Title: Type-II band alignment for atomic layer deposited HfSiO4 on α-Ga2O3

There is increasing interest in α-polytype Ga2O3 for power device applications, but there are few published reports on dielectrics for this material. Finding a dielectric with large band offsets for both valence and conduction bands is especially challenging given its large bandgap of 5.1 eV. One option is HfSiO4 deposited by atomic layer deposition (ALD), which provides conformal, low damage deposition and has a bandgap of 7 eV. The valence band offset of the HfSiO4/Ga2O3 heterointerface was measured using x-ray photoelectron spectroscopy. The single-crystal α-Ga2O3 was grown by halide vapor phase epitaxy on sapphire substrates. The valence band offset was 0.82 ± 0.20 eV (staggered gap, type-II alignment) for ALD HfSiO4 on α-Ga0.2O3. The corresponding conduction band offset was −2.72 ± 0.45 eV, providing no barrier to electrons moving into Ga2O3.

 
more » « less
Award ID(s):
1856662
NSF-PAR ID:
10440269
Author(s) / Creator(s):
; ; ; ; ; ; ; ; ;
Publisher / Repository:
American Vacuum Society
Date Published:
Journal Name:
Journal of Vacuum Science & Technology A
Volume:
41
Issue:
2
ISSN:
0734-2101
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. There is increasing interest in the alpha polytype of Ga2O3 because of its even larger bandgap than the more studied beta polytype, but in common with the latter, there is no viable p-type doping technology. One option is to use p-type oxides to realize heterojunctions and NiO is one of the candidate oxides. The band alignment of sputtered NiO on α-Ga2O3 remains type II, staggered gap for annealing temperatures up to 600 °C, showing that this is a viable approach for hole injection in power electronic devices based on the alpha polytype of Ga2O3. The magnitude of both the conduction and valence band offsets increases with temperature up to 500 °C, but then is stable to 600 °C. For the as-deposited NiO/α-Ga2O3 heterojunction, ΔEV = −2.8 and ΔEC = 1.6 eV, while after 600 °C annealing the corresponding values are ΔEV = −4.4 and ΔEC = 3.02 eV. These values are 1−2 eV larger than for the NiO/β-Ga2O3 heterojunction.

     
    more » « less
  2. Germanium alloyed with α-tin (GeSn) transitions to a direct bandgap semiconductor of significance for optoelectronics. It is essential to localize the carriers within the active region for improving the quantum efficiency in a GeSn based laser. In this work, epitaxial GeSn heterostructure material systems were analyzed to determine the band offsets for carrier confinement: (i) a 0.53% compressively strained Ge 0.97 Sn 0.03 /AlAs; (ii) a 0.81% compressively strained Ge 0.94 Sn 0.06 /Ge; and (iii) a lattice matched Ge 0.94 Sn 0.06 /In 0.12 Al 0.88 As. The phonon modes in GeSn alloys were studied using Raman spectroscopy as a function of Sn composition, that showed Sn induced red shifts in wavenumbers of the Ge–Ge longitudinal optical phonon mode peaks. The material parameter b representing strain contribution to Raman shifts of a Ge 0.94 Sn 0.06 alloy was determined as b = 314.81 ± 14 cm −1 . Low temperature photoluminescence measurements were performed at 79 K to determine direct and indirect energy bandgaps of E g,Γ = 0.72 eV and E g,L = 0.66 eV for 0.81% compressively strained Ge 0.94 Sn 0.06 , and E g,Γ = 0.73 eV and E g,L = 0.68 eV for lattice matched Ge 0.94 Sn 0.06 epilayers. Chemical effects of Sn atomic species were analyzed using X-ray photoelectron spectroscopy (XPS), revealing a shift in Ge 3d core level (CL) spectra towards the lower binding energy affecting the bonding environment. Large valence band offset of Δ E V = 0.91 ± 0.1 eV and conduction band offset of Δ E C,Γ–X = 0.64 ± 0.1 eV were determined from the Ge 0.94 Sn 0.06 /In 0.12 Al 0.88 As heterostructure using CL spectra by XPS measurements. The evaluated band offset was found to be of type-I configuration, needed for carrier confinement in a laser. In addition, these band offset values were compared with the first-principles-based calculated Ge/InAlAs band alignment, and it was found to have arsenic up-diffusion limited to 1 monolayer of epitaxial GeSn overlayer, ruling out the possibility of defects induced modification of band alignment. Furthermore, this lattice matched GeSn/InAlAs heterostructure band offset values were significantly higher than GeSn grown on group IV buffer/substrates. Therefore, a lattice matched GeSn/InAlAs material system has large band offsets offering superior carrier confinement to realize a highly efficient GeSn based photonic device. 
    more » « less
  3. X Ray Photoelectron Spectroscopy was used to measure valence band offsets for Al 2 O 3 deposited by Atomic Layer Deposition on α -(Al x Ga 1-x ) 2 O 3 alloys over a wide range of Al contents, x, from 0.26–0.74, corresponding to a bandgap range from 5.8–7 eV. These alloys were grown by Pulsed Laser Deposition. The band alignments were type I (nested) at x <0.5, with valence band offsets 0.13 eV for x = 0.26 and x = 0.46. At higher Al contents, the band alignment was a staggered alignment, with valence band offsets of − 0.07 eV for x = 0.58 and −0.17 for x = 0.74, ie. negative valence band offsets in both cases. The conduction band offsets are also small at these high Al contents, being only 0.07 eV at x = 0.74. The wide bandgap of the α -(Al x Ga 1-x ) 2 O 3 alloys makes it difficult to find dielectrics with nested band alignments over the entire composition range. 
    more » « less
  4. Valence band offsets for SiO 2 deposited by Atomic Layer Deposition on α -(Al x Ga 1-x ) 2 O 3 alloys with x = 0.26–0.74 were measured by X-ray Photoelectron Spectroscopy. The samples were grown with a continuous composition spread to enable investigations of the band alignment as a function of the alloy composition. From measurement of the core levels in the alloys, the bandgaps were determined to range from 5.8 eV (x = 0.26) to 7 eV (x = 0.74). These are consistent with previous measurements by transmission spectroscopy. The valence band offsets of SiO 2 with these alloys of different composition were, respectively, were −1.2 eV for x = 0.26, −0.2 eV for x = 0.42, 0.2 eV for x = 0.58 and 0.4 eV for x = 0.74. All of these band offsets are too low for most device applications. Given the bandgap of the SiO 2 was 8.7 eV, this led to conduction band offsets of 4.1 eV (x = 0.26) to 1.3 eV (x = 0.74). The band alignments were of the desired nested configuration for x > 0.5, but at lower Al contents the conduction band offsets were negative, with a staggered band alignment. This shows the challenge of finding appropriate dielectrics for this ultra-wide bandgap semiconductor system. 
    more » « less
  5. The band alignments of two candidate dielectrics for ScAlN, namely, SiO2 and Al2O2, were obtained by x-ray photoelectron spectroscopy. We compared the effect of deposition method on the valence band offsets of both sputtered and atomic layer deposition films of SiO2 and Al2O3 on Sc0.27Al0.73 N (bandgap 5.1 eV) films. The band alignments are type I (straddled gap) for SiO2 and type II (staggered gap) for Al2O3. The deposition methods make a large difference in relative valence band offsets, in the range 0.4–0.5 eV for both SiO2 and Al2O3. The absolute valence band offsets were 2.1 or 2.6 eV for SiO2 and 1.5 or 1.9 eV for Al2O3 on ScAlN. Conduction band offsets derived from these valence band offsets, and the measured bandgaps were then in the range 1.0–1.1 eV for SiO2 and 0.30–0.70 eV for Al2O3. These latter differences can be partially ascribed to changes in bandgap for the case of SiO2 deposited by the two different methods, but not for Al2O3, where the bandgap as independent of deposition method. Since both dielectrics can be selectively removed from ScAlN, they are promising as gate dielectrics for transistor structures.

     
    more » « less