Inorganic salt hydrates are promising materials for thermochemical energy storage as they undergo reversible solid-gas chemical reactions with water vapor to yield high energy densities with negligible self-discharge. However, material-level challenges such as structural and hygrothermal instabilities during the dehydration (charging) and hydration (discharging) reaction have limited their practical application in the buildings sector. The objective of this study is to address these irreversibilities in SrCl2 and MgCl2 by establishing a fabrication procedure that minimizes vapor diffusion resistance and lowers kinetic barriers for nucleation via particle size reduction. Furthermore, the distinct phase behavior of these two salts is leveraged to demonstrate a new binary salt mixture. Characterization of these materials was done using simultaneous thermogravimetric analysis (TGA) and differential scanning calorimetry (DSC) with a humidity generator. The results demonstrate that ball milling to particle sizes <50 μm yields a structurally stable material with improved hydration kinetics, while a 50/50 mass ratio of the binary mixture extends the range of conditions for the hydration reaction. Importantly, the salt mixture achieves a high specific energy density of 1100 J g-1 and peak thermal power output of 1.4 W g-1 under conditions at which the individual salts either deliquesce (MgCl2) or do not fully/rapidly hydrate (SrCl2). This work provides a procedure for the standardized fabrication and rational design of thermochemical salt mixtures with complementary phase behavior.
more »
« less
Salt Hydrate Thermochemical Energy Storage in Buildings: Analyzing Storage Density and Thermal Power Output
Thermochemical energy storage is promising for building applications as it offers high energy density and near-lossless storage. For example, inorganic salt hydrates that undergo reversible solid-gas thermochemical reactions can be used for thermal load shifting and/or shedding in buildings. However, this technology is still in early stages of development and drawbacks need to be addressed to make such a thermal battery viable. As salt hydrates differ in their morphology, crystal and/or particle size, and hygrothermal stability, it is critical to characterize thermochemical reactions accurately under specific operating conditions. Not only is the amount of heat delivered important, but so is the rate at which this heat is extracted for thermal end-use in buildings. However, the latter is not well reported in the literature, which is largely focused on energy storage rather than power density during the hydration reaction (battery discharge). To address this gap and the lack of standardized measurement methods, this work lays out a systematic simultaneous thermal analysis (STA) method for characterizing five different salt hydrate thermochemical materials (TCM). The effects of particle size, temperature and vapor pressure are analyzed to obtain the energy storage density and thermal power density across a full hydration-dehydration cycle under controlled conditions.
more »
« less
- Award ID(s):
- 2238705
- PAR ID:
- 10478934
- Publisher / Repository:
- American Society of Mechanical Engineers
- Date Published:
- Journal Name:
- Proceedings of the ASME 2023 17th International Conference on Energy Sustainability collocated with the ASME 2023 Heat Transfer Summer Conference
- ISBN:
- 978-0-7918-8718-9
- Subject(s) / Keyword(s):
- energy storage, thermodynamics, heat energy generation/storage/transfer, energy conversion, alternative energy sources
- Format(s):
- Medium: X
- Location:
- Washington, DC, USA
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Structurally stabilized composites are promising for using phase change materials in high‐temperature thermal energy storage (TES). However, conventional skeleton materials, which typically comprise 30–50 wt% of the composite, mainly provide sensible heat storage and contribute minimally to overall energy density. This study introduces a new class of redox‐active oxide‐molten salt (ROMS) composites that overcome this limitation by combining sensible, latent, and thermochemical heat storage in a single particle. Specifically, porous, redox‐active Ca2AlMnO5+δ(CAM) complex oxide particles were demonstrated as a suitable support matrix, with the pores filled by eutectic NaCl/CaCl2salt. X‐ray diffraction confirms excellent phase compatibility between CAM and the salt. Scanning electron microscopy/energy dispersive X‐ray spectroscopy and nano X‐ray tomography show good salt infiltration and wettability within the CAM pores. Thermogravimetric analysis reveals that a 60 wt% CAM/40 wt% salt composite achieves an energy density of 267 kJ kg−1over a narrow 150 °C window, with ≈50 kJ kg−1from thermochemical storage. Additionally, the composite shows higher thermal conductivity than salt alone, enabling faster energy storage and release. ROMS composites thus represent a novel and efficient solution for high‐performance TES.more » « less
-
Inorganic salt hydrates are promising phase-change materials (PCMs) for thermal energy storage due to their high latent heat of fusion. However, their practical application is often limited by their unstable form, dehydration, large supercooling, and low thermal conductivity. Porous melamine foam and its carbonized derivatives are potential supporting porous materials to encapsulate inorganic salt hydrate PCMs to address these problems. This work investigates the effect of pyrolysis temperature on the morphology and structure of the carbonized foams and their thermal energy storage performance. Pyrolysis of melamine foam at 700−900 °C leads to the formation of crystalline sodium cyanate and sodium carbonate particles on the foam skeleton surface, which allows the spontaneous impregnation of the carbon foam with molten CaCl2·6H2O.The form-stable foam-CaCl2·6H2O composite effectively suppresses supercooling and dehydration, demonstrating the efficacy of carbon foam as a promising supporting material for inorganic salt hydrate PCMs.more » « less
-
Aqueous redox flow batteries using low-cost organic and inorganic active materials have received growing interest for sustainable energy storage. In this study, a low-cost, high redox potential (1.08 V vs. NHE) and high capacity ammonium bromide (NH 4 Br, 214.4 A h L −1 ) catholyte was coupled with an organic viologen anolyte to demonstrate 1.51 V high voltage (SPr) 2 V/Br − aqueous redox flow batteries under pH neutral conditions for the first time. Benefitting from the high water solubility of both the NH 4 Br catholyte and (SPr) 2 V anolyte, the newly designed (SPr) 2 V/Br − organic flow battery was operated at up to 1.5 M and an energy density of up to 30.4 W h L −1 . Using multiwall carbon nanotubes as an electrochemical additive for the Br 3 − /Br − redox couple, the highly energy dense (SPr) 2 V/Br − flow battery manifested outstanding current performance, up to 78% energy efficiency at 40 mA cm −2 current density and 227 mW cm −2 power density, the highest power density known for pH neutral organic flow batteries.more » « less