Abstract Entropy‐stabilized oxide (ESO) research has primarily focused on discovering unprecedented structures, chemistries, and properties in the single‐phase state. However, few studies discuss the impacts of entropy stabilization and secondary phases on functionality and in particular, electrical conductivity. To address this gap, electrical transport mechanisms in the canonical ESO rocksalt (Co,Cu,Mg,Ni,Zn)O are assessed as a function of secondary phase content. When single‐phase, the oxide conducts electrons via Cu+/Cu2+small polarons. After 2 h of heat treatment, Cu‐rich tenorite secondary phases form at some grain boundaries (GBs), enhancing grain interior electronic conductivity by tuning defect chemistry toward higher Cu+carrier concentrations. 24 h of heat treatment yields Cu‐rich tenorite at all GBs, followed by the formation of anisotropic Cu‐rich tenorite and equiaxed Co‐rich spinel secondary phases in grains, further enhancing grain interior electronic conductivity but slowing electronic transport across the tenorite‐rich GBs. Across all samples, the total electrical conductivity increases (and decreases reversibly) by four orders of magnitude with heat‐treatment‐induced phase transformation by tuning the grains’ defect chemistry toward higher carrier concentration and lower migration activation energy. This work demonstrates the potential to selectively grow secondary phases in ESO grains and at GBs, thereby tuning the electrical properties using microstructure design, nanoscale engineering, and heat treatment, paving the way to develop many novel materials.
more »
« less
Nucleation and growth behavior of multicomponent secondary phases in entropy-stabilized oxides
Abstract The rocksalt structured (Co,Cu,Mg,Ni,Zn)O entropy-stabilized oxide (ESO) exhibits a reversible phase transformation that leads to the formation of Cu-rich tenorite and Co-rich spinel secondary phases. Using atom probe tomography, kinetic analysis, and thermodynamic modeling, we uncover the nucleation and growth mechanisms governing the formation of these two secondary phases. We find that these phases do not nucleate directly, but rather they first form Cu-rich and Co-rich precursor phases, which nucleate in regions rich in Cu and cation vacancies, respectively. These precursor phases then grow through cation diffusion and exhibit a rocksalt-like crystal structure. The Cu-rich precursor phase subsequently transforms into the Cu-rich tenorite phase through a structural distortion-based transformation, while the Co-rich precursor phase transforms into the Co-rich spinel phase through a defect-mediated transformation. Further growth of the secondary phases is controlled by cation diffusion within the primary rocksalt phase, whose diffusion behavior resembles other common rocksalt oxides. Graphical abstract
more »
« less
- Award ID(s):
- 2011967
- PAR ID:
- 10377036
- Publisher / Repository:
- Cambridge University Press (CUP)
- Date Published:
- Journal Name:
- Journal of Materials Research
- Volume:
- 38
- Issue:
- 1
- ISSN:
- 0884-2914
- Page Range / eLocation ID:
- p. 198-214
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Abstract Rationalizing synthetic pathways is crucial for material design and property optimization, especially for polymorphic and metastable phases. Over‐stoichiometric rocksalt (ORX) compounds, characterized by their face‐sharing configurations, are a promising group of materials with unique properties; however, their development is significantly hindered by challenges in synthesizability. Here, taking the recently identified Li superionic conductor, over‐stoichiometric rocksalt Li–In–Sn–O (o‐LISO) material as a prototypical ORX compound, the mechanisms of phase formation are systematically investigated. It is revealed that the spinel‐like phase with unconventional stoichiometry forms as coherent precipitate from the high‐temperature‐stabilized cation‐disordered rocksalt phase upon fast cooling. This process prevents direct phase decomposition and kinetically locks the system in a metastable state with the desired face‐sharing Li configurations. This insight enables us to enhance the ionic conductivity of o‐LISO to be >1 mS cm−1at room temperature through low‐temperature post‐annealing. This work offers insights into the synthesis of ORX materials and highlights important opportunities in this new class of materials.more » « less
-
Despite significant interest in their functional properties, the mechanical behavior of high-entropy oxides (HEOs) is not well studied, particularly at elevated temperatures. Bulk (Co,Cu,Mg,Ni,Zn)O (transition metal (TM)-HEO) samples were deformed under compression at applied stresses and temperatures ranging from 5 to 31 MPa and 600 to 850 °C, respectively. All of the deformation conditions result in creep stress exponents of n < 3, indicating that TM-HEO exhibits superplastic deformation. A transition from structural to solution-precipitation-based superplasticity is observed during deformation above 650 °C. Additionally, TM-HEO exhibits shear-thickening behavior when deformed at stresses above 9 MPa. The formation and behavior of a Cu-rich tenorite secondary phase during deformation is identified as a key factor underpinning the deformation mechanisms. The microstructure and phase state of TM-HEO before deformation also influenced the behavior, with finer grain sizes and increasing concentrations of Cu-rich tenorite, resulting in the increased prevalence of solution-precipitation deformation. While complex, the results of this study indicate that TM-HEO deforms through known superplastic deformation mechanisms. Superplasticity is a highly efficient manufacturing method and could prove to be a valuable strategy for forming HEO ceramics into complex geometries.more » « less
-
High‐entropy oxides (HEOs) are being extensively studied for various functional applications, but there is limited research into the mechanical behavior of these materials, especially at elevated temperatures. Bulk (Co, Cu, Mg, Ni, Zn)O (transition metal (TM)‐HEO) samples are formed into dome shapes at 800 °C and 70 kPa. Deformation experiments and finite element analysis (FEA) reveal that TM‐HEO has a creep stress exponent ofn = 0.6, indicating that TM‐HEO deforms through superplastic deformation and exhibits shear‐thickening behavior. Comparisons of experimental strain rates to those calculated using existing superplasticity mechanism models signify that TM‐HEO deforms through grain boundary sliding accommodated by a solution‐precipitation mechanism from a secondary phase. A Cu‐rich tenorite phase, commonly observed in the grain boundaries of TM‐HEO, is proposed as the secondary phase facilitating deformation. It is important to highlight here that the superplastic deformation behavior in TM‐HEO is active under modest temperature and pressure conditions, as noted above. Low‐temperature superplastic deformation will provide a powerful method of manufacturing HEO ceramics into net shape parts, greatly expanding their potential applications.more » « less
-
Abstract One hypothesized mechanism that triggers deep‐focus earthquakes in oceanic subducting slabs below ∼300 km depth is transformational faulting due to the olivine‐to‐spinel phase transition. This study uses finite element modeling to investigate phase transformation‐induced stress redistribution and material weakening in olivine. A thermodynamically consistent constitutive model is developed to capture the evolution of phase transformation in olivine under different pressure and temperature conditions. The overall numerical model enables considering multiscale material features, including the polycrystalline structure, mesoscale heterogeneity, and various phases or variants of phases at the microscopic level, and accounts for viscoplastic behaviors with thermo‐mechanical coupling effects. The model is validated with several benchmarks, including a phase diagram of phase transformation from olivine to spinel. The validated model is used to study the interactive behaviors between defects (heterogeneity) and phase transformation. The simulation results reveal that spinel formation under pressure initiates near inclusions and along the grain boundaries, consistent with experimental observations. At lower temperatures, the transformation leads to the formation of thin conjugate bands of spinel diagonal to the compression loading direction. Local stress analysis along these bands also suggests the initiation of faulting. In contrast, the numerical results at higher transformation rates show that significant spinel formation occurs over a larger area at elevated temperatures, leading to ductile behavior, which agrees with experimental findings. Numerical simulation of multiple inclusions under confined pressure also shows the formation of a network of spinel bands resembling phase‐transformation patterns observed in the laboratory experiments. Additionally, stress softening patterns due to phase transformation are similar to experimental observations.more » « less