Highly conductive Ge-doped AlN with conductivity of 0.3 (Ω cm)−1 and electron concentration of 2 × 1018 cm−3 was realized via a non-equilibrium process comprising ion implantation and annealing at a moderate thermal budget. Similar to a previously demonstrated shallow donor state in Si-implanted AlN, Ge implantation also showed a shallow donor behavior in AlN with an ionization energy ∼80 meV. Ge showed a 3× higher conductivity than its Si counterpart for a similar doping level. Photoluminescence spectroscopy indicated that higher conductivity for Ge-doped AlN was achieved primarily due to lower compensation. This is the highest n-type conductivity reported for AlN doped with Ge to date and demonstration of technologically useful conductivity in Ge-doped AlN.
This content will become publicly available on October 23, 2024
Near-ideal behavior in Schottky contacts to Si-doped AlN was observed as evidenced by a low ideality factor of 1.5 at room temperature. A temperature-independent Schottky barrier height of 1.9 eV was extracted from temperature-dependent I–V measurements. An activation energy of ∼300 meV was observed in the series resistance, which corresponded to the ionization energy of the deep Si donor state. Both Ohmic and Schottky contacts were stable up to 650 °C, with around four orders of magnitude rectification at this elevated temperature. These results demonstrate the potential of AlN as a platform for power devices capable of operating in extreme environments.
more » « less- Award ID(s):
- 2145340
- NSF-PAR ID:
- 10495575
- Publisher / Repository:
- AIP
- Date Published:
- Journal Name:
- Applied Physics Letters
- Volume:
- 123
- Issue:
- 17
- ISSN:
- 0003-6951
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
more » « less
-
more » « less
State-of-the-art semiconducting aluminum nitride (AlN) films were characterized by cathodoluminescence (CL) spectroscopy in the range of 200–500 nm in an attempt to identify the energy levels within the bandgap and their associated defects. Near-band edge emission (around 206 nm) and high-intensity peaks centered in the near UV range (around 325 nm) are observed for both n- and p-type AlN films. The near UV peaks are potentially associated with oxygen contamination in the films. The p-type AlN films contain at least two unidentified peaks above 400 nm. Assuming that the dopant concentration is independent of compensation (i.e., in the perfect doping limit), three effective donor states are found from Fermi–Dirac statistics for Si-doped AlN, at ∼0.035, ∼0.05, and ∼0.11 eV. Similarly, a single effective acceptor energy of ∼0.03–0.05 eV (depending on the degeneracy factory considered) was found for Be doped AlN. CL investigation of doped AlN films supports claims that AlN may be a promising optoelectronic material, but also points to contaminant mitigation and defect theory as major areas for future study.
-
more » « less
High room temperature n-type mobility, exceeding 300 cm2/Vs, was demonstrated in Si-doped AlN. Dislocations and CN−1 were identified as the main compensators for AlN grown on sapphire and AlN single crystalline substrates, respectively, limiting the lower doping limit and mobility. Once the dislocation density was reduced by the growth on AlN wafers, C-related compensation could be reduced by controlling the process supersaturation and Fermi level during growth. While the growth on sapphire substrates supported only high doping ([Si] > 5 × 1018 cm−3) and low mobility (∼20 cm2/Vs), growth on AlN with proper compensation management enabled controlled doping at two orders of magnitude lower dopant concentrations. This work is of crucial technological importance because it enables the growth of drift layers for AlN-based power devices.
-
more » « less
We report the effect of extended duration electron beam exposure on the minority carrier transport properties of 10 MeV proton irradiated (fluence ∼1014cm−2) Si-doped
β -Ga2O3Schottky rectifiers. The diffusion length (L ) of minority carriers is found to decrease with temperature from 330 nm at 21 °C to 289 nm at 120 °C, with an activation energy of ∼26 meV. This energy corresponds to the presence of shallow Si trap-levels. Extended duration electron beam exposure enhancesL from 330 nm to 726 nm at room temperature. The rate of increase forL is lower with increased temperature, with an activation energy of 43 meV. Finally, a brief comparison of the effect of electron injection on proton irradiated, alpha-particle irradiated and a reference Si-dopedβ -Ga2O3Schottky rectifiers is presented. -
more » « less
Abstract This letter reports the demonstration of Aluminum nitride (AIN) Schottky barrier diodes on bulk AlN substrates by metalorganic chemical vapor phase deposition with breakdown voltages exceeding 3 kV. The devices exhibited good rectifying characteristics with ON/OFF ratios of 106–108and excellent thermal stability from 298 to 623 K. The device Schottky barrier height increased from 0.89 to 1.85 eV, and the ideality factor decreased from 4.29 to 1.95 with increasing temperature, ascribed to the inhomogeneous metal/AlN interface. This work demonstrates the potential of AlN as an ultra-wide bandgap semiconductor for developing multi-kV AlN high-voltage and high-power devices.