Abstract All‐solid‐state flexible asymmetric supercapacitors (ASCs) are developed by utilization of graphene nanoribbon (GNR)/Co0.85Se composites as the positive electrode, GNR/Bi2Se3composites as the negative electrode, and polymer‐grafted‐graphene oxide membranes as solid‐state electrolytes. Both GNR/Co0.85Se and GNR/Bi2Se3composite electrodes are developed by a facile one‐step hydrothermal growth method from graphene oxide nanoribbons as the nucleation framework. The GNR/Co0.85Se composite electrode exhibits a specific capacity of 76.4 mAh g−1at a current density of 1 A g−1and the GNR/Bi2Se3composite electrode exhibits a specific capacity of 100.2 mAh g−1at a current density of 0.5 A g−1. Moreover, the stretchable membrane solid‐state electrolytes exhibit superior ionic conductivity of 108.7 mS cm−1. As a result, the flexible ASCs demonstrate an operating voltage of 1.6 V, an energy density of 30.9 Wh kg−1at the power density of 559 W kg−1, and excellent cycling stability with 89% capacitance retention after 5000 cycles. All these results demonstrate that this study provides a simple, scalable, and efficient approach to fabricate high performance flexible all‐solid‐state ASCs for energy storage.
more »
« less
Amphipathic Binder Integrating Ultrathin and Highly Ion‐Conductive Sulfide Membrane for Cell‐Level High‐Energy‐Density All‐Solid‐State Batteries
Abstract Current sulfide solid‐state electrolyte (SE) membranes utilized in all‐solid‐state lithium batteries (ASLBs) have a high thickness (0.5–1.0 mm) and low ion conductance (<25 mS), which limit the cell‐level energy and power densities. Based on ethyl cellulose's unique amphipathic molecular structure, superior thermal stability, and excellent binding capability, this work fabricates a freestanding SE membrane with an ultralow thickness of 47 µm. With ethyl cellulose as an effective disperser and a binder, the Li6PS5Cl is uniformly dispersed in toluene and possesses superior film formability. In addition, an ultralow areal resistance of 4.32 Ω cm−2and a remarkable ion conductance of 291 mS (one order higher than the state‐of‐the‐art sulfide SE membrane) are achieved. The ASLBs assembled with this SE membrane deliver cell‐level high gravimetric and volumetric energy densities of 175 Wh kg−1and 675 Wh L−1, individually.
more »
« less
- Award ID(s):
- 1924534
- PAR ID:
- 10367333
- Publisher / Repository:
- Wiley Blackwell (John Wiley & Sons)
- Date Published:
- Journal Name:
- Advanced Materials
- Volume:
- 33
- Issue:
- 52
- ISSN:
- 0935-9648
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Abstract Sulfide solid‐state electrolytes have remarkable ionic conductivity and low mechanical stiffness but suffer from relatively narrow electrochemical and chemical stability with electrodes. Therefore, pairing sulfide electrolytes with the proper cathode is crucial in developing stable all‐solid‐state Li batteries (ASLBs). Herein, one type of thioantimonate ion conductor, Li6+xGexSb1−xS5I, with different compositions is systematically synthesized and studied, among these compositions, an outstanding ionic conductivity of 1.6 mS cm−1is achieved with Li6.6Ge0.6Sb0.4S5I. To improve the energy density and advance the interface compatibility, a metal sulfide FeS2cathode with a high theoretical capacity (894 mAh g−1) and excellent compatibility with sulfide electrolytes is coupled with Li6.6Ge0.6Sb0.4S5I in ASLBs without additional interface engineering. The structural stabilities of Li6.6Ge0.6Sb0.4S5I and FeS2during cycling are characterized by operando energy dispersive X‐ray diffraction, which allows rapid collection of structural data without redesigning or disassembling the sealed cells and risking contamination by air. The electrochemical stability is assessed, and a safe operating voltage window ranging from 0.7≈2.4 V (vs. In–Li) is confirmed. Due to the solid confinement in the ASLBs, the Fe0aggregation and polysulfides shuttle effects are well addressed. The ASLBs exhibit an outstanding initial capacity of 715 mAh g−1at C/10 and are stable for 220 cycles with a high capacity retention of 84.5% at room temperature.more » « less
-
Sulfide solid-state electrolyte (SE) possesses high room-temperature ionic conductivity. However, fabrication of the free-standing, sheet-type thin sulfide SE film electrolyte to enable all-solid-state batteries to deliver high energy and power density remains challenging. Herein we show that argyrodite sulfide (Li6PS5Cl) SE can be slurry cast to form free-standing films with low (≤5 wt%) loadings of poly(isobutylene) (PIB) binder. Two factors contribute to a lower areal specific resistance (ASR) of the thin film SEs benchmarked to the pristine powder pellet SSE counterparts: i) 1–2 orders reduced thickness and ii) reasonably comparable ionic conductivity at room temperature after the isostatic pressing process. Nevertheless, an increasing polymer binder loading inevitably introduced voids in the thin film SEs, compromising anode/electrolyte interfacial ion transport. Our findings highlight that electrolyte/electrode interfacial stability, as well as the selection of slurry components, including sulfide SE, binder, and solvent, play essential roles in thin film sulfide electrolyte development.more » « less
-
Abstract Sulfide solid-state electrolytes (SSEs) are promising candidates to realize all solid-state batteries (ASSBs) due to their superior ionic conductivity and excellent ductility. However, their hypersensitivity to moisture requires processing environments that are not compatible with today’s lithium-ion battery manufacturing infrastructure. Herein, we present a reversible surface modification strategy that enables the processability of sulfide SSEs (e. g., Li6PS5Cl) under humid ambient air. We demonstrate that a long chain alkyl thiol, 1-undecanethiol, is chemically compatible with the electrolyte with negligible impact on its ion conductivity. Importantly, the thiol modification extends the amount of time that the sulfide SSE can be exposed to air with 33% relative humidity (33% RH) with limited degradation of its structure while retaining a conductivity of above 1 mS cm-1for up to 2 days, a more than 100-fold improvement in protection time over competing approaches. Experimental and computational results reveal that the thiol group anchors to the SSE surface, while the hydrophobic hydrocarbon tail provides protection by repelling water. The modified Li6PS5Cl SSE maintains its function after exposure to ambient humidity when implemented in a Li0.5In | |LiNi0.8Co0.1Mn0.1O2ASSB. The proposed protection strategy based on surface molecular interactions represents a major step forward towards cost-competitive and energy-efficient sulfide SSE manufacturing for ASSB applications.more » « less
-
Abstract Ion‐insertion capacitors show promise to bridge the gap between supercapacitors of high power densities and batteries of high energy densities. While research efforts have primarily focused on Li+‐based capacitors (LICs), Na+‐based capacitors (SICs) are theoretically cheaper and more sustainable. Owing to the larger size of Na+compared to Li+, finding high‐rate anode materials for SICs has been challenging. Herein, an SIC anode architecture is reported consisting of TiO2nanoparticles anchored on a sheared‐carbon nanotubes backbone (TiO2/SCNT). The SCNT architecture provides advantages over other carbon architectures commonly used, such as reduced graphene oxide and CNT. In a half‐cell, the TiO2/SCNT electrode shows a capacity of 267 mAh g−1at a 1 C charge/discharge rate and a capacity of 136 mAh g−1at 10 C while maintaining 87% of initial capacity over 1000 cycles. When combined with activated carbon (AC) in a full cell, an energy density and power density of 54.9 Wh kg−1and 1410 W kg−1, respectively, are achieved while retaining a 90% capacity retention over 5000 cycles. The favorable rate capability, energy and power density, and durability of the electrode is attributed to the enhanced electronic and Na+conductivity of the TiO2/SCNT architecture.more » « less