Title: Mechanics of Microspheres Reinforced Hollow Microcells
Abstract Emerging polymeric foams exhibiting unique microstructure of microspherical shells with reinforcing dense microspheres creates a new opportunity for impact-tolerant foam paddings in sport gears applications. This paper describes the static response of reinforced microcell consisting of an outer spherical shell and uniformly distributed microspheres while quantifying the stiffening effect. The distribution of the microspheres is illustrated using the Fourier series, allowing tuning of the reinforcing strategy. Expressions of the external and internal works are derived, whereas the Ritz energy method is adopted to calculate the deformations due to a compressive load distributed over a range of areas. Emphasis is given to the effect of the geometrical attributes of the microcell and the reinforcing microspheres on the resulting deformation response and stiffening effect. The framework is used to investigate the response of several case studies to elucidate the effects of relative radii ratio, reinforcement density, microcell wall thickness, and loading configurations on the stiffness. A new normalized strain energy parameter is introduced to simplify and accelerate the analysis while providing insights on the underpinnings of the observed buckling response. The results strongly suggest the viability of the newly discovered foam microstructure in managing static loads while providing an opportunity to strategically tune the mechanical response using the analytical framework presented herein.  more » « less
Award ID(s):
1925539
NSF-PAR ID:
10247234
Author(s) / Creator(s):
; ;
Date Published:
Journal Name:
Journal of Applied Mechanics
Volume:
88
Issue:
4
ISSN:
0021-8936
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. null (Ed.)
    This paper reports the unique microstructure of polyurea foams that combines the advantages of open and closed cell polymeric foams, which were synthesized through a self-foaming process. The latter was the result of aggressive mechanical mixing of diamine curative, isocyanate, and deionized water at ambient conditions, which can be adjusted on-demand to produce variable density polyurea foam. The spherical, semi-closed microcellular structure has large perforations on the cell surface resulting from the concurrent expansion of neighboring cells and small holes at the bottom surface of the cells. This resulted in a partially perforated microcellular structure of polyurea foam. As a byproduct of the manufacturing process, polyurea microspheres nucleate and deposit on the inner cell walls of the foam, acting as a reinforcement. Since cell walls and the microspheres are made of polyurea, the resulting reinforcement effect overcomes the fundamental interfacial issue of different adjacent materials. The partially perforated, self-reinforced polyurea foam is compared to the performance of traditional counterparts in biomechanical impact scenarios. An analytical model was developed to explicate the stiffening effect associated with the reinforcing microspheres. The model results indicate that the reinforced microcell exhibited, on average, ~30% higher stiffness than its barren counterpart. 
    more » « less
  2. The proliferation of ordered cellular structures in industrial and technological applications is justified by their superior mechanical performance, including tunable energy absorption strategies and potential multifunctionality. This research evaluates the mechanical response of composite lattice structures fabricated using vat photopolymerization additive manufacturing process and printable particulate composite materials. Several generations of modified printable resins are prepared by hybridizing flexible resin with varying glass microballoons reinforcement weight percentages. Multifaceted characterization regiments highlight the process–property–performance interrelationship by submitting printed composite structures to quasi‐static and impact‐loading scenarios combined with digital stills and high‐speed photography, respectively. Image analyses of optical and scanning electron micrographs quantify the dimensional accuracy of the composite lattice structures with cylindrical and hexagonal cellular geometries. The mechanical characterization uncovers the effect of cell geometry and reinforcement on the global structural behavior, eliciting differences in load‐bearing capacity, local strain developments, and structural densification. Exploratory digital image correlation supports the global structural deformations, revealing their relationship with the developed local strain state within the unit cells. The outcomes of this research elucidate the effect of strain rate, unit cell geometry, and reinforcing ratios on the structural performance of composite lattice structures at the macro‐ and microstructure levels.

     
    more » « less
  3. Abstract There is a need for new in vitro systems that enable pharmaceutical companies to collect more physiologically-relevant information on drug response in a low-cost and high-throughput manner. For this purpose, three-dimensional (3D) spheroidal models have been established as more effective than two-dimensional models. Current commercial techniques, however, rely heavily on self-aggregation of dissociated cells and are unable to replicate key features of the native tumor microenvironment, particularly due to a lack of control over extracellular matrix components and heterogeneity in shape, size, and aggregate forming tendencies. In this study, we overcome these challenges by coupling tissue engineering toolsets with microfluidics technologies to create engineered cancer microspheres. Specifically, we employ biosynthetic hydrogels composed of conjugated poly(ethylene glycol) (PEG) and fibrinogen protein (PEG-Fb) to create engineered breast and colorectal cancer tissue microspheres for 3D culture, tumorigenic characterization, and examination of potential for high-throughput screening (HTS). MCF7 and MDA-MB-231 cell lines were used to create breast cancer microspheres and the HT29 cell line and cells from a stage II patient-derived xenograft (PDX) were encapsulated to produce colorectal cancer (CRC) microspheres. Using our previously developed microfluidic system, highly uniform cancer microspheres (intra-batch coefficient of variation (CV) ≤ 5%, inter-batch CV < 2%) with high cell densities (>20×106 cells/ml) were produced rapidly, which is critical for use in drug testing. Encapsulated cells maintained high viability and displayed cell type-specific differences in morphology, proliferation, metabolic activity, ultrastructure, and overall microsphere size distribution and bulk stiffness. For PDX CRC microspheres, the percentage of human (70%) and CRC (30%) cells was maintained over time and similar to the original PDX tumor, and the mechanical stiffness also exhibited a similar order of magnitude (103 Pa) to the original tumor. The cancer microsphere system was shown to be compatible with an automated liquid handling system for administration of drug compounds; MDA-MB-231 microspheres were distributed in 384 well plates and treated with staurosporine (1 μM) and doxorubicin (10 μM). Expected responses were quantified using CellTiter-Glo® 3D, demonstrating initial applicability to HTS drug discovery. PDX CRC microspheres were treated with Fluorouracil (5FU) (10 to 500 μM) and displayed a decreasing trend in metabolic activity with increasing drug concentration. Providing a more physiologically relevant tumor microenvironment in a high-throughput and low-cost manner, the PF hydrogel-based cancer microspheres could potentially improve the translational success of drug candidates by providing more accurate in vitro prediction of in vivo drug efficacy. Citation Format: Elizabeth A. Lipke, Wen J. Seeto, Yuan Tian, Mohammadjafar Hashemi, Iman Hassani, Benjamin Anbiah, Nicole L. Habbit, Michael W. Greene, Dmitriy Minond, Shantanu Pradhan. Production of cancer tissue-engineered microspheres for high-throughput screening [abstract]. In: Proceedings of the American Association for Cancer Research Annual Meeting 2022; 2022 Apr 8-13. Philadelphia (PA): AACR; Cancer Res 2022;82(12_Suppl):Abstract nr 175. 
    more » « less
  4. null (Ed.)
    Background:: Sandwich structures are progressively being used in various engineering applications due to the superior bending-stiffness-to-weight ratio of these structures. We adapted a novel technique to incorporate carbon nanotubes (CNTs) and polyhedral oligomeric silsesquioxanes (POSS) into a sandwich composite structure utilizing a sonochemical and high temperature vacuum assisted resin transfer molding technique. Objective:: The objective of this work was to create a sandwich composite structure comprised of a nanophased foam core and reinforced nanophased face sheets, and to examine the thermal and mechanical properties of the structure. To prepare sandwich structure, POSS nanoparticles were sonochemically attached to CNTs and dispersed in a high temperature resin system to make the face sheet materials and also coated on expandable thermoplastic microspheres for the fabrication of foam core materials. Method:: The nanophased foam core was fabricated with POSS infused thermoplastic microspheres (Expancel) using a Tetrahedron MTP-14 programmable compression molder. The reinforced nanophased face sheet were fabricated by infusing POSS coated CNT in epoxy resin and then curing into a compression stainless steel mold. Result:: Thermal analysis of POSS-infused thermoplastic microspheres foam (TMF) showed an increase in thermal stability in both nitrogen and oxygen atmospheres, 19% increase in thermal residue were observed for 4 wt% GI-POSS TMF compared to neat TMF. Quasi-static compression results indicated significant increases (73%) in compressive modulus, and an increase (5%) in compressive strength for the 1 wt% EC-POSS/CNTs resin system. The nanophased sandwich structure constructed from the above resin system and the foam core system displayed an increase (9%) in modulus over the neat sandwich structure. Conclusion:: The incorporation of POSS-nanofillier in the foam core and POSS-coated nanotubes in the face sheet significantly improved the thermal and mechanical properties of sandwich structure. Furthermore, the sandwich structure that was constructed from nanophased resin system showed an increase in modulus, with buckling in the foam core but no visible cracking. 
    more » « less
  5. null (Ed.)
    Production-volume and cost requirements currently limit machine tool manufacturers’ ability to produce application-specific tooling with traditional methods, motivating the development of innovative manufacturing technologies. To this end, we detail a manufacturing framework for the design and production of application-specific cutting tools based on industry standard tungsten carbide-cobalt (WC-Co)-based “carbide” cutting materials using additive manufacturing (AM). Herein, novel diamond-reinforced carbide structures were designed and manufactured via AM and subsequently tested in comparison to current commercial products that are traditionally-processed. The resulting diamond-reinforced composites were free from large scale cracking and maintained microstructures with multiple reinforcing phases. Diamond incorporation had a remarkable effect on the processing, microstructure, and machining performance of the WC-Co based material in comparison to a commercial carbide cutting tool of similar composition as well as the base WC-Co matrix. Detailed microstructure and phase analysis, as well as machining experiments, demonstrate the ability to exploit laser-based directed energy deposition (DED)-based AM to create multifunctional cutting tools that can be designed to meet ever-increasing manufacturing demands across many industries. 
    more » « less