Title: Mechanical Characterization of Epoxy Resin Manufactured Using Frontal Polymerization
Frontal polymerization (FP) is a promising alternative manufacturing method for thermoset-based fiber-reinforced polymer composites (FRP) in comparison with the traditional autoclave/oven-curing method, due to its rapid curing process, low energy consumption, and low cost. Optimizing the weight contents of initiators relative to the resin’s mass is needed to adjust the mechanical properties of FRPs in industrial applications. This study investigates the effect of varying the photo-initiator (PI) weight content on tensile properties and the frontal polymerization characteristics, including the front velocity, front temperature, and degree of cure, in the FP process of the epoxy resin. Specifically, a dual-initiator system, including PI and thermal-initiator (TI), is used to initiate the polymerization process by ultraviolent (UV) light. The weight content of the TI is fixed at 1 w%, and the relative PI concentration is varied from 0.2 w% to 0.5 wt%. Results show that increasing the PI amount from 0.2 wt% to 0.3 wt% significantly improves the front velocity and the degree of cure by about two times. Increasing the PI content from 0.3 wt% to 0.4 wt% results in 15% and 26% higher degree of cure and front velocity, respectively. Moreover, due to the different front velocity in the top and bottom regions of the specimen, the specimens with 0.4 wt% PI exhibited a curved shape. The specimen with 0.5 wt% PI is thermally degraded and foamed. By comparing tensile properties, it is found that increasing the PI concentration from 0.2 wt% to 0.3 wt% improves the tensile strength and Young’s modulus by 3.91% and 7%, respectively, while the tensile strength and the Young’s modulus of frontal polymerized specimens are on average 8% and 14% higher than traditionally oven-cured ones, respectively.  more » « less
Award ID(s):
2208130
NSF-PAR ID:
10469089
Author(s) / Creator(s):
; ; ; ; ; ;
Publisher / Repository:
DEStech Publications
Date Published:
Format(s):
Medium: X
Location:
Greater Boston, MA
Sponsoring Org:
National Science Foundation
More Like this
  1. Due to the incapability of one-dimensional (1D) and two-dimensional (2D) models in simulating the frontal polymerization (FP) process in laminated composites with multiple fiber angles (e.g., cross-ply, angle-ply), modeling a three-dimensional (3D) domain, which is more representative of practical applications, provides critical guidance in the control and optimization of the FP process. In this paper, subroutines are developed to achieve the 3D modeling of FP in unidirectional and cross-ply carbon fiber laminates with finite element analysis, which are validated against the experimental data. The 3D model is employed to study the effect of triggering direction in relevance to the fiber direction on the FP process, which cannot be studied using traditional 1D/2D models. Our findings suggest that triggering in the fiber direction leads to a higher front velocity, in comparison to cases where front was triggered in the direction perpendicular to the fiber. Moreover, the average front velocity in cross-ply laminates is on average 20~25% lower than that in unidirectional laminates. When triggered using two opposite fronts in the in-plane direction, the maximum temperature of the thermal spike in the cross-ply laminate, when two fronts merge, is about 100 °C lower than that in the unidirectional laminate. In cross-ply laminates, a sloped pattern forms across the thickness direction as the front propagates in the in-plane direction, as opposed to the traditionally observed uniform propagation pattern in unidirectional cases. Furthermore, the effect of thermal conductivity is studied using two additional composite laminates with glass (1.14 W/m·K) and Kevlar fibers (0.04 W/m·K). It is shown that the frontal velocity, degree of cure, and the thermal spike temperature decrease as the thermal conductivity reduces. 
    more » « less
  2. Abstract

    Frontal polymerization (FP) of epoxy monomers is typically achieved with a radical‐induced cationic frontal polymerization (RICFP) process that combines a thermal radical initiator with an onium salt superacid generator. In this paper, we show that both thermal and UV‐initiated cationic frontal polymerizations are possible for common epoxy and vinyl ether monomers with only an iodonium superacid generator in the absence of a standalone thermal radical initiator. Increasing superacid generator concentration resulted in an increase in front velocity, as did the addition of vinyl ether to epoxies. The front velocity is reduced by the addition of 4‐methoxyphenol (MeHQ), indicating free‐radicals play a significant role.

     
    more » « less
  3. Ozden, O. (Ed.)
    Adhesively bonded composite joints can help reduce weight in structures and avoid material damage from fastener holes, but stress concentrations formed at the edges of the adhesive bond line are a main cause of failure. Stress concentrations within the adhesive can be reduced by lowering the stiffness at these edges and increasing the stiffness in the center of the joint. This may be achieved using a dual-cure adhesive system, where conventional curing is first used to bond a lap joint, after which high energy radiation is applied to the joint to induce additional crosslinking in specific regions. Anhydride-cured epoxy resins have been formulated to include a radiation sensitizer enabling the desired cure behavior. Tensile testing was performed on cured systems containing varying levels of radiation sensitizer in order to evaluate its effects on young’s modulus as a function of radiation dose. 
    more » « less
  4. Since the inception of carbon fiber-reinforced polymers (CFRPs) they have steadily gained in popularity due to their light weight, high tensile strength and modulus, and environmental toughness. However, curing of CFRPs of the thermosetting type generally must be performed within an autoclave, whose fixed, physical dimensions effectively limit the maximum size of the part. Alternative curing chemistries may potentially eliminate the requirement for an autoclave, which would allow creation of much larger panels. This project seeks to develop a thermoset composite matrix that is radiation-curable using the Cu(I)-catalyzed azide-alkyne cycloaddition (CuAAC) click reaction. Previously, Storey et al.(1,2) reported that the azide-modified epoxy resin, di(3-azido-2-hydroxypropyl) ether of bisphenol-A (DAHP-BPA), could be cured by reaction with polyfunctional alkyne crosslinkers under mild conditions using Cu(I) catalysis. In the absence of reducing agents, Cu(II) compounds are catalytically inactive; however, upon exposure to ultraviolet light, they are reduced to Cu(I), which then catalyzes the reaction, allowing it to progress to a high degree of cure at room temperature. Herein, we report the kinetics of photo-induced CuAAC polymerization of the DAHP-BPA and several polyfunctional propargyl amine based crosslinkers, monitored by real-time FTIR as well as mechanical properties of fully cured materials. Polymerizations were studied as a function of Cu(II) compound type, Cu(II) concentration, UV light (365 nm) intensity, and duration of irradiation. 
    more » « less
  5. Abstract

    Formulations containing vinyl ethers and epoxy were successfully polymerized through a radical‐induced cationic frontal polymerization mechanism, using an iodonium salt superacid generator with a peroxide thermal radical initiator and fumed silica as a filler. It was found that an increase of vinyl ether content resulted in higher front velocities for divinyl ethers in formulations with trimethylolpropane triglycidyl ether. However, increased hydroxymonovinyl ether either decreased the front velocity or suppressed frontal polymerization. The kinetic effects of the superacid generator and thermal radical initiator with varying vinyl ether content were also studied. It was observed that increasing concentrations of initiators increased the front velocity, with the system exhibiting higher sensitivity to the superacid generator concentration.

     
    more » « less