Title: Crack initiation, propagation, and arrest in sintering powder aggregates
Abstract

Cracking during sintering is a common problem in powder processing and is usually caused by constraint that prevents the sintering material from shrinking in one or more directions. Different factors influence sintering‐induced cracking, including temperature schedule, packing density, and specimen geometry. Here we use the discrete element method to directly observe the stress distribution and sinter‐cracking behavior in edge notched panels sintered under a uniaxial restraint. This geometry allows an easy comparison with traditional fracture mechanics parameters, facilitating analysis of sinter‐cracking behavior. We find that cracking caused by self‐stress during sintering resembles the growth of creep cracks in fully dense materials. By deriving the constrained densification rate from the appropriate constitutive equations, we discover that linear shrinkage transverse to the loading axis is accelerated by a contribution from the effective Poisson's ratio of a sintering solid. Simulation of different notch geometries and initial relative densities reveals conditions that favor densification and minimize crack growth, alluding to design methods for avoiding cracking in actual sintering processes. We combine the far‐field stress and crack length to compute the net section stress, finding that it characterizes the stress profile between the notches and correlates with the sinter‐crack growth rate, demonstrating its potential to quantitatively describe sinter‐cracking.

  more » « less
Award ID(s):
1826064
PAR ID:
10377222
Author(s) / Creator(s):
 ;  ;  
Publisher / Repository:
Wiley-Blackwell
Date Published:
Journal Name:
Journal of the American Ceramic Society
Volume:
103
Issue:
9
ISSN:
0002-7820
Page Range / eLocation ID:
p. 4754-4773
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. ( , Progress in Additive Manufacturing 2020)
    Shamsaei ‪Nima, Seifi ‪Mohsen (Ed.)
    Binder jet three-dimensional (3D) printing is a scalable, potentially low-cost additive manufacturing route able to process materials not attainable to other techniques, especially nonweldable materials. It relies on postprocess sintering to achieve final properties but encounters problems with distortion and cracking during sintering. The present work seeks to understand how part design geometry and 3D printing build orientation influence cracking during sintering, with the goal of mitigating the problem. In situ monitoring experiments reveal how sinter-cracks initiate and grow in 3D-printed notched panel specimens during densification. Different design geometries and build directions are tested to identify sinter-crack-resistant regimes. 
    more » « less
  2. ; ; ; ; ( , Journal of the American Ceramic Society)
    Commonly used constitutive laws for crystalline and viscous materials have been compared to predict the densification behavior under hot‐pressing and sinter‐forging. Experimental results, from literature for one loading condition, have been used to extract the constitutive laws for amorphous and crystalline materials and, these in‐turn, have been used to predict behavior under a different set of loading conditions. Ideally, the constitutive parameters obtained from one set of loading conditions and thermal history should apply to a different set of conditions. However, there is a lack of systematic experimental studies in which this can be checked. In this paper, we use constitutive parameters obtained from one set of conditions to predict the densification response under a different set of loading conditions. For both sintering of amorphous and crystalline materials, we use two different constitutive parameters and compare the predictions of these for the case where experimental results are not available. In addition, the effect of temperature on densification behavior for stress‐assisted sintering has been investigated. It is shown that the two commonly used constitutive models for viscous sintering (Scherer and Skorohod–Olevsky) predict similar behavior for amorphous materials. However, for crystalline materials, the predictions of the Riedel–Svoboda and the Kuhn–Sofronis–McMeeking (KSM) models are different. Finally, it is shown that the dependence of the normalized densification on temperature, under constant heating rate conditions, with parameters obtained from isothermal experiments, is a good test for the models. 
    more » « less
  3. ; ; ; ( , Journal of the American Ceramic Society)
    Abstract

    This work investigates the effects of doping on both the thermodynamics and kinetics of sintering in aluminum‐doped yttrium oxide nanoparticles (Al‐doped Y2O3), with the objective of delineating their interdependent effects at different stages of the process. Direct measurements of surface and grain boundary energies using differential scanning calorimetry showed that Al‐doping decreases both interfacial energies, leading to an increase in dihedral angle (from 152.7 ± 5.6° to 165.8 ± 5.5°) and, therefore, sintering stress. Densification and grain growth analyses showed that despite this increase in sintering stress, the onset of sintering is delayed for the Al‐doped samples, demonstrating that a large dihedral angle is a necessary but not sufficient condition for densification. The measurements of activation energies for densification and grain growth point out that Al suppresses grain boundary mobility by increasing the activation energy from 400 to 448 kJ/mol, hindering densification at the intermediate stages of sintering. At temperatures above 1150℃, grain growth is activated in the Al‐doped samples, which rapidly releases the accumulated sintering stress and exhibits a higher densification rate than in undoped Y2O3. This study demonstrates a complex interconnectivity between the thermodynamics and kinetics at different temperature ranges of sintering and reinforces the need for a comprehensive description for proper design of sintering aids.

     
    more » « less
  4. ; ; ; ( , Advanced Materials Technologies)
    Abstract

    Nanoparticle 3D printing and sintering is a promising method to achieve freeform interconnects on compliant substrates for applications such as soft robotics and wearable healthcare devices. However, previous strategies to sinter metallic nanoparticles while preserving the soft polymer substrate are rife with problems such as cracking and low conductivity of the metallic features. In this paper, the mechanisms of cracking in nanoparticle‐based 3D printed and sintered stretchable interconnects are identified and architecture and processing strategies are demonstrated to achieve crack‐free interconnects fully embedded in thin (<100 μm in thickness) stretchable polydimethylsiloxane (PDMS) with external connectivity. Capillary forces between nanoparticles developed through rapid solvent evaporation in the colloidal ink is hypothesized to initiate cracking during drying. Additionally, the presence of oxygen promotes the removal of organic surfactants and binders in the nanoparticle ink which increases nanoparticle agglomeration, grain growth, and subsequently conductivity. An experimental step‐wise variation of the thermal/atmospheric process conditions supports this hypothesis and shows that the presence of air during a low temperature drying step reduces the capillary stress to produce crack‐free interconnects with high conductivities (up to 56% of bulk metal) while having an excellent compatibility with the underlying polymer materials. Finally, stretchable interconnects fully‐encapsulated in PDMS polymer, with 3D pillar architectures for external connectivity are demonstrated, thus also solving an important “last‐mile” problem in the packaging of stretchable electronics.

     
    more » « less
  5. ; ; ; ( , Extreme Mechanics Letters)
    Thermoplastic pipes are widely used in the semiconductor industry, where they are used to drain highly corrosive liquid waste. When exposed to oxidizing environments, thermoplastic pipes can undergo stress-corrosion cracking (SCC), potentially causing them to fail prematurely in the absence of appropriate design and maintenance guidelines. Here, the stress-corrosion cracking behavior of polypropylene, commonly used in waste drainage pipes for dilute sulfuric acid/hydrogen peroxide mixtures (Piranha solutions), is investigated as a function of applied energy release rate. Sub-critical crack growth experiments are performed with compact tension specimens in sulfuric acid/hydrogen peroxide mixtures using a custom constant-force loading system to evaluate the effects of temperature and chemical composition on SCC crack growth. The activation energy for the SCC process is 99.7 ± 15.3 kJ/mol, and the crack growth rate depends sensitively on the concentrations of sulfuric acid and hydrogen peroxide in the mixture. We propose a practical guideline to calculate the service life of polypropylene pipes in Piranha solutions using crack velocity curves and show that accidental exposure to a concentrated Piranha solution can significantly reduce service life. 
    more » « less
  • Citation Formats
  • MLA
  • APA
  • Chicago
  • BibTeX
  • Save / Share this Record
  • Send to Email