In this paper, we present concurrent atomistic-continuum (CAC) simulations of the hydrogen (H) diffusion along a grain boundary (GB), nearby which a large population of dislocations are piled up, in a plastically deformed bi-crystalline bcc iron sample. With the microscale dislocation slip and the atomic structure evolution at the GB being simultaneously retained, our main findings are: (i) the accumulation of tens of dislocations near the H-charged GB can induce a local internal stress as high as 3 GPa; (ii) the more dislocations piled up at the GB, the slower the H diffusion ahead of the slip–GB intersection; and (iii) H atoms diffuse fast behind the pileup tip, get trapped within the GB, and diffuse slowly ahead of the pileup tip. The CAC simulation-predicted local H diffusivity, Dpileup−tip, and local stresses, σ, are correlated with each other. We then consolidate such correlations into a mechanics model by considering the dislocation pileup as an Eshelby inclusion. These findings will provide researchers with opportunities to: (a) characterize the interplay between plasticity, H diffusion, and crack initiation underlying H-induced cracking (HIC); (b) develop mechanism-based constitutive rules to be used in diffusion–plasticity coupling models for understanding the interplay between mechanical and mass transport in materials at the continuum level; and (c) connect the atomistic deformation physics of polycrystalline materials with their performance in aqueous environments, which is currently difficult to achieve in experiments.
more »
« less
Multiscale computational and experimental analysis of slip-GB reactions: In situ high-resolution electron backscattered diffraction and concurrent atomistic-continuum simulations
In this paper, in situ high-resolution electron backscattered diffraction (EBSD) is combined with concurrent atomistic-continuum (CAC) simulations to study the interactions between dislocation-mediated slip and grain boundaries (GBs) in Ni. It is found that the local stress associated with slip-GB intersections first increases upon the pileup of dislocations, then remains high even after the nucleation of dislocations in the neighboring grain, only relaxing after the nucleated dislocations propagate away from the GB due to more incoming dislocations participating in the pileup. The local stress relaxation is accompanied by an atomic-scale GB structure reconfiguration, which affects not only the subsequent dislocation transmission, but also the configuration of those dislocations away from the GB. These findings demonstrate the importance of incorporating local stress history at higher length scale models, such as crystal plasticity finite element.
more »
« less
- PAR ID:
- 10474403
- Publisher / Repository:
- Elsevier
- Date Published:
- Journal Name:
- Scripta Materialia
- Volume:
- 232
- Issue:
- C
- ISSN:
- 1359-6462
- Page Range / eLocation ID:
- 115500
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Abstract Dislocations, linear defects in a crystalline lattice characterized by their slip systems, can provide a record of grain internal deformation. Comprehensive examination of this record has been limited by intrinsic limitations of the observational methods. Transmission electron microscopy reveals individual dislocations, but images only a few square$$\upmu$$ m of sample. Oxidative decoration requires involved sample preparation and has uncertainties in detection of all dislocations and their types. The possibility of mapping dislocation density and slip systems by conventional (Hough-transform based) EBSD is investigated here with naturally and experimentally deformed San Carlos olivine single crystals. Geometry and dislocation structures of crystals deformed in orientations designed to activate particular slip systems were previously analyzed by TEM and oxidative decoration. A curvature tensor is calculated from changes in orientation of the crystal lattice, which is inverted to calculate density of geometrically necessary dislocations with the Matlab Toolbox MTEX. Densities of individual dislocation types along with misorientation axes are compared to orientation change measured on the deformed crystals. After filtering (denoising), noise floor and calculated dislocation densities are comparable to those reported from high resolution EBSD mapping. For samples deformed in [110]c and [011]c orientations EBSD mapping confirms [100](010) and [001](010), respectively, as the dominant slip systems. EBSD mapping thus enables relatively efficient observation of dislocation structures associated with intracrystalline deformation, both distributed, and localized at sub-boundaries, over substantially larger areas than has previously been possible. This will enable mapping of dislocation structures in both naturally and experimentally deformed polycrystals, with potentially new insights into deformation processes in Earth’s upper mantle.more » « less
-
Bulk, polycrystalline (Co, Cu, Mg, Ni, Zn)O was synthesized using solid-state sintering. Micropillars were prepared and mechanically deformed along three crystallographic orientations: (001), (101), and (111). Pillars (001) and (111) cracked, while Pillar (101) remained intact. Pillars (001) and (101) exhibited activated slip systems, confirmed by a large stress drop, and the presence of slip bands, respectively. Schmid factor (SF) analysis was performed to examine the effect of grain orientations on dislocation activity and slip behavior. SF values range from 0 to 0.5, with non-zero values indicating potential for slip. Six slip systems exist in the (Co, Cu, Mg, Ni, Zn)O rock salt crystal structure: 1/2⟨110⟩11¯0. For the (001) orientation, four slip systems are potentially active (SF = 0.5). For the (101) orientation, there are four potentially active slip systems (SF = 0.25). For the (111) orientation, no potentially active slips systems exist (SF = 0). Dislocation structures, which were observed post-compression via transmission electron microscopy, demonstrated variations in size, number, and distribution across the pillar, depending on micropillar orientation. Entangled dislocations created misorientation in Pillar (001), which led to the possible formation of subgrains, while singular dislocations were observed in Pillar (101), and a lack of dislocations was observed in Pillar (111). Zener–Stroh type dislocation entanglement-mediated cracking is the proposed cause of the transgranular-type cracks in Pillar (001). The possible subgrain formation, or lack of formation, respectively, caused intergranular-type cracks to additionally form in Pillar (001), while Pillar (111) only exhibited transgranular-type brittle fracture. In combination, these findings highlight the importance of dislocation activity, without the need for elevated temperature, and grain orientation in controlling the mechanical deformation response in single-phase (Co, Cu, Mg, Ni, Zn)O.more » « less
-
Structural aluminum alloys are often less-than ideal materials for studying sub-grain strain gradients via EBSD, at typical resolution settings. Sharply defined slip bands are not generally observed due to cross-slip, and secondphase particles formed during solidification of work-hardened alloys provide obstacles that disrupt potential structure development, leading to what can seem like random distributions of geometrically necessary dislocations (GNDs). This study considers the roles of length-scale and second-phase particles in sub-grain distributions of AA6016-T4 following deformation. Second-phase particles are shown to play a stronger role than grain boundaries (GBs) in local GND accumulations. The net Burgers vector is used to show the transition from crystallographic-level slip to macro-scale slip as length scale increases, with a corresponding transition in the GND vs. step size graph. A strain gradient crystal plasticity model is applied to assess predictability of the observations. Real 3D structures were extracted, via serial sectioning, following application of different strain paths. Predicted GND and total dislocation evolution closely follows observed values. The model is then used to study the relative contributions of GBs and second-phase particles to GND localization, leading to the conclusion that second-phase particles must be included in the model to reflect observed behavior.more » « less
-
A novel dislocation-density-based crystal plasticity model for nanocrystalline face-centered cubic metals is developed based on the thermally-activated mechanism of dislocations depinning from grain boundaries. Dislocations nucleated from grain boundary dislocation sources are assumed to be the primary carriers of plasticity in the nanocrystals. The evolution of the dislocation density thereby involves a competition between the nucleation of dislocations from grain boundary defect structures, such as ledges, and the absorption of dislocations into the grain boundary via diffusion processes. This model facilitates the simulation of plastic deformation in nanocrystalline metals, with consideration of the initial microstructure resulting from a particular processing method, to be computed as a direct result of dislocation-mediated plasticity only. The exclusion of grain boundary-mediated plasticity mechanisms in the formulation of the crystal plasticity model allows for the exploration of the fundamental role dislocations play in nanocrystalline plasticity. The combined effect of average grain size, grain size distribution shape, and initial dislocation density on the mechanical performance and strain-rate sensitivity are explored with the model. Further, the influence of the grain boundary diffusivity on post-yielding strain-hardening behavior is investigated to discern the impact that the choice of processing route has on the resulting deformation response of the material.more » « less
- Free Publicly Accessible Full Text
-
Accepted Manuscript1.0
- Journal Article:
- https://doi.org/10.1016/j.scriptamat.2023.115500