Title: Structural, Optical and Mechanical Properties of Nanocrystalline Molybdenum Thin Films Deposited under Variable Substrate Temperature
Molybdenum (Mo), which is one among the refractory metals, is a promising material with a wide variety of technological applications in microelectronics, optoelectronics, and energy conversion and storage. However, understanding the structure–property correlation and optimization at the nanoscale dimension is quite important to meet the requirements of the emerging nanoelectronics and nanophotonics. In this context, we focused our efforts to derive a comprehensive understanding of the nanoscale structure, phase, and electronic properties of nanocrystalline Mo films with variable microstructure and grain size. Molybdenum films were deposited under varying temperature (25–500 °C), which resulted in Mo films with variable grain size of 9–22 nm. The grazing incidence X-ray diffraction analyses indicate the (110) preferred growth behavior the Mo films, though there is a marked decrease in hardness and elastic modulus values. In particular, there is a sizable difference in maximum and minimum elastic modulus values; the elastic modulus decreased from ~460 to 260–280 GPa with increasing substrate temperature from 25–500 °C. The plasticity index and wear resistance index values show a dramatic change with substrate temperature and grain size. Additionally, the optical properties of the nanocrystalline Mo films evaluated by spectroscopic ellipsometry indicate a marked dependence on the growth temperature and grain size. This dependence on grain size variation was particularly notable for the refractive index where Mo films with lower grain size fell in a range between ~2.75–3.75 across the measured wavelength as opposed to the range of 1.5–2.5 for samples deposited at temperatures of 400–500 °C, where the grain size is relatively higher. The conductive atomic force microscopy (AFM) studies indicate a direct correlation with grain size variation and grain versus grain boundary conduction; the trend noted was improved electrical conductivity of the Mo films in correlation with increasing grain size. The combined ellipsometry and conductive AFM studies allowed us to optimize the structure–property correlation in nanocrystalline Mo films for application in electronics and optoelectronics.  more » « less
Award ID(s):
1827745
NSF-PAR ID:
10331316
Author(s) / Creator(s):
; ; ; ;
Date Published:
Journal Name:
Materials
Volume:
15
Issue:
3
ISSN:
1996-1944
Page Range / eLocation ID:
754
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. Abstract

    This work reports on the correlation between structure, surface/interface morphology and mechanical properties of pulsed laser deposited (PLD)β-Ga2O3films on transparent quartz substrates. By varying the deposition temperature in the range of 25 °C–700 °C, ∼200 nm thick Ga2O3films with variable microstructure and amorphous-to-nanocrystalline nature were produced onto quartz substrates by PLD. The Ga2O3films deposited at room temperature were amorphous; nanocrystalline Ga2O3films were realized at 700 °C. The interface microstructure is characterized with a typical nano-columnar morphology while the surface exhibits the uniform granular morphology. Corroborating with structure and surface/interface morphology, and with increasing deposition temperature, tunable mechanical properties were seen in PLD Ga2O3films. At 700 °C, for nanocrystalline Ga2O3films, the dense grain packing reduces the elastic modulus Erwhile improving the hardness. The improved crystallinity at elevated temperatures coupled with nanocrystallinity, theβ-phase stabilization is accounted for the observed enhancement in the mechanical properties of PLD Ga2O3films. The structure-morphology-mechanical property correlation in nanocrystalline PLDβ-Ga2O3films deposited on quartz substrates is discussed in detail.

     
    more » « less
  2. Many biological lab-on-a-chip applications require electrical and optical manipulation as well as detection of cells and biomolecules. This provides an intriguing challenge to design robust microdevices that resist adverse electrochemical side reactions yet achieve optical transparency. Physical isolation of biological samples from microelectrodes can prevent contamination, electrode fouling, and electrochemical byproducts; thus this manuscript explores hafnium oxide (HfO2) films - originating from traditional transistor applications – for suitability in electrokinetic microfluidic devices for biological applications. HfO2 films with deposition times of 6.5, 13, and 20 min were sputter deposited onto silicon and glass substrates. The structural, optical, and electrical properties of the HfO2 films were investigated using atomic force microscopy (AFM), X-ray diffraction, energy dispersive X-ray spectroscopy, Fourier transform infrared spectroscopy, ellipsometry, and capacitance voltage. Electric potential simulations of the HfO2 films and a biocompatibility study provided additional insights. Film grain size after corrosive Piranha treatment was observed via AFM. The crystalline structure investigated via X-ray diffraction revealed all films exhibited the (111) characteristic peak with thicker films exhibiting multiple peaks indicative of anisotropic structures. Energy dispersive X-ray spectroscopy via field emission scanning electron microscopy and Fourier transform infrared spectroscopy both corroborated the atomic ratio of the films as HfO2. Ellipsometry data from Si yielded thicknesses of 58, 127, and 239 nm and confirmed refractive index and extinction coefficients within the normal range for HfO2; glass data yielded unreliable thickness verifications due to film and substrate transparency. Capacitance-voltage results produced an average dielectric constant of 20.32, and the simulations showed that HfO2 dielectric characteristics were sufficient to electrically passivate planar microelectrodes. HfO2 biocompatibility was determined with human red blood cells by quantifying the hemolytic potential of the HfO2 films. Overall results support hafnium oxide as a viable passivation material for biological lab-on-a-chip applications. 
    more » « less
  3. Abstract

    This work demonstrates the processing, modeling, and characterization of nanocrystalline refractory metal tantalum (Ta) as a new structural material for microelectromechanical system (MEMS) thermal actuators (TAs). Nanocrystalline Ta films have a coefficient of thermal expansion (CTE) and Young’s modulus comparable to bulk Ta but an approximately ten times greater yield strength. The mechanical properties and grain size remain stable after annealing at temperatures as high as 1000 °C. Ta has a high melting temperature (Tm = 3017 °C) and a low resistivity (ρ = 20 µΩ cm). Compared to TAs made from the dominant MEMS material, polycrystalline silicon (polysilicon,Tm = 1414 °C,ρ = 2000 µΩ cm), Ta TAs theoretically require less than half the power input for the same force and displacement, and their temperature change is half that of polysilicon. Ta TAs operate at a voltage 16 times lower than that of other TAs, making them compatible with complementary metal oxide semiconductors (CMOS). We selectα-phase Ta and etch 2.5-μm-thick sputter-deposited films with a 1 μm width while maintaining a vertical sidewall profile to ensure in-plane movement of TA legs. This is 25 times thicker than the thickest reactive-ion-etchedα-Ta reported in the technical literature. Residual stress sensitivities to sputter parameters and to hydrogen incorporation are investigated and controlled. Subsequently, a V-shaped TA is fabricated and tested in air. Both conventional actuation by Joule heating and passive self-actuation are as predicted by models.

     
    more » « less
  4. Nanostructured molybdenum disulfide (MoS2) thin films were grown on a nanohole-patterned silicon substrate using plasma-enhanced atomic layer deposition. A nanoscale hole-patterned silicon substrate was fabricated for the growth of MoS2 film using the self-assembly-based nanofabrication method. The nanoscale holes can significantly increase the surface area of the substrate while the formation and growth of nanostructures normally start at the surface of the substrate. Hydrogen sulfide (H2S) gas was used as the S source in the growth of molybdenum disulfide (MoS2) while molybdenum (V) chloride (MoCl5) powder was used as the Mo source. The MoS2 film had a stoichiometric ratio of 1 (Mo) to 2 (S), and had peaks of E12g and A1g, which represent the in-plane and out-plane vibration modes of the Mo–S bond, respectively. It was found that the MoS2 film grown in the nanoscale hole, especially at the wall of the hole, has more hexagonal-like structures due to the effects of nanoscale space confinement and the nanoscale interface although the film shows an amorphous structure. Post-growth high-temperature annealing ranging from 800 to 900 °C produced local crystalline structures in the film, which are compatible with those reported by other researchers. 
    more » « less
  5. The microstructural transformations of binary nanometallic multilayers (NMMs) to equiaxed nanostructured materials were explored by characterizing a variety of nanoscale multilayer films. Four material systems of multilayer films, Hf-Ti, Ta-Hf, W-Cr, and Mo-Au, were synthesized by magnetron sputtering, heat treated at 1000 °C, and subsequently characterized by transmission electron microscopy. Binary systems were selected based on thermodynamic models predicting stable nanograin formation with similar global compositions around 20–30 at.%. All NMMs maintained nanocrystalline grain sizes after evolution into an equiaxed structure, where the systems with highly mobile incoherent interfaces or higher energy interfaces showed a more significant increase in grain size. Furthermore, varying segregation behaviors were observed, including grain boundary (GB) segregation, precipitation, and intermetallic formation depending on the material system selected. The pathway to tailored microstructures was found to be governed by key mechanisms and factors as determined by a film’s initial characteristics, including global and local composition, interface energy, layer structure, and material selection. This work presents a global evaluation of NMM systems and demonstrates their utility as foundation materials to promote tailored nanomaterials. 
    more » « less