A new record‐high room‐temperature electron Hall mobility (
Due to the coexistence of many emergent phenomena, including 2D superconductivity and a large Rashba spin‐orbit coupling, 5d transition metal oxides‐based two‐dimensional electron systems (2DESs) have been prospected as one of the potential intrants for modern electronics. However, despite the lighter electron mass, the mobility of carriers, a key requisite for high‐performance devices, in 5d‐oxides devices remains far behind their 3d‐oxides analogs. The carriers’ mobility in these oxides is significantly hampered by the inevitable presence of defects. Here, very high mobility (≈22 650 cm2V−1s−1) of 5d‐2DES confined at the LaAlO3/KTaO3interface is reported. The high mobility, which is beyond the values observed in SrTiO32DESs in the same carrier‐density range, is achieved using the ionic‐liquid gating at room temperature. The authors postulate that the ionic‐liquid gating affects the oxygen vacancies and efficiently reduces any disorder at the interface. Investigating density and mobility in a broad range of back‐gate voltage, the authors reveal that the mobility follows the power‐law
- NSF-PAR ID:
- 10385161
- Publisher / Repository:
- Wiley Blackwell (John Wiley & Sons)
- Date Published:
- Journal Name:
- Advanced Materials Interfaces
- Volume:
- 9
- Issue:
- 35
- ISSN:
- 2196-7350
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
more » « less
μ RT = 194 cm2 V−1 s−1atn ≈ 8 × 1015 cm−3) for β‐Ga2O3is demonstrated in the unintentionally doped thin film grown on (010) semi‐insulating substrate via metal‐organic chemical vapor deposition (MOCVD). A peak electron mobility of ≈9500 cm2 V−1 s−1is achieved at 45 K. Further investigation on the transport properties indicates the existence of sheet charges near the epilayer/substrate interface. Si is identified as the primary contributor to the background carrier in both the epilayer and the interface, originating from both surface contamination and growth environment. The pregrowth hydrofluoric acid cleaning of the substrate leads to an obvious decrease in Si impurity both at the interface and in the epilayer. In addition, the effect of the MOCVD growth condition, particularly the chamber pressure, on the Si impurity incorporation is studied. A positive correlation between the background charge concentration and the MOCVD growth pressure is confirmed. It is noteworthy that in a β‐Ga2O3film with very low bulk charge concentration, even a reduced sheet charge density plays an important role in the charge transport properties. -
more » « less
Abstract The performance of all‐solid‐state batteries (ASSBs) relies on the Li+transport and stability characteristics of solid electrolytes (SEs). Li3PS4is notable for its stability against lithium metal, yet its ionic conductivity remains a limiting factor. This study leverages local structural disorder via O substitution to achieve an ionic conductivity of 1.38 mS cm−1with an activation energy of 0.34 eV for Li3PS4−
x Ox (x = 0.31). Optimal O substitution transforms Li+transport from 2D to 3D pathways with increased ion mobility. Li3PS3.69O0.31exhibits improvements in the critical current density and stability against Li metal and retains its electrochemical stability window compared with Li3PS4. The practical implementation of Li3PS3.69O0.31in ASSBs half‐cells, particularly when coupled with TiS2as the cathode active material, demonstrates substantially enhanced capacity and rate performance. This work elucidates the utility of introducing local structural disorder to ameliorate SE properties and highlights the benefits of strategically combining the inherent strengths of sulfides and oxides via creating oxysulfide SEs. -
more » « less
Abstract Ultrafast time‐domain thermoreflectance (TDTR) is utilized to extract the through‐plane thermal conductivity (
Λ LSCO) of epitaxial La0.5Sr0.5CoO3−δ (LSCO) of varying thickness (<20 nm) on LaAlO3and SrTiO3substrates. These LSCO films possess ordered oxygen vacancies as the primary means of lattice mismatch accommodation with the substrate, which induces compressive/tensile strain and thus controls the orientation of the oxygen vacancy ordering (OVO). TDTR results demonstrate that the room‐temperatureΛ LSCOof LSCO on both substrates (1.7 W m−1K−1) are nearly a factor of four lower than that of bulk single‐crystal LSCO (6.2 W m−1K−1). Remarkably, this approaches the lower limit of amorphous oxides (e.g., 1.3 W m−1K−1for glass), with no dependence on the OVO orientation. Through theoretical simulations, origins of the glass‐like thermal conductivity of LSCO are revealed as a combined effect resulting from oxygen vacancies (the dominant factor), Sr substitution, size effects, and the weak electron/phonon coupling within the LSCO film. The absence of OVO dependence in the measuredΛ LSCOis rationalized by two main effects: (1) the nearly isotropic phononic thermal conductivity resulting from the imperfect OVO planes when δ is small; (2) the missing electronic contribution toΛ LSCOalong the through‐plane direction for these ultrathin LSCO films on insulating substrates. -
more » « less
Abstract Lattice defects typically reduce lattice thermal conductivity, which has been widely exploited in applications such as thermoelectric energy conversion. Here, an anomalous dependence of the lattice thermal conductivity on point defects is demonstrated in epitaxial WO3thin films. Depending on the substrate, the lattice of epitaxial WO3expands or contracts as protons are intercalated by electrolyte gating or oxygen vacancies are introduced by adjusting growth conditions. Surprisingly, the observed lattice volume, instead of the defect concentration, plays the dominant role in determining the thermal conductivity. In particular, the thermal conductivity increases significantly with proton intercalation, which is contrary to the expectation that point defects typically lower the lattice thermal conductivity. The thermal conductivity can be dynamically varied by a factor of
≈ 1.7 via electrolyte gating, and tuned over a larger range, from 7.8 to 1.1 W m−1K−1, by adjusting the oxygen pressure during film growth. The electrolyte‐gating‐induced changes in thermal conductivity and lattice dimensions are reversible through multiple cycles. These findings not only expand the basic understanding of thermal transport in complex oxides, but also provide a path to dynamically control the thermal conductivity. -
more » « less
Abstract High quality dielectric‐semiconductor interfaces are critical for reliable high‐performance transistors. This paper reports the in situ metal–organic chemical vapor deposition of Al2O3on β‐Ga2O3as a potentially better alternative to the most commonly used atomic layer deposition (ALD). The growth of Al2O3is performed in the same reactor as Ga2O3using trimethylaluminum and O2as precursors without breaking the vacuum at a growth temperature of 600 °C. The fast and slow near interface traps at the Al2O3/β‐Ga2O3interface are identified and quantified using stressed capacitance–voltage (CV) measurements on metal oxide semiconductor capacitor (MOSCAP) structures. The density of shallow and deep level initially filled traps (Dit) are measured using ultraviolet‐assisted CV technique. The average Ditfor the MOSCAP is determined to be 6.4
× 1011cm−2eV−1. The conduction band offset of the Al2O3/ Ga2O3interface is also determined from CV measurements and found out to be 1.7 eV which is in close agreement with the existing literature reports of ALD Al2O3/Ga2O3interface. The current–voltage characteristics are also analyzed and the average breakdown field is extracted to be approximately 5.8 MV cm−1. This in situ Al2O3dielectric on β‐Ga2O3with improved dielectric properties can enable Ga2O3‐based high‐performance devices.