The BaTiO3 ceramics applications based on electronic properties have very high gradient scientific and industrial-technological interests. Our scientific research has been based on nano BaTiO3 modified with Yttrium based organometallic salt (MOD-Y). The samples have been consolidated at a sintering temperature of 1350 °C. Within the study, the new frontiers for different electronic properties between the layers of BaTiO3 grains have been introduced. The research target was grain boundary investigations and the influence on dielectric properties. After scanning electron microscopy and dielectric measurements, it has been established that modified BaTiO3 samples with larger grains showed a better compact state that led to a higher dielectric constant value. DC bias stability was also investigated and showed a connection between the grain size and capacitance stability. Analyses of functions that could approximate experimental curves were successfully employed. Practical application of fractal corrections was performed, based on surface (αs) and pore size (αp) corrections, which resulted in obtainment of the relation between the capacitance and Curie temperature. Successful introduction of fractal corrections for capacitance-Curie temperature dependence for a set of experimental data is an important step towards further miniaturization of intergranular capacitors.
more »
« less
Temperature dependence of dielectric nonlinearity of BaTiO 3 ceramics
In many commercially utilized ferroelectric materials, the motion of domain walls is an important contributor to the functional dielectric and piezoelectric responses. This paper compares the temperature dependence of domain wall motion for BaTiO3 ceramics with different grain sizes, point defect concentrations, and formulations. The grain boundaries act as significant pinning points for domain wall motion such that fine-grained materials show smaller extrinsic contributions to the properties below the Curie temperature and lower residual ferroelectric contributions immediately above the Curie temperature. Oxygen vacancy point defects make a modest change in the extrinsic contributions of undoped BaTiO3 ceramics. In formulated BaTiO3, extrinsic contributions to the dielectric response were suppressed over a wide temperature range. It is believed this is due to a combination of reduced grain size, the existence of a core-shell microstructure, and a reduction in domain wall continuity over the grain boundaries.
more »
« less
- PAR ID:
- 10480943
- Publisher / Repository:
- OAE Publishing
- Date Published:
- Journal Name:
- Microstructures
- Volume:
- 3
- Issue:
- 4
- ISSN:
- 2770-2995
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Ferroelectric materials such as barium titanate (BaTiO3) have a wide range of applications in nano scale electronic devices due to their outstanding properties. In this study, we developed an easily extendable atomistic ReaxFF reactive force field for BaTiO3 that can capture both its field- as well as temperature-induced ferroelectric hysteresis and corresponding changes due to surface chemistry and bulk defects. Using our force field, we were able to reproduce and explain a number of experimental observations: (1) existence of a critical thickness of 4.8 nm below which ferroelectricity vanishes in BaTiO3; (2) migration and clustering of oxygen vacancies (OVs) in BaTiO3 and reduction in the polarization and the curie temperature due to the OVs; (3) domain wall interaction with surface chemistry to influence ferroelectric switching and polarization magnitude. This new computational tool opens up a wide range of possibilities for making predictions for realistic ferroelectric interfaces in energy-conversion, electronic and neuromorphic systems.more » « less
-
The effect of an electric field on local domain structure near a 24° tilt grain boundary in a 200 nm-thick Pb(Zr0.2Ti0.8)O3bi-crystal ferroelectric film was probed using synchrotron nanodiffraction. The bi-crystal film was grown epitaxially on SrRuO3-coated (001) SrTiO324° tilt bi-crystal substrates. From the nanodiffraction data, real-space maps of the ferroelectric domain structure around the grain boundary prior to and during application of a 200 kV cm−1electric field were reconstructed. In the vicinity of the tilt grain boundary, the distributions of densities ofc-type tetragonal domains with thecaxis aligned with the film normal were calculated on the basis of diffracted intensity ratios ofc- anda-type domains and reference powder diffraction data. Diffracted intensity was averaged along the grain boundary, and it was shown that the density ofc-type tetragonal domains dropped to ∼50% of that of the bulk of the film over a range ±150 nm from the grain boundary. This work complements previous results acquired by band excitation piezoresponse force microscopy, suggesting that reduced nonlinear piezoelectric response around grain boundaries may be related to the change in domain structure, as well as to the possibility of increased pinning of domain wall motion. The implications of the results and analysis in terms of understanding the role of grain boundaries in affecting the nonlinear piezoelectric and dielectric responses of ferroelectric materials are discussed.more » « less
-
In this work with a model system (Ba,Ca)TiO3, we analyze the morphologies of CaTiO3-rich precipitates and their impacts on the microstructures in their surrounding BaTiO¬3-rich matrix. Also, the response of ferroelectric domains around CaTiO3-rich precipitates during heating and cooling is observed in-situ with transmission electron microscopy. Domains attached to precipitates are observed remaining unchanged up to the Curie point at which they disappear. During cooling, domains are observed to form in the vicinity of precipitates and being held in place down to room temperature. Both observations corroborate previous findings that precipitates act as domain pinning points, behaving in a similar manner to earlier experiments with electrical field biasing. Dislocations are often seen around precipitates in the matrix grain and are observed interfering with domains during heating cycles. Dislocations may provide an additional mechanism to restrict domain wall motion and offer a greater piezoelectric hardening effect.more » « less
-
Adding excessive metal oxide doping to a powder batch is a known way to compensate for the loss of volatile cation species during high temperature sintering. An important case in the piezoelectric ceramics is the bismuth oxide in the lead-free ferroelectric ceramic bismuth sodium titanate (BNT). Building from the earlier knowledge about excessive bismuth oxide's influences on the properties of BNT, we further note that varying the sintering temperature can both control the distribution of excessive Bi3+ and impact the relaxor/normal ferroelectric behaviors and corresponding phase transition. In addition to the nature of polarization, the sintering temperature also significantly manipulates the electrical conductivity. A hypothetical mechanism for the resistive grain boundary is proposed, based on inferences from electrical—microstructure—processing relations in 85% Bi0.5Na0.5TiO3-15% BaTiO3 with batched Bi2O3 excess and acceptor Mg2+ in a co-doped strategy.more » « less
- Free Publicly Accessible Full Text
-
Accepted Manuscript1.0
- Journal Article:
- https://doi.org/10.20517/microstructures.2023.43