Explore Research Products in the PAR
It may take a few hours for recently added research products to appear in PAR search results.


Title: Thermal and Mechanical Properties of Recyclable Composites Prepared from Bio-Olefins and Industrial Waste
Ordinary Portland Cement (OPC) production consumes tremendous amounts of fresh water and energy and releases vast quantities of CO2 into the atmosphere. Not only would an alternative to OPC whose production requires no water, releases little CO2, and consumes less energy represent a transformative advance in the pursuit of industrial decarbonization, but the greater availability of safe drinking water would lead to significantly improved public health, particularly among vulnerable populations most at risk from contaminated water supply. For any OPC alternative to be adopted on any meaningful scale, however, its structural capabilities must meet or exceed those of OPC. An inverse vulcanization of brown grease, sunflower oil, and elemental sulfur (5:5:90 weight ratio) was successfully modified to afford the high-sulfur-content material SunBG90 in quantities > 1 kg, as was necessary for standardized ASTM and ISO testing. Water absorption (ASTM C140) and thermal conductivity (ISO 8302) values for SunBG90 (<1 wt% and 0.126 W·m−1·K−1, respectively) were 84% and 94% lower than those for OPC, respectively, suggesting that SunBG90 would be more resistant against freeze-thaw and thermal stress damage than OPC. Consequently, not only does SunBG90 represent a more environmentally friendly material than OPC, but its superior thermomechanical properties suggest that it could be a more environmentally robust material on its own merits, particularly for outdoor structural applications involving significant exposure to water and seasonal or day/night temperature swings.  more » « less
Award ID(s):
2203669
PAR ID:
10434788
Author(s) / Creator(s):
; ; ; ; ;
Date Published:
Journal Name:
Journal of Composites Science
Volume:
7
Issue:
6
ISSN:
2504-477X
Page Range / eLocation ID:
248
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. ; ; ; ; (, Chemistry)
    High sulfur-content materials (HSMs) formed via inverse vulcanization of elemental sulfur with animal fats and/or plant oils can exhibit remarkable mechanical strength and chemical resistance, sometimes superior to commercial building products. Adding pozzolan fine materials—fly ash (FA), silica fume (SF), ground granulated blast furnace slag (GGBFS), or metakaolin (MK)—can further improve HSM mechanical properties and stability. Herein, we detail nine materials comprised of rancidified chicken fat, elemental sulfur, and canola or sunflower oil (to yield CFS or GFS, respectively) and, with or without FA, SF, GGBFS, or MK. The base HSMs, CFS90 or GFS90, contained 90 wt% sulfur, 5 wt% chicken fat, and 5 wt% canola or sunflower oil, respectively. For each HSM/fine combination, the resulting material was prepared using a 95:5 mass input ratio of HSM/fine. No material exhibited water uptake >0.2 wt% after immersion in water for 24 h, significantly lower than the 28 wt% observed with ordinary Portland cement (OPC). Impressively, CFS90, GFS90, and all HSM/fine combinations exhibited compressive strength values 15% to 55% greater than OPC. After immersion in 0.5 M H2SO4, CFS90, GFS90, and its derivatives retained 90% to 171% of the initial strength of OPC, whereas OPC disintegrated under these conditions. CFS90, GFS90, and its derivatives collectively show promise as sustainable materials and materials with superior performance versus concrete. 
    more » « less
  2. ; ; ; ; ; (, Energies)
    Rusănescu, C; Ungureanu, N (Ed.)
    Excessive land application of poultry litter (PL) may lead to surface runoff of nitrogen (N) and phosphorus (P), which cause eutrophication, fish death, and water pollution that ultimately have negative effects on humans and animals. Increases in poultry production in the Delmarva Peninsula underscore the need for more efficient, cost-effective, and sustainable disposal technologies for processing PL instead of direct land application. The pyrolysis conversion process can potentially produce nutrient-rich poultry litter biochar (PLB), while the pyrolysis process can change the N and P to a more stable component, thus reducing its runoff. Pyrolysis also kills off any microorganisms that would otherwise trigger negative environmental health effects. This study is to apply an integrated method and investigate the effect of pyrolysis temperature (300 °C, 500 °C), poultry litter source (different feedstock composition), and bedding material mixture (10% pine shavings) on PLB qualities and quantities. Proximate and ultimate analysis showed PL sources and bedding material addition influenced the physicochemical properties of feedstock. The SEM and BET surface results indicate that pyrolysis temperature had a significant effect on changing the PLB morphology and structure, as well as the pH value (7.78 at 300 °C vs. 8.78 at 500 °C), extractable phosphorus (P) (18.73 ppm at 300 °C vs. 11.72 ppm at 500 °C), sulfur (S) (363 ppm at 300 °C vs. 344 ppm at 500 °C), and production yield of PLBs (47.65% at 300 °C vs. 60.62% at 500 °C). The results further suggest that adding a bedding material mixture (10% pine shavings) to PLs improved qualities by reducing the content of extractable P and S, as well as pH values of PLBs. This study also found the increment in both the pore volume and the area of Bethel Farm was higher than that of Sun Farm. Characterization and investigation of qualities and quantities of PLB using the integrated framework suggest that PL from Bethel Farm could produce better-quality PLB at a higher pyrolysis temperature and bedding material mixture to control N and P runoff problems. 
    more » « less
  3. ; ; ; ; (, ACS Applied Materials & Interfaces)
    This study investigates the H2O and CO2 sorption behavior of two chemically distinct polystyrene-divinylbenzene-based ion exchange sorbents: a primary amine and a permanently charged strong base quaternary ammonium (QA+) group with (bi)carbonate counter anions. We compare their distinct interactions with H2O and CO2 through simultaneous thermal gravimetric, calorimetric, gas analysis, and molecular modeling approaches to evaluate their performance for dilute CO2 separations like direct air capture. Thermal and hybrid (heat + low-temperature hydration) desorption experiments demonstrate that the QA+-based sorbent binds both water and CO2 more strongly than the amine counterparts but undergoes degradation at moderate temperatures, limiting its compatibility with thermal swing regeneration. However, a low-temperature moisture-driven regeneration pathway is uniquely effective for the QA+-based sorbent. To inform the energetics of a moisture-based CO2 separation (i.e., a moisture swing), we compare calorimetric water sorption enthalpies to Clausius–Clapeyron-derived total isosteric enthalpies. To our knowledge, this includes the first direct calorimetric measurement of water sorption enthalpy in a QA+-based sorbent. Both methods reveal monolayer-multilayer sorption behavior for both sorbents, with the QA+-based material having slightly higher water sorption enthalpies at the initially occupied strongest sorption sites. Molecular modeling supports this observation, showing higher water sorption energies and denser charge distributions in the QA+-based sorbent at λH2O = 1 mmol/mmolsite. Mixed gas experiments in the QA+-based sorbent show that not only does water influence CO2 binding, but CO2 influences water uptake through counterion-dependent hydration states, and that moisture swing responsiveness in this material causes hydration-induced CO2 release and drying-induced CO2 uptake, an important feature for low-energy CO2 separation under ambient conditions. Overall, the two classes of sorbents offer distinct pathways for the CO2 separation. 
    more » « less
  4. ; ; ; (, Journal of Polymer Science)
    ABSTRACT High sulfur‐content materials (HSMs) prepared via inverse vulcanization are attractive for a range of sustainable material applications, particularly when synthesized from waste‐derived feedstocks such as brown grease (BG). Two BG‐based composites,SunBG90andaBG90, were prepared using elemental sulfur and either native or allylated brown grease, respectively. This study explores the effect of reinforcing these sulfur‐rich networks with low loadings (0.5–2 wt. %) of highcis‐1,4‐content liquid polybutadiene (PBD). Incorporation of PBD resulted in significant increases in storage modulus, with a near‐linear relationship between PBD content and stiffness enhancement for both material types. At −60°C, storage modulus increased more than fivefold foraBG90and more than tripled forSunBG90. In contrast, flexural strength and flexural modulus exhibited non‐linear responses, with diminishing or reversed gains at higher PBD loadings, suggesting limits to rubber domain compatibility and dispersion. Thermal analysis confirmed high decomposition temperatures (212°C–226°C) and stable glass transitions, indicating thermal robustness of the reinforced networks. Compared with previous studies requiring higher PBD loadings, these results demonstrate that BG‐based HSMs can be effectively reinforced at low additive levels, offering mechanically robust, low‐cost, and renewable alternatives for structural applications. 
    more » « less
  5. ; ; ; ; (, Macromol)
    The unique properties and sustainability advantages of sulfur polymer cement have led to efforts to use them as alternatives to traditional Portland cement. The current study explores the impact of environmental stresses on the strength development of polymer composite SunBG90, a material composed of animal and plant fats/oils vulcanized with 90 wt. % sulfur. The environmental stresses investigated include low temperature (−25 °C), high temperature (40 °C), and submersion in water, hexanes, or aqueous solutions containing strong electrolyte, strong acid, or strong base. Samples were analyzed for the extent to which exposure to these stresses influenced the thermo-morphological properties and the compressional strength of the materials compared to identical materials allowed to develop strength at room temperature. Differential scanning calorimetry (DSC) analysis revealed distinct thermos-morphological transitions in stressed samples and the notable formation of metastable γ-sulfur in hexane-exposed specimens. Powder X-ray diffraction confirmed that the crystalline domains identified by DSC were primarily γ-sulfur, with ~5% contribution of γ-sulfur in hexane-exposed samples. Compressive strength testing revealed high strength retention other than aging at elevated temperatures, which led to ~50% loss of strength. These findings reveal influences on the strength development of SunBG90, lending important insight into possible use as an alternative to OPC. 
    more » « less
  • Citation Formats
  • MLA
  • APA
  • Chicago
  • BibTeX
  • Save / Share this Record
  • Send to Email