Title: Shear-assisted grain coarsening in colloidal polycrystals
Grain growth under shear annealing is crucial for controlling the properties of polycrystalline materials. However, their microscopic kinetics are not well understood because individual atomic trajectories are difficult to track. Here, we study grain growth with single-particle kinetics in colloidal polycrystals using video microscopy. Rich grain-growth phenomena are revealed in three shear regimes, including the normal grain growth (NGG) in weak shear melting–recrystallization process in strong shear. For intermediate shear, early stage NGG is arrested by built-up stress and eventually gives way to dynamic abnormal grain growth (DAGG). We find that DAGG occurs via a melting–recrystallization process, which naturally explains the puzzling stress drop at the onset of DAGG in metals. Moreover, we visualize that grain boundary (GB) migration is coupled with shear via disconnection gliding. The disconnection-gliding dynamics and the collective motions of ambient particles are resolved. We also observed that grain rotation can violate the conventional relation R × θ = c o n s t a n t (R is the grain radius, and θ is the misorientation angle between two grains) by emission and annihilation of dislocations across the grain, resulting in a step-by-step rotation. Besides grain growth, we discover a result in shear-induced melting: The melting volume fraction varies sinusoidally on the angle mismatch between the triangular lattice orientation of the grain and the shear direction. These discoveries hold potential to inform microstructure engineering of polycrystalline materials.  more » « less
Award ID(s):
2003659
NSF-PAR ID:
10230896
Author(s) / Creator(s):
; ; ; ; ;
Date Published:
Journal Name:
Proceedings of the National Academy of Sciences
Volume:
117
Issue:
39
ISSN:
0027-8424
Page Range / eLocation ID:
24055 to 24060
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. Recent advances pertaining to modeling of grain fragmentation during deformation and recrystallization of polycrystalline metals using viscoplastic self-consistent (VPSC) polycrystal plasticity are combined into a field fluctuations VPSC (FF-VPSC) model. The FF-VPSC model is a higher-order formulation calculating the second moments of lattice rotation rates based on the second moments of stress fields inside grains and resulting intragranular misorientation distributions. The misorientation distributions are used to define a grain fragmentation sub-model for improving predictions of deformation texture evolution and to formulate kinetics sub-models for nucleation as well as to influence the stored energy governing grain growth for the predictions of recrystallization texture evolution. Formation of a copper-like texture in moderately high stacking fault energy (SFE) Cu and a brass-like texture in low SFE brass during rolling to very large strains are successfully predicted using the model. Remarkably, the model also predicts recrystallization textures from the deformation textures of the two metals after adjusting tradeoffs between transition-bands and grain boundary nucleation mechanisms. Additionally, rolling and recrystallization of an interstitial-free steel, tension and recrystallization of AA5182-O, and recrystallization of an additively manufacturing cobalt-based alloy MarM-509 are simulated to predict texture evolution. Through these case studies involving multiple alloys and thermo-mechanical processes we show that, in addition to being predictive with good accuracy, the key advantage of the model lies in its versatility. The FF-VPSC model, simulation results, and insights from the results are presented and discussed in this paper. 
    more » « less
  2. null (Ed.)
    Among metal additive manufacturing technologies, additive friction stir deposition stands out for its ability to create freeform and fully-dense structures without melting and solidification. Here, we employ a comparative approach to investigate the process-microstructure linkages in additive friction stir deposition, utilizing two materials with distinct thermomechanical behavior—an Al-Mg-Si alloy and Cu—both of which are challenging to print using beam-based additive processes. The deposited Al-Mg-Si is shown to exhibit a relatively homogeneous microstructure with extensive subgrain formation and a strong shear texture, whereas the deposited Cu is characterized by a wide distribution of grain sizes and a weaker shear texture. We show evidence that the microstructure in Al-Mg-Si primarily evolves by continuous dynamic recrystallization, including geometric dynamic recrystallization and progressive lattice rotation, while the heterogeneous microstructure of Cu results from discontinuous recrystallization during both deposition and cooling. In Al-Mg-Si, the continuous recrystallization progresses with an increase of the applied strain, which correlates with the ratio between the tool rotation rate and travel velocity. Conversely, the microstructure evolution in Cu is found to be less dependent on , instead varying more with changes to . This difference originates from the absence of Cu rotation in the deposition zone, which reduces the influence of tool rotation on strain development. We attribute the distinct process-microstructure linkages and the underlying mechanisms between Al-Mg-Si and Cu to their differences in intrinsic thermomechanical properties and interactions with the tool head. 
    more » « less
  3. Abstract

    The effect of pressure on grain‐growth kinetics of olivine was investigated up to 10 GPa at 1773 K under relatively water‐poor conditions. The results are interpreted using a relationto obtain the activation volume = 5.0 ± 1.1 cm3/mol forn = 2 or = 5.2 ± 1.1 cm3/mol forn = 3. The small activation volume means that grain‐growth kinetics in pure olivine aggregates is fast even in the dry deep upper mantle, implying that grain‐size is controlled by the pinning by other phases or by dynamic recrystallization except for the early stage after the phase transformation from wadsleyite in upwelling materials. The present results are applied to seismic wave attenuation that is likely controlled by grain‐boundary processes. The inferred peak in attenuation just below the oceanic lithosphere‐asthenosphere boundary from the NoMelt array is difficult to be explained by the pressure effects assuming the absorption band behavior because such a model requires a much larger activation volume than determined in this work and it also fails to explain high attenuation in the deep asthenosphere. This suggests that either melt accumulation or other processes such as elastically accommodated grain‐boundary sliding (EAGBS) is responsible for the peak in attenuation. The present results are also applied to EAGBS. We suggest that the deep upper mantle is likely to be relaxed by EAGBS, which implies that the shear velocity of the deep upper mantle can be several percent smaller than that inferred from single crystal elasticity.

     
    more » « less
  4. Cold sintering densification and coarsening mechanisms are considered from the perspective of the nonequilibrium chemo-mechanical process known in Earth Sciences as pressure solution creep (or dissolutionprecipitation creep). This is an important mechanism of densification and deformation in many geological rock formations in the Earth’s upper crust, and although very slow in nature, it is of direct relevance to the cold sintering process. In cold sintering, we select particulate materials and identify experimental processing parameters to significantly accelerate the kinetics of dissolution-precipitation phenomena, with appropriate consideration of chemistry, applied stress, particle size and temperatures. In the theory of pressure solution, pressure-driven densification is considered to involve the consecutive stages of dissolution at grain contact points, then diffusive transport along the grain boundaries towards open pore surfaces, and then precipitation, all driven by chemical potential gradients. In this study, it is shown that cold sintering of BaTiO3, ZnO and KH2PO4 (KDP) ceramic materials proceeds by the same type of serial process, with the pressure solution creep rate being controlled by the slowest kinetic step. This is demonstrated by the values of activation energy (Ea) for densification, which are in good agreement with the existing literature on dissolution, precipitation, or coarsening. The influence of pressure on the morphology of ZnO grains also supports the pressure solution mechanism. Other characteristics that can be understood qualitatively in terms of pressure solution are observed in the in systems such as BaTiO3 and KDP. We further consider activation energies for grain growth with respect to the precipitation process, as well as evidence for coalescence and Ostwald ripening during cold sintering. For completeness we also consider materials that show significant plastic deformation under compression. Our findings point the way for new advances in densification, microstructural control, and reductions in cold sintering pressure, via the use of appropriate transient solvents in metals and hybrid organic-inorganic systems, such as the Methylammonium lead bromide (MAPBr) perovskite. 
    more » « less
  5. Abstract

    To study the mechanical behavior of polymineralic rocks, we performed deformation experiments on two‐phase aggregates of olivine (Ol) + ferropericlase (Per) with periclase fractions (fPer) between 0.1 and 0.8. Each sample was deformed in torsion atT = 1523 K,P = 300 MPa at a constant strain rate to a final shear strain ofγ = 6 to 7. The stress‐strain data and calculated values of the stress exponent,n, indicate that Ol in our samples deformed by dislocation‐accommodated sliding along grain interfaces while Per deformed via dislocation creep. At shear strains ofγ < 1, the strengths of samples withfPer > 0.5 match model predictions for both phases deforming at the same stress, the lower‐strength bound for two‐phase materials, while the strengths of samples withfPer < 0.5 are greater than predicted by models for both phases deforming at the same strain rate, the upper‐strength bound. These observations suggest a transition from a weak‐phase supported to a strong‐phase supported regime with decreasingfPer. Aboveγ = 4, however, the strength of all two‐phase samples is greater than those predicted by either the uniform‐stress or the uniform‐strain rate bound. We hypothesize that the high strengths in the Ol + Per system are due to the presence of phase boundaries in two‐phase samples, for which deformation is rate limited by dislocation motion along interfacial boundaries. This observation contrasts with the mechanical behavior of samples consisting of Ol + pyroxene, which are weaker, possibly due to impurities at phase boundaries.

     
    more » « less