The growth of monoclinic phase‐pure gallium oxide (β‐Ga2O3) layers by metal–organic chemical vapor deposition on c‐plane sapphire and aluminum nitride (AlN) templates using silicon‐oxygen bonding (SiOx) as a phase stabilizer is reported. The β‐Ga2O3layers are grown using triethylgallium, oxygen, and silane for gallium, oxygen, and silicon precursors, respectively, at 700 °C, with and without silane flow in the process. The samples grown on sapphire with SiOxphase stabilization show a notable change from samples without phase stabilization in the roughness and resistivity, from 16.2 to 4.2 nm and from 85.82 to 135.64 Ω cm, respectively. X‐ray diffraction reveals a pure‐monoclinic phase, and Raman spatial mapping exhibits higher tensile strain in the films in the presence of SiOx. The β‐Ga2O3layers grown on an AlN template, using the same processes as for sapphire, show an excellent epitaxial relationship between β‐Ga2O3and AlN and have a significant change in β‐Ga2O3surface morphology.
more »
« less
Demonstration of thick phase-pure β-Ga2O3 on a c-plane sapphire substrate using MOCVD
We demonstrated a metal-organic chemical vapor deposition (MOCVD) of smooth, thick, and monoclinic phase-pure gallium oxide (Ga2O3) on c-plane sapphire using silicon-oxygen bonding (SiOx) as a phase stabilizer. The corundum (α), monoclinic (β), and orthorhombic (ε) phases of Ga2O3 with a bandgap in the 4.4 – 5.1 eV range, are promising materials for power semiconductor devices and deep ultraviolet (UV) solar-blind photodetectors. The MOCVD systems are extensively used for homoepitaxial growth of β-Ga2O3 on (001), (100), (010), and (¯2 01) β-Ga2O3 substrates. These substrates are rare/expensive and have very low thermal conductivity; thus, are not suitable for high-power semiconductor devices. The c-plane sapphire is typically used as a substrate for high-power devices. The β-Ga2O3 grows in the (¯2 01) direction on sapphire. In this direction, the presence of high-density oxygen dangling bonds, frequent stacking faults, twinning, and other phases and planes impede the heteroepitaxy of thick β-Ga2O3. Previously phase stabilizations with SiOx have been reported for tetragonal and monoclinic hafnia. We were able to grow ~580nm thick β-Ga2O3 on sapphire by MOCVD at 750 oC through phase stabilization using silane. The samples grown with silane have a reduction in the surface roughness and resistivity from 10.7 nm to 4.4 nm and from 371.75 Ω.cm to 135.64 Ω.cm, respectively. These samples show a pure-monoclinic phase determined by x-ray diffraction (XRD); have tensile strain determined by Raman strain mapping. These results show that a thick, phase-pure -Ga2O3 can be grown on c-plane sapphire which can be suitable for creating power devices with better thermal management.
more »
« less
- PAR ID:
- 10431786
- Editor(s):
- Teherani, Ferechteh H.; Rogers, David J.
- Date Published:
- Journal Name:
- Proc. SPIE 12422, Oxide-based Materials and Devices
- Volume:
- XIV
- Page Range / eLocation ID:
- 15
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Si-doped β-phase (010) Ga2O3 epi-films with fast growth rates were comprehensively investigated using trimethylgallium (TMGa) as the Ga precursor via metalorganic chemical vapor deposition (MOCVD). Two main challenges facing the MOCVD growth of thick (010) β-Ga2O3 films with fast growth rates include high impurity carbon (C) incorporation and rough surface morphologies due to the formation of imbedded 3D pyramid-shaped structures. In this work, two different categories of oxygen source (high-purity O2 > 99.9999% and O2* with 10 ppm of [H2O]) were used for β-Ga2O3 MOCVD growth. Our study revealed that the size and density of the 3D defects in the β-Ga2O3 epi-films were significantly reduced when the O2* was used. In addition, the use of off-axis (010) Ga2O3 substrates with 2° off-cut angle leads to further reduction of defect formation in β-Ga2O3 with fast growth rates. To suppress C incorporation in MOCVD β-Ga2O3 grown with high TMGa flow rates, our findings indicate that high O2 (or O2*) flow rates are essential. Superior room temperature electron mobilities as high as 110–190 cm2/V·s were achieved for β-Ga2O3 grown using O2* (2000 sccm) with a growth rate of 4.5 μm/h (film thickness of 6.3 μm) within the doping range of 1.3 × 1018–7 × 1015 cm−3. The C incorporation is significantly suppressed from ∼1018 cm−3 to <5 × 1016 cm−3 ([C] detection limit) for β-Ga2O3 grown using high O2 (O2*) flow rate of 2000 sccm. Results from this work will provide guidance on developing high-quality, thick β-Ga2O3 films required for high power electronic devices with vertical configurations.more » « less
-
Halide vapor phase epitaxial (HVPE) Ga2O3 films were grown on c-plane sapphire and diamond substrates at temperatures up to 550 °C without the use of a barrier dielectric layer to protect the diamond surface. Corundum phase α-Ga2O3 was grown on the sapphire substrates, whereas the growth on diamond resulted in regions of nanocrystalline β-Ga2O3 (nc-β-Ga2O3) when oxygen was present in the HVPE reactor only during film growth. X-ray diffraction confirmed the growth of α-Ga2O3 on sapphire but failed to detect any β-Ga2O3 reflections from the films grown on diamond. These films were further characterized via Raman spectroscopy, which revealed the β-Ga2O3 phase of these films. Transmission electron microscopy demonstrated the nanocrystalline character of these films. From cathodoluminescence spectra, three emission bands, UVL′, UVL, and BL, were observed for both the α-Ga2O3/sapphire and nc-Ga2O3/diamond, and these bands were centered at approximately 3.7, 3.2, and 2.7 eV.more » « less
-
The hot-wall metalorganic chemical vapor deposition (MOCVD) concept, previously shown to enable superior material quality and high performance devices based on wide bandgap semiconductors, such as Ga(Al)N and SiC, has been applied to the epitaxial growth of β-Ga 2 O 3 . Epitaxial β-Ga 2 O 3 layers at high growth rates (above 1 μm/h), at low reagent flows, and at reduced growth temperatures (740 °C) are demonstrated. A high crystalline quality epitaxial material on a c-plane sapphire substrate is attained as corroborated by a combination of x-ray diffraction, high-resolution scanning transmission electron microscopy, and spectroscopic ellipsometry measurements. The hot-wall MOCVD process is transferred to homoepitaxy, and single-crystalline homoepitaxial β-Ga 2 O 3 layers are demonstrated with a [Formula: see text]01 rocking curve width of 118 arc sec, which is comparable to those of the edge-defined film-fed grown ([Formula: see text]01) β-Ga 2 O 3 substrates, indicative of similar dislocation densities for epilayers and substrates. Hence, hot-wall MOCVD is proposed as a prospective growth method to be further explored for the fabrication of β-Ga 2 O 3 .more » « less
-
Growing a thick high-quality epitaxial layer on the β-Ga2O3 substrate is crucial in commercializing β-Ga2O3 devices. Metal organic chemical vapor deposition (MOCVD) is also well-established for the large-scale commercial growth of β-Ga2O3 and related heterostructures. This paper presents a systematic study of the Schottky barrier diodes fabricated on two different Si-doped homoepitaxial β-Ga2O3 thin films grown on Sn-doped (001) and (010) β-Ga2O3 substrates by MOCVD. X-ray diffraction analysis of the MOCVD-grown sample, room temperature current density–voltage data for different Schottky diodes, and C–V measurements are presented. Diode characteristics, such as ideality factor, barrier height, specific on-resistance, and breakdown voltage, are studied. Temperature dependence (170–360 K) of the ideality factor, barrier height, and Poole–Frenkel reverse leakage mechanism are also analyzed from the J–V–T characteristics of the fabricated Schottky diodes.more » « less