1. Twinning characteristics in rolled AZ31B magnesium alloy under three stress states

   https://doi.org/https://doi.org/10.1016/j.matchar.2021.111050  

   Carneiro, L.; Culbertson, D.; Zhu, X.; Yu, Q.; Jiang, Y. (May 2021, Materials characterization)

   null (Ed.)

   Stress-strain responses and twinning characteristics are studied for a rolled AZ31B magnesium alloy under three different stress states: tension along the normal direction (NDT), compression along the rolled direction (RDC), and torsion about the normal direction (NDTOR) using companion specimens interrupted at incremental strain levels. Tension twinning is extensively induced in twinning-favorable NDT and RDC. All the six variants of tension twin are activated under NDT, whereas a maximum of four variants is activated under RDC. Under NDTOR, both tension twins and compression twins are activated at relatively large strains and twinning occurs in a small fraction of favored grains rather than in the majority of grains. Secondary and tertiary twins are observed in the favorably-orientated grains at high strain levels. Deformation under each stress state shows three stages of strain hardening rate: fast decrease (Stage I), sequential increase (Stage II), and progressive decrease (Stage III). The increase in the hardening rate, which is more significant under NDT and RDC as compared to NDTOR, is attributed to the hardening effect of twin boundaries and twinning texture-induced slip activities. The hardening effect of twin boundaries include the dynamic Hall-Petch hardening induced by the multiplication of twin boundaries (TBs) and twin-twin boundaries (TTBs) as well as the hardening effect associated with the energetically unfavorable TTB formation. When the applied plastic strain is larger than 0.05 under NDT and RDC, the tension twin volume fraction is higher than 50%. The twinning-induced texture leads to the activation of non-basal slips mainly in the twinned volume, i.e. prismatic slips under NDT and pyramidal slips under RDC. The low work hardening under NDTOR is due to the prevailing basal slips with reduced twinning activities under NDTOR. 

   more » « less
2. Effects of initial {10-12} twins on cyclic deformation and fatigue of magnesium alloy at low strain amplitudes

   https://doi.org/https://doi.org/10.1016/j.matchar.2019.01.017  

   Wang, F.; Lui, M.; Sun, J.; Feng, M.; Jin, L.; Dong, J.; Jiang, Y. (March 2019, Materials characterization)

   An extruded AZ31B (Mg-3Al-1Zn-0.5Mn) magnesium alloy with a twin volume fraction of 60% was subjected to fully reversed strain-controlled tension-compression along the extrusion direction at strain amplitudes ranging from 0.23% to 0.45%. Dislocation slips were the dominant plastic deformation mechanisms without involving persistent twinning-detwinning. At an identical strain amplitude, the fatigue life of the pre-twinned alloy was much lower than that of the as-extruded alloy. Fatigue cracks were mainly initiated on the prismatic or prismatic-basal slip bands in the parent grains. The material volume reduction of the parent grains in the pre-twinned alloy enhanced fatigue damage. Twin cracks were not observed. 

   more » « less
3. Deformation-induced HCP phase transformation of CrCoNiSi0.3 medium-entropy alloy under high strain rate tension

   https://doi.org/10.1063/5.0202924  

   Chang, Hui; Zhang, Tuanwei; Qiao, Junwei; Liaw, Peter K; Jiao, Zhiming; Li, Zhiqiang; Quan, Long; Wang, Zhihua (April 2024, Applied Physics Letters)

   The yield strength of a CrCoNiSi0.3 medium-entropy alloy is significantly increased from 450 MPa (quasi-static, 0.001 s−1) to 1600 MPa (at a strain rate of 5000 s−1) under dynamic tension, with a considerable ductility of 60%. The high strain-rate sensitivity (SRS) of strength and work hardening is obtained, and the strength SRS reaches 0.408. The dominant deformation mechanisms are abundant multiple-twinning, increasing fractions of deformation twins and phase transformation from face-centered-cubic to hexagonal-close-packed (HCP) phases with a strain rate. A universal dislocation-hardened constitutive model considering the evolution of the twin and HCP transformation is established to predict the flow stress and microstructure evolution. 

   more » « less
4. Local microstructure and micromechanical stress evolution during deformation twinning in hexagonal polycrystals

   https://doi.org/10.1557/jmr.2020.14  

   Kumar, Mariyappan Arul; Beyerlein, Irene J. (February 2020, Journal of Materials Research)

   Deformation twinning is a prevalent plastic deformation mode in hexagonal close-packed (HCP) materials, such as magnesium, titanium, and zirconium, and their alloys. Experimental observations indicate that these twins occur heterogeneously across the polycrystalline microstructure during deformation. Morphological and crystallographic distribution of twins in a deformed microstructure, or the so-called twinning microstructure, significantly controls material deformation behavior, ductility, formability, and failure response. Understanding the development of the twinning microstructure at the grain scale can benefit design efforts to optimize microstructures of HCP materials for specific high-performance structural applications. This article reviews recent research efforts that aim to relate the polycrystalline microstructure with the development of its twinning microstructure through knowledge of local stress fields, specifically local stresses produced by twins and at twin/grain–boundary intersections on the formation and thickening of twins, twin transmission across grain boundaries, twin–twin junction formation, and secondary twinning. 

   more » « less
5. Deviations from Theoretical Orientation Relationship Along Tensile Twin Boundaries in Magnesium

   https://doi.org/10.1007/978-3-030-36647-6_20  

   Leu, Brandon; Arul Kumar, M.; Liu, Y.; Beyerlein, I. J. (April 2020, Magnesium technology)

   Deformation twinning is a prevalent mode of plastic deformation in hexagonal close packed (HCP) magnesium. Twin domains are associated with significant lattice reorientation and localized shear. The theoretical misorientation angle for the most common 1012 tensile twin in magnesium is 86.3°. Through electron backscatter diffraction characterization of twinning microstructure, we show that the twin boundary misorientation at the twin tips is approximately 85°, and it is close to the theoretical value only along the central part of the twin. The variations in twin/matrix misorientation along the twin boundary control the twin thickening process by affecting the nucleation, glide of twinning partials, and migration of twinning facets. To understand this observation, we employ a 3D crystal plasticity model with explicit twinning. The model successfully captures the experimentally observed misorientation variation, and it reveals that the twin boundary misorientation variations are governed by the local plasticity that accommodates the characteristic twin shear. 

   more » « less