Slot‐die coating is a premetered, film‐deposition process compatible with a wide range of materials. Of topical interest to precision electronics applications is the deposition of high‐cost nanomaterial dispersions over moderately sized (
- Award ID(s):
- 1728313
- NSF-PAR ID:
- 10290127
- Date Published:
- Journal Name:
- Journal of Micro and Nano-Manufacturing
- Volume:
- 8
- Issue:
- 4
- ISSN:
- 2166-0468
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
more » « less
Abstract >10 cm2 ) areas with submicron wet film thickness. In this work, a two‐dimensional (2D) model has been developed to understand the limits of the process and to predict the thinnest possible film achievable. Coined thelow‐flow limit , this parametric operating boundary presents the minimum uniform, defect‐free film achievable at a given set of liquid properties and die/substrate geometry. We investigate the low‐flow limit with a model that allows menisci to locate anywhere on the die lands, faces, and substrates with prescribed contact angles, thereby minimizing the assumptions on the bead configuration. The model is validated via comparison of its low‐flow limit predictions to published experimental data. Analysis yields insights into the mechanics of coating bead breakdown at the low‐flow limit. -
Self-sufficient and non-contact sensors play multiple roles in lunar, planetary exploration, and Earth structures. These sensors allow engineers to accurately examine structural integrity and defects on mechanical components for optimal operations. Structural integrity allows the industry to ensure the safety and capacity of key structures. Materials like α-alumina can be employed as sensors due to the photoluminescent properties that they possess. Piezospectroscopy is a non-destructive evaluation (NDE) method capable of capturing in-situ stress using α-alumina due to the chromium ion impurities that it contains. The chromium ion impurities carry spectral characteristics, that when excited with an Nd: YAG laser (532 nm), demonstrate capabilities for structural integrity monitoring. In this work, a 3D printing method is developed to autonomously create sensors that are compatible with use in space environments. The 3D printing method intends to provide the industry flexible and adaptive solutions for structural integrity monitoring. This method includes a modified Fused Deposition Method printer by exchanging its original nozzle with a syringe base nozzle. The printing parameters such as printing speed, printing bed temperature, coating thickness, and syringe volume are determined during the testing process. Challenges include achieving uniform integration and nanoparticle dispersion as well as adhesion between the matrix and the substrates. The parameters to encounter these challenges will depend on the materials used. Experiments with three different volume fractions (VF) of α-alumina within an epoxy were performed to address the printing challenges. The sensors were applied to nine specimens, three of each VF but with varying deposition rates after the mixture process. These experiments considered the mixing and deposition method while testing the dispersion within the α-alumina and the epoxy matrix. The substrates, on which the epoxy matrix was deposited, underwent a surface treatment to ensure adhesion between the substrate and the sensor matrix. During this experiment, the epoxy matrix was deposited with a syringe onto a substrate and cured at room temperature. The specimens were tested with a tensile load using an electromechanical MTS. While the samples are tensile loaded, the sensors were characterized via photoluminescent piezo spectroscopy to determine which VF demonstrates the best stress sensing capabilities, along with the adhesion between the matrix and the substrate. The data collected allows the optimal VF to be established for future applications.more » « less
-
more » « less
Abstract In this study, loose nanofiltration membranes made of polysulfone dissolved in co-solvents PolarClean and gamma-Valerolactone were prepared via slot die coating (SDC) on a roll-to-roll (R2R) system by directly coating them onto a support layer or free standing. A solution flow rate of 20 mL/min, substrate speed of 17.1 mm/s, and coating gap of 0.1 mm resulted in the formation of membranes without structural defects. Pre-wetting the support layer with dope solution minimized shrinkage of membrane layer thickness and improved interfacial adhesion. Membrane samples produced using SDC exhibited properties and performance consistent with bench-scale doctor blade extruded samples; pre-wetted and uncompressed samples (SDC-3) exhibited the highest rejection of bovine serum albumin (99.20% ± 1.31%) and along with adequate mean permeability during filtration (70.5 ± 8.33 LMH/bar). This study shows that combining sustainable materials development with SDC provides a holistic approach to membrane separations to bridge materials discovery and membrane formation.
-
more » « less
Rapid chemistry and processing development has increased the performance of perovskite solar cells (PSCs) in an unprecedented manner, yet postdeposition annealing impedes high‐throughput manufacturing. Herein, SnO2and carbon charge transport films are fabricated entirely through an integrated robotic setup utilizing inkjet printing and intense pulse light (IPL) as a high‐speed postprocess annealing method; hence, process optimization is crucial for successful fabrication of PSCs. This work investigates the role of inkjet deposition parameters as well as IPL annealing on the morphology and uniformity of films with aid of spectroscopy and spectrophotometry. Initially PSCs exceeding 13% efficiency are developed by only fabricating the SnO2film through the robotic setup, but spin coating all other films followed by IPL annealing to demonstrate successful fabrication of SnO2layer. Finally, SnO2and carbon back contact films are entirely fabricated through the integrated robotic setup in a high humid ambient environment (>60%), resulting in PSCs exceeding 5% efficiency. Unlike successful direct annealing of SnO2wet films, IPL annealing of wet carbon severely damaged the phase and morphology necessitating rapid solvent removal before IPL annealing. This work establishes pioneering steps towards utilizing IPL in an entirely automated fabrication line, allowing for scalable fabrication of PSCs through non‐roll‐to‐roll.
-
more » « less
Abstract This work studies Metal Inert Gas (MIG) based Wire Arc Additive Manufacturing (WAAM) for nanoparticle enhanced AA7075. MIG WAAM is important for production and large structures due to its high deposition rates compared to Tungsten Inert Gas (TIG) or powder-based AM processes. Both MIG and TIG take advantage of wire feedstock, which is more readily available than powdered metals since the welding technology has been established for decades. Powder based processes allow for more complicated geometries but take significantly more time to produce and can suffer from voids which lead to non-uniform part density. TIG is normally used in welding of aluminum because it results in fewer defects, but the TiC/TiB2 nanoparticles eliminate solidification cracking normally associated with high strength aluminum alloys during welding. Porosity is another problem faced when welding aluminum, which can be affected by many things including deposition parameters, atmosphere and even the welding equipment used. Effects of different deposition parameters have been comprehensively studied including the deposition geometry and metallurgical properties. The process is also monitored with current/voltage measurement and high-speed imaging to understand the droplet transfer mode and molten pool development. The results are used to optimize process parameters to achieve the fewest defects possible while comparing different metal transfer modes. Multi-scale characterizations will be performed to examine the porosity distribution, solidification mode and grain size through optical microscopy. Future works will explore the distribution of secondary phases, precipitates, and nanoparticles through scanning electron microscopy (SEM) as well as conducting some mechanical testing of the as built structures such as hardness mapping and tensile tests.
- Free Publicly Accessible Full Text
-
Accepted Manuscript1.0
- Journal Article:
- https://doi.org/10.1115/1.4049668