skip to main content
US FlagAn official website of the United States government
dot gov icon
Official websites use .gov
A .gov website belongs to an official government organization in the United States.
https lock icon
Secure .gov websites use HTTPS
A lock ( lock ) or https:// means you've safely connected to the .gov website. Share sensitive information only on official, secure websites.

Explore Research Products in the PAR
It may take a few hours for recently added research products to appear in PAR search results.


Title: Quantifying Microstructure Features for High-Performance Solid Oxide Cells
Focused ion beam (FIB) – scanning electron microscopy (SEM) allowed the characterization of the microstructure of two solid oxide fuel cells prepared at different sintering temperatures. 3D volume reconstruction showed that a relatively low sintering temperature significantly and positively affected distribution, volume and particle size of yttria-stabilized zirconia, nickel, and pore phases inside the anode, as well as the extent of the important triple-phase boundary interface. The poor performance of the T1 sample sintered at a higher temperature is explained by the poorly connected pore network and very low-density triple-phase boundary. The pore space inside the T1 anode was unable to ensure continuous hydrogen flow from the inlet to the outlet and thus exhibited very low gas permeability. In contrast, the T2 sample sintered at a lower temperature had approximately equal amounts of YSZ and nickel and larger pores, which allowed formation of significantly more TPB electrochemical reaction sites. The higher power density of the T2 cell was also the result of its robust pore network capable of transporting hydrogen throughout the anode. The methodology used in this paper eliminates the need for employing hypothetical structures and provides accurate estimates of the investigated parameters by evaluating microstructures that were successfully reconstructed using high-resolution microscopy techniques.  more » « less
Award ID(s):
1920166
PAR ID:
10409426
Author(s) / Creator(s):
Date Published:
Journal Name:
arXivorg
ISSN:
2331-8422
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. ; ; ; ; (, The International Journal of Advanced Manufacturing Technology)
    null (Ed.)
    Binder jet 3D printing combined with post-deposition sintering is a non-beam additive manufacturing (AM) method for the creation of complex metallic structures. Binder saturation and particle morphology are two important factors affecting the quality of printed parts. Here, we investigated the effects of binder saturation on dimension accuracy, porosity, microstructure and microhardness of nickel-based alloy 625 samples made of differently atomized powders. Argon gas atomized (GA) and water atomized (WA) nickel-based alloy 625 powders were used to binder jet samples for a detailed comparative study. The optimal binder saturation for WA system is 60% to 70%, whereas for GA system the optimal is about 80%. Generally, GA samples achieved better overall quality than WA samples in terms of packing density, dimensional accuracy, sintered density, and microhardness. This difference is attributed mainly to the particle morphology including sphericity and roundness. The critical threshold for visible binder bleeding phenomenon in WA and GA systems is determined to be 120% and 140% binder saturation, respectively. Mechanisms for binder bleeding phenomenon at different saturation levels for WA and GA systems are discussed in detail. A pore evolution model is proposed to better understand the printing and sintering processes. 
    more » « less
  2. ; ; ; (, Journal of the American Ceramic Society)
    Abstract Ceramics such as lead zirconate titanate (PZT) tend to dissolve incongruently, and thus pose a challenge in the cold sintering process. Moist lead nitrate has previously been shown to enable a cold sinter‐assisted densification of PZT by a viscous phase sintering mechanism. In this paper, lead acetate trihydrate is demonstrated to lower the required temperature of the cold sintering step to 200°C. This densification process was described as a two‐step process: cold sintering of PZT with lead acetate trihydrate and post‐annealing the as‐cold sintered PZT ceramics. Unlike in the case of lead nitrate, PZT densification with lead acetate trihydrate occurs by a liquid phase assisted sintering mechanism, leading to an as‐cold sintered relative density of 84% at 200°C. After performing a post‐anneal step at 900°C, >97% relative densities were achieved in samples that were cold sintered with lead acetate trihydrate. This step not only densified PZT but also refined the grain boundaries. In the post‐annealed samples, the room‐temperature relative permittivity at 100 Hz was ~1600, slightly higher than that reported in samples that used lead nitrate as a sintering aid; the loss tangent was about 3.8%. For measurements at 10 Hz, the remanent polarization in both cases was ~28 µC/cm2. Both Rayleigh analysis and aging studies showed that a higher irreversible contribution to the permittivity exists in samples that used lead nitrate as a cold sintering aid. 
    more » « less
  3. ; ; ; (, International Journal of Applied Ceramic Technology)
    Abstract This study binder jets a tungsten carbide‐nickel (WC‐Ni) sintered‐agglomerated composite powder, and postprocesses the preforms using an initial sintering step followed by a hot isostatic pressing (HIP) step. The effects of sintering temperatures, sintering durations, and HIP temperatures on notable properties (e.g., porosity, microstructure, hardness, and oxidation behavior) are quantified. The highest average relative density produced in this study was 96.8%, and volumetric shrinkage of these coupons was about 64%. Microstructural characterization shows that the WC grains are homogenously distributed throughout the nickel matrix and grow to an average diameter of 1.6  (a 60% increase) during processing. X‐ray diffraction patterns indicate that no unwanted products were formed. Processed coupons achieved a maximum hardness of 54 Rockwell C, limited by their internal porosity. Oxidation tests result in the production of WO3and NiWO4at temperatures above 600°C. Methodologies and results from this study can be leveraged to additively manufacture highly dense, geometrically complex WC‐Ni parts with small carbide grains, low nickel content, desirable microstructure, and suitable functional properties. 
    more » « less
  4. ; ; ; ; ; ; (, Advanced Engineering Materials)
    Cold sintering of surface‐modified iron compacts results in a co‐continuous phosphate interphase between iron particles that provide both enhanced green strength and green density similar to the process that has been successfully introduced in low‐temperature densification of ceramic materials. Relative density as high as 95% along with transverse rupture strength of ≈ 75 MPa, which is almost six times that of conventional powdered metal iron compact and 2.5 times that of warm compacted controls, is achieved. Dilatometry study at different pressures shows a small but significant improvement in densification process during cold sintering relative to the larger densification of warm compacted control. Strength model based on microstructural analysis as well as in situ diffused reflectance infrared Fourier transform spectroscopy (DRIFTS) experiments reveals the nature of the interphase that imparts the large cohesive strength under the cold sintered assisted warm compaction. The process is conducive to produce iron compacts for green machining. Furthermore, the samples when subjected to high‐temperature sintering yield a fully sintered iron compact with density > 7.2 g cm−3and transverse rupture strength as high as 780 MPa. All in all, there are major new opportunities with the cold sintered assisted warm compaction of powdered metals that will also be discussed. 
    more » « less
  5. ; ; (, Metallography, Microstructure, and Analysis)
    Deacon, Ryan M (Ed.)
    Abstract Tungsten heavy alloys are used in demanding high pressure die casting applications due to their high temperature strength, high thermal conductivity, and low thermal expansion. High cost limits applications to small sintered die inserts and manual gas tungsten arc weld repairs. A new tungsten heavy alloy consumable, Anviloy wire, was developed for automated cladding of hot work tool steel dies. Literature regarding characterization of tungsten heavy alloy die steel clads was lacking. Understanding base metal dilution effect on clad microstructure is critical but required new sample preparation methods. An Anviloy wire-H13 clad was made using hot wire gas tungsten arc cladding and analyzed with metallography. Samples were found to have grain boundary M6C carbide phase as-welded with the help of an alkaline sodium picrate etchant. An isothermally aged arc crucible melted sample of the same composition was characterized using metallography, scanning electron microscopy, and transmission electron diffraction. The clad representative arc crucible melted sample was subjected to isothermal aging at 725°C for 100 hours. Isothermal aging resulted in precipitation of a high volume fraction of intermetallic platelets. Using a new carbon extraction replica sample preparation method involving two chemical polishing steps, transmission electron diffraction of precipitates indicated they were mu phase intermetallic. 
    more » « less
  • Citation Formats
  • MLA
  • APA
  • Chicago
  • BibTeX
  • Save / Share this Record
  • Send to Email