Title: Interfacial Properties of Hybrid Cellulose Nanocrystal/Carbonaceous Nanomaterial Composites
Cellulose nanocrystal (CNCs) assisted carbon nanotubes (CNTs) and graphene nanoplatelets (GnP) were used to modify the interfacial region of carbon fiber (CF) and polymer matrix to strengthen the properties of carbon fiber-reinforced polymer (CFRP). Before transferring CNC-CNTs and CNC-GnPs on the CF surface by an immersion coating method, the nanomaterials were dispersed in DI water homogeneously by using probe sonication technique without additives. The results showed that the addition of CNC-CNT and CNC-GnP adjusted the interfacial chemistry of CFRP with the formation of polar groups. Furthermore, according to the single fiber fragmentation test (SFFT), the interfacial shear strength (IFSS) of CNC-GnP 6:1 and CNC-CNT 10:1 added CFRP increased to 55 MPa and 64 MPa due to modified interfacial chemistry by the incorporation of the nanomaterials. This processing technique also resulted in improvement in interlaminar shear strength (ILSS) in CFRPs from 35 MPa (neat composite) to 45 (CNC-GnP 6:1) MPa and 52 MPa (CNC-CNT 10:1).  more » « less
Award ID(s):
1930277
PAR ID:
10378814
Author(s) / Creator(s):
Date Published:
Journal Name:
Proceedings of the American Society for Composites—Thirty-Sixth Technical Conference on Composite Materials
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. Depositing carbon nanotubes (CNTs) into carbon fiber reinforced polymer composites (CFRPs) is challenging because of the need for complicated lab-scale processes and toxic chemical dispersants that makes conventional means of processing less compatible with existing industrial procedures for large-scale applications. In this work, a scalable supercritical CO2-assisted atomization technique is used to effectively deposit hybrid CNTs in CFRPs allowing them to boost their functionality and tailor the microstructure. Cellulose nanocrystals (CNCs) are utilized to create hybrid nanostructures with CNTs (CNC bonded CNT) that enables stabilization of CNTs in nontoxic media, i.e., water, and this promotes the scalability of the process. According to Zeta potential values, CNCs successfully stabilize CNTs in water suspension. Scanning electron microscopy (SEM) micrographs show hybrid CNC bonded CNTs are homogeneously dispersed on the carbon fiber surface. According to the in-situ bending test under the optical microscope, crack propagation is hindered by engineered hybrid CNT nanostructures in the modified CFRP whereas neat CFRP exhibits low crack growth resistance due to the uninterrupted crack propagation in the continuous epoxy matrix. Our results imply that this strategy probes the importance of new controlled manufacturing of hybrid nanostructures through evaporation‑induced self‑assembly of nanocolloidal droplets, and allows for tailoring of the desired properties of nanostructured composites.

     
    more » « less
  2. Carbon fiber reinforced polymer (CFRP) composites have been increasingly used to replace metal parts in many industries such as aerospace, marine, automotive, and sporting goods. The CFRP parts compared with their metallic counter parts have the advantages of lightweight, significantly higher tensile strength, stiffer, and corrosion resistant. On the other hand, compared with many metal parts, the CFRP parts have many well-known disadvantages including the lower toughness, lower through-thickness tensile and shear strengths, lower thermal conductivity, lower electrical conductivity, and lower operating temperature. These disadvantages have made the conversion from metal parts into CFRP parts challenging and costly to design, manufacture, and maintain. The use of nanoparticles in polymer has been studied in the recent two decades. Carbon nanotubes (CNTs) and carbon nanofibers (CNFs) have been dispersed in various thermoset and thermoplastic polymers and improved the mechanical, electrical, and thermal properties; however, the properties were not comparable to CFRP. Later, researchers tried to infuse CNTs or CNFs into either carbon fiber preforms [1] or glass fiber preforms [2] for improving the mechanical properties. But the results were marginal and with great uncertainty due to the challenges of nanoparticle dispersion, filtering, and alignment while being infused through the fiber preform. The glass fiber preform experiments ended with relatively more consistent improvement than the carbon fiber preform experiments since that the glass fiber preform has significantly larger pores than the carbon fiber preform' s. The small pore size presented a great challenge for infusing millions of unaligned long CNTs or CNFs through the carbon fiber preform without being filtered. To infuse long CNFs or CNTs through the carbon fiber preform and achieve reliable improvements, especially for 55% or higher carbon fiber volume fraction with increasingly tighter pores, an innovative plan for the processing and nano-reinforcing strategy is necessary. The z-threading strategy [3, 4, 5] has been reported to have consistent experimental successes in achieving the statistically meaningful improvement in multifunctional properties. The manufacturing steps of the CNF z-threaded CFRP (ZT-CFRP) are: (1) disperse the CNFs in a resin, (2) use a strong electrical field to align the CNFs in either the B-stage epoxy film or a CNF/resin impregnated sponge layer, whereas the CNFs are aligned in the through-thickness direction of the film or sponge layer. (3) place the resin film or sponge layer on a preheated dry carbon fiber fabric and press the resin film into the hot carbon fabric and allow the resin flow to carry the well-aligned CNFs to thread through the pores in the carbon fabric. (4) cool down the resin saturated and CNF z-threaded carbon fiber fabric to obtain the ZT-CFRP prepreg. (5) use the ZT-CFRP prepreg to make the ZT-CFRP laminate. Compared with the traditional CFRP, the ZT-CFRP laminates were reported of having improvement in the Mode-I delamination toughness, interlaminar shear strength, longitudinal compressive strength, through-thickness electrical conductivity, through-thickness thermal conductivity, and can reach the carbon fiber volume fraction of 55-80%. It is an effective approach to achieve a multifunctional CFRP for potentially expanding CFRP's applications. 
    more » « less
  3. Previous studies have provided evidence that reinforcement of epoxy adhesives with nanostructures such as carbon nanofibers (CNFs) produces higher strength bonded joints between carbon fiber reinforced polymer (CFRP) laminates and shifts bond-line failure modes from the adhesive into the laminate. Despite this, there has been no research dedicated to applying reinforced adhesives to the bonding of nano-reinforced CFRP such as CNF z-threaded carbon fiber reinforced polymer (ZT-CFRP) laminates, which have been proven to exhibit increased interlaminar shear strength, mode-I delamination toughness, and compressive strength over traditional CFRP. This study examined the effectiveness of using CNF reinforced epoxy adhesives for unidirectional ZT-CFRP laminate bonding through single-lap shear tests using the ASTM D5868-01 standard. Unidirectional CFRP laminate samples bonded with both epoxy adhesive and CNF reinforced epoxy adhesive were also tested for comparison. It was found that the average shear strength observed for ZT-CFRP samples bonded with CNF reinforced epoxy adhesive was approximately 44% and 26 % higher than that of CFRP samples bonded with epoxy adhesive and CNF reinforced epoxy adhesive, respectively. Microscopic image analysis was performed to examine the mode of bond failure. The roles of nanomaterials in the fracture mechanism of the adhesives and the composite laminates are also discussed. 
    more » « less
  4. Carbon fiber-based structural lithium-ion batteries are attracting significant attention in the automotive and aerospace industries due to their dual capability of energy storage and mechanical load-bearing, leading to weight reduction. These batteries utilize lightweight carbon fiber (CF) composites, which offer excellent stiffness, strength-to-weight ratios, and electrical conductivity. Polyacrylonitrile-based CFs, comprising graphitic and amorphous carbon, are particularly suitable for Li-ion battery applications as they allow the storage of lithium ions. However, integrating lithium iron phosphate (LFP) into CFs poses challenges due to complex lab-scale processes and the use of toxic dispersants, hindering large-scale industrial compatibility. To address this, we investigate the development of water-based LFP-integrated CF structural Li-ion batteries. Homogeneous suspensions are created using cellulose nanocrystals (CNCs) to form hybrid structures. The battery system employs LFP-modified CF as the cathode, unsized CF as the anode, and a water-based electrolyte. The LFP-CNC-graphene nanoplatelet (GNP) hybrids are coated onto CFs through immersion coating. Scanning electron microscopy (SEM) images confirm the well-dispersed and well-adhered LFP-CNC-GNP structures on the CF surface, contributing to their mechanical interlocking and electrochemical performance. The batteries demonstrate a specific energy density of 62.67 Wh/kg and a specific capacity of 72.7 mAh/g. Furthermore, the cyclic voltammetry experiments reveal the stability of the LFP-CNC-GNP-coated CF batteries over 200 cycles without degradation. This research enables the engineering of hybrid nanostructured battery laminates using novel LFP-CNC-GNP-coated CFs, opening avenues for the development of innovative Li-ion structural batteries. 
    more » « less
  5. Abstract

    Highly conductive and mechanically strong microfibers are attractive in energy storage, thermal management, and wearable electronics. Here, a highly conductive and strong carbon nanotube/nanofibrillated cellulose (CNT–NFC) composite microfiber is developed via a fast and scalable 3D‐printing method. CNTs are successfully dispersed in an aqueous solution using 2,2,6,6‐tetramethylpiperidinyl‐1‐oxyl (TEMPO) oxidated NFCs, resulting in a mixture solution with an obvious shear‐thinning property. Both NFC and CNT fibers inside the all‐fiber‐based microfibers are well aligned, which helps to improve the interaction and percolation between these two building blocks, leading to a combination of high mechanical strength (247 ± 5 MPa) and electrical conductivity (216.7 ± 10 S cm−1). Molecular modeling is applied to offer further insights into the role of CNT–NFC fiber alignment for the excellent mechanical strength. The combination of high electrical conductivity, mechanical strength, and the fast yet scalable 3D‐printing technology positions the CNT–NFC composite microfiber as a promising candidate for wearable electronic devices.

     
    more » « less