemistry. These redesigned pores may be ideal for conducting sub-nm aqueous separations with permeabilities exceeding those of classical biological water channels, aquaporins, by more than an order of magnitude at over 10 billion water molecules per channel per second.
-
We demonstrated for the first time that inkjet printing can be a low-cost, easy, fast, and scalable method for depositing ultrathin (7.5–60 nm) uniform graphene oxide (GO) nanofiltration membranes on polymeric supports for highly effective water purification. A large area (15 × 15 cm 2 ) GO nanofiltration membrane was printed successfully on a modified polyacrylonitrile (M-PAN) support. Water permeance and rejection of small organic molecules (<1 nm, charged and uncharged) of printed GO membranes can be adjusted by controlling the GO “ink” concentration and/or printing time. Compared with commercial polymeric nanofiltration membranes, printed GO membranes, after optimization, showed approximately one order of magnitude higher water permeance and much higher rejection (>95%) of small organic molecules. Printed GO membranes also showed excellent performance in removing pharmaceutical contaminants, with ∼95% rejection and <10% water permeance decline over extended-period permeation testing. We believe that inkjet printing could be an effective method for preparing ultrathin GO membranes for effective water nanofiltration purification.more » « less
-
Membranes used for desalination still face challenges during operation. One of these challenges is the buildup of salt ions at the membrane surface. This is known as concentration polarization, and it has a negative effect on membrane water permeance and salt rejection. In an attempt to decrease concentration polarization, a line-and-groove nanopattern was applied to a nanofiltration (NF) membrane. Aqueous sodium sulfate (Na2SO4) solutions were used to test the rejection and permeance of both pristine and patterned membranes. It was found that the nanopatterns did not reduce but increased the concentration polarization at the membrane surface. Based on these studies, different pattern shapes and sizes should be investigated to gain a fundamental understanding of the influence of pattern size and shape on concentration polarization.more » « less
- Free Publicly Accessible Full Text
-
Accepted Manuscript1.0
- Journal Article:
- https://doi.org/10.3390/pr7020076