Title: Radiation Damage in the Ultra-Wide Bandgap Semiconductor Ga 2 O 3
We present a review of the published experimental and simulation radiation damage results in Ga 2 O 3 . All of the polytypes of Ga 2 O 3 are expected to show similar radiation resistance as GaN and SiC, considering their average bond strengths. However, this is not enough to explain the orders of magnitude difference of the relative resistance to radiation damage of these materials compared to GaAs and dynamic annealing of defects is much more effective in Ga 2 O 3 . It is important to examine the effect of all types of radiation, given that Ga 2 O 3 devices will potentially be deployed both in space and terrestrial applications. Octahedral gallium monovacancies are the main defects produced under most radiation conditions because of the larger cross-section for interaction compared to oxygen vacancies. Proton irradiation introduces two main paramagnetic defects in Ga 2 O 3 , which are stable at room temperature. Charge carrier removal can be explained by Fermi-level pinning far from the conduction band minimum due to gallium interstitials (Ga i ), vacancies (V Ga ), and antisites (Ga O ). One of the most important parameters to establish is the carrier removal rate for each type of radiation, since this directly impacts the current in devices such as transistors or rectifiers. When compared to the displacement damage predicted by the Stopping and Range of Ions in Matter(SRIM) code, the carrier removal rates are generally much lower and take into account the electrical nature of the defects created. With few experimental or simulation studies on single event effects (SEE) in Ga 2 O 3 , it is apparent that while other wide bandgap semiconductors like SiC and GaN are robust against displacement damage and total ionizing dose, they display significant vulnerability to single event effects at high Linear Energy Transfer (LET) and at much lower biases than expected. We have analyzed the transient response of β -Ga 2 O 3 rectifiers to heavy-ion strikes via TCAD simulations. Using field metal rings improves the breakdown voltage and biasing those rings can help control the breakdown voltage. Such biased rings help in the removal of the charge deposited by the ion strike.  more » « less
Award ID(s):
1856662 2015795
NSF-PAR ID:
10353825
Author(s) / Creator(s):
; ; ; ; ; ; ; ; ; ; ; ; ;
Date Published:
Journal Name:
ECS Journal of Solid State Science and Technology
Volume:
11
Issue:
9
ISSN:
2162-8769
Page Range / eLocation ID:
095001
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. Large area (1 mm2) vertical NiO/βn-Ga2O/n+Ga2O3heterojunction rectifiers are demonstrated with simultaneous high breakdown voltage and large conducting currents. The devices showed breakdown voltages (VB) of 3.6 kV for a drift layer doping of 8 × 1015cm−3, with 4.8 A forward current. This performance is higher than the unipolar 1D limit for GaN, showing the promise ofβ-Ga2O3for future generations of high-power rectification devices. The breakdown voltage was a strong function of drift region carrier concentration, with VBdropping to 1.76 kV for epi layer doping of 2 × 1016cm−3. The power figure-of-merit, VB2/RON, was 8.64 GW·cm−2, where RONis the on-state resistance (1.5 mΩ cm2). The on-off ratio switching from 12 to 0 V was 2.8 × 1013, while it was 2 × 1012switching from 100 V. The turn-on voltage was 1.8 V. The reverse recovery time was 42 ns, with a reverse recovery current of 34 mA.

     
    more » « less
  2. Neutrons generated through charge-exchange9Be (p; ni)9Be reactions, with energies ranging from 0–33 MeV and an average energy of ∼9.8 MeV were used to irradiate conventional Schottky Ga2O3rectifiers and NiO/Ga2O3p-n heterojunction rectifiers to fluences of 1.1–2.2 × 1014cm−2. The breakdown voltage was improved after irradiation for the Schottky rectifiers but was highly degraded for their NiO/Ga2O3counterparts. This may be a result of extended defect zones within the NiO. After irradiation, the switching characteristics were degraded and irradiated samples of both types could not survive switching above 0.7 A or 400 V, whereas reference samples were robust to 1 A and 1 kV. The carrier removal rate in both types of devices was ∼45 cm−1. The forward currents and on-state resistances were only slightly degraded by neutron irradiation.

     
    more » « less
  3. The effect of doping in the drift layer and the thickness and extent of extension beyond the cathode contact of a NiO bilayer in vertical NiO/β-Ga2O3 rectifiers is reported. Decreasing the drift layer doping from 8 × 1015 to 6.7 × 1015 cm−3 produced an increase in reverse breakdown voltage (VB) from 7.7 to 8.9 kV, the highest reported to date for small diameter devices (100 μm). Increasing the bottom NiO layer from 10 to 20 nm did not affect the forward current–voltage characteristics but did reduce reverse leakage current for wider guard rings and reduced the reverse recovery switching time. The NiO extension beyond the cathode metal to form guard rings had only a slight effect (∼5%) in reverse breakdown voltage. The use of NiO to form a pn heterojunction made a huge improvement in VB compared to conventional Schottky rectifiers, where the breakdown voltage was ∼1 kV. The on-state resistance (RON) was increased from 7.1 m Ω cm2 in Schottky rectifiers fabricated on the same wafer to 7.9 m Ω cm2 in heterojunctions. The maximum power figure of merit (VB)2/RON was 10.2 GW cm−2 for the 100 μm NiO/Ga2O3 devices. We also fabricated large area (1 mm2) devices on the same wafer, achieving VB of 4 kV and 4.1 A forward current. The figure-of-merit was 9 GW  cm−2 for these devices. These parameters are the highest reported for large area Ga2O3 rectifiers. Both the small area and large area devices have performance exceeding the unipolar power device performance of both SiC and GaN. 
    more » « less
  4. NiO/β-Ga 2 O 3 vertical rectifiers exhibit near-temperature-independent breakdown voltages ( V B ) of >8 kV to 600 K. For 100 μm diameter devices, the power figure of merit ( V B ) 2 / R ON , where R ON is the on-state resistance, was 9.1 GW cm −2 at 300 K and 3.9 GW cm −2 at 600 K. By sharp contrast, Schottky rectifiers fabricated on the same wafers show V B of ∼1100 V at 300 K, with a negative temperature coefficient of breakdown of 2 V K −1 . The corresponding figures of merit for Schottky rectifiers were 0.22 GW cm −2 at 300 K and 0.59 MW cm −2 at 600 K. The on–off ratio remained >10 10 up to 600 K for heterojunction rectifiers but was 3 orders of magnitude lower over the entire temperature range for Schottky rectifiers. The power figure of merit is higher by a factor of approximately 6 than the 1-D unipolar limit of SiC. The reverse recovery times were ∼26 ± 2 ns for both types of devices and were independent of temperature. We also fabricated large area, 1 mm 2 rectifiers. These exhibited V B of 4 kV at 300 K and 3.6 kV at 600 K. The results show the promise of using this transparent oxide heterojunction for high temperature, high voltage applications. 
    more » « less
  5. In this paper, the short circuit ruggedness of Gallium Oxide (Ga 2 O 3 ) vertical FinFET is studied using Technology Computer-Aided-Design (TCAD) simulations. Ga 2 O 3 is an emerging ultra-wide bandgap material and Ga 2 O 3 vertical FinFET can achieve the normally-off operation for high voltage applications. Ga 2 O 3 has a relatively low thermal conductivity and, thus, it is critical to explore the design space of Ga 2 O 3 vertical FinFETs to achieve an acceptable short-circuit capability for power applications. In this study, appropriate TCAD models and parameters calibrated to experimental data are used. For the first time, the breakdown voltage simulation accuracy of Ga 2 O 3 vertical FinFETs is studied systematically. It is found that a background carrier generation rate between 10 5 cm −3 s −1 and 10 12 cm −3 s −1 is required in simulation to obtain correct results. The calibrated and robust setup is then used to study the short circuit withstand time (SCWT) of an 800 V-rated Ga 2 O 3 vertical FinFET with different inter-fin architectures. It is found that, due to the high thermal resistance in Ga 2 O 3 , to achieve an SCWT >1 μ s, low gate overdrive is needed which increases R on,sp by 66% and that Ga 2 O 3 might melt before the occurrence of thermal runaway. These results provide important guidance for developing rugged Ga 2 O 3 power transistors. 
    more » « less