Micro- and nanoporous materials have gathered attention from the scientific community due to their size dependent properties, including but not limited to high specific surface area, surface diffusivity, bulk diffusivity and permeability, catalytic activity, and distinct optical properties. In this work, spherical nanoporous copper (np-Cu) powders, due to their nanosized porosity and low Cu2O content, show hemispherical total reflectance of 20% which is significantly lower than its bulk counterpart value for solid or molten copper of approximately 97% at wavelengths of most commercial Laser Powder Bed Fusion (L-PBF) commercial machines. The low-reflectance of np-Cu powders has the potential to be used in L-PBF to improve laser absorption, volumetric energy efficiency, and throughput of this additive manufacturing process. In fact, a prepared mixture of solid Cu powders containing only 5 wt.% of np-Cu powders reflects 34.8 % less than pure copper powders as shown in this paper. Np-Cu powders are fabricated via chemical dealloying of gas atomized CuAl alloy in a robust and scalable approach, and then mixed with pure copper powders to prepare hybrid feedstocks. Under this framework, the crucial role of deglomeration strategies to achieve homogeneity and flowability of np-Cu/Cu hybrid mixtures are evaluated via particle imaging to determine agglomerate size and composition with an eye at obtaining a high-quality print in L-PBF. In np-Cu powders fabrication, washing them in low-surface tension fluids upholds the highest degree of deglomeration in their fabrication process, and for hybrid feedstocks preparation, pre-mixing Cu and CuAl prior to dealloying yields the best homogeneity results with smallest size of agglomerates and good flowability.
This content will become publicly available on December 1, 2025
Laser powder-bed fusion (L-PBF) additive manufacturing presents ample opportunities to produce net-shape parts. The complex laser-powder interactions result in high cooling rates that often lead to unique microstructures and excellent mechanical properties. Refractory high-entropy alloys show great potential for high-temperature applications but are notoriously difficult to process by additive processes due to their sensitivity to cracking and defects, such as un-melted powders and keyholes. Here, we present a method based on a normalized model-based processing diagram to achieve a nearly defect-free TiZrNbTa alloy via in-situ alloying of elemental powders during L-PBF. Compared to its as-cast counterpart, the as-printed TiZrNbTa exhibits comparable mechanical properties but with enhanced elastic isotropy. This method has good potential for other refractory alloy systems based on in-situ alloying of elemental powders, thereby creating new opportunities to rapidly expand the collection of processable refractory materials via L-PBF.
more » « less- NSF-PAR ID:
- 10503322
- Publisher / Repository:
- Springer Nature
- Date Published:
- Journal Name:
- Communications Materials
- Volume:
- 5
- Issue:
- 1
- ISSN:
- 2662-4443
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
more » « less
Abstract -
NA (Ed.)more » « less
Abstract Multiprincipal-element alloys are an enabling class of materials owing to their impressive mechanical and oxidation-resistant properties, especially in extreme environments1,2. Here we develop a new oxide-dispersion-strengthened NiCoCr-based alloy using a model-driven alloy design approach and laser-based additive manufacturing. This oxide-dispersion-strengthened alloy, called GRX-810, uses laser powder bed fusion to disperse nanoscale Y2O3particles throughout the microstructure without the use of resource-intensive processing steps such as mechanical or in situ alloying3,4. We show the successful incorporation and dispersion of nanoscale oxides throughout the GRX-810 build volume via high-resolution characterization of its microstructure. The mechanical results of GRX-810 show a twofold improvement in strength, over 1,000-fold better creep performance and twofold improvement in oxidation resistance compared with the traditional polycrystalline wrought Ni-based alloys used extensively in additive manufacturing at 1,093 °C5,6. The success of this alloy highlights how model-driven alloy designs can provide superior compositions using far fewer resources compared with the ‘trial-and-error’ methods of the past. These results showcase how future alloy development that leverages dispersion strengthening combined with additive manufacturing processing can accelerate the discovery of revolutionary materials.
-
more » « less
This study investigated the influence of diverse laser processing parameters on the thermophysical properties of Ti-6Al-4V and AlSi10Mg alloys manufactured via laser powder bed fusion. During fabrication, the laser power (50 W, 75 W, 100 W) and laser scanning speed (0.2 m/s, 0.4 m/s, 0.6 m/s) were adjusted while keeping other processing parameters constant. Besides laser processing parameters, this study also explored the impact of test temperatures on the thermophysical properties of the alloys. It was found that the thermophysical properties of L-PBF Ti-6Al-4V alloy samples were sensitive to laser processing parameters, while L-PBF AlSi10Mg alloy showed less sensitivity. In general, for the L-PBF Ti-6Al-4V alloy, as the laser power increased and laser scan speed decreased, both thermal diffusivity and conductivity increased. Both L-PBF Ti-6Al-4V and L-PBF AlSi10Mg alloys demonstrated similar dependence on test temperatures, with thermal diffusivity and conductivity increasing as the test temperature rose. The CALPHAD software Thermo-Calc (2023b), applied in Scheil Solidification Mode, was utilized to calculate the quantity of solution atoms, thus enhancing our understanding of observed thermal conductivity variations. A detailed analysis revealed how variations in laser processing parameters and test temperatures significantly influence the alloy’s resulting density, specific heat, thermal diffusivity, and thermal conductivity. This research not only highlights the importance of processing parameters but also enriches comprehension of the mechanisms influencing these effects in the domain of laser powder bed fusion.
-
more » « less
Abstract An oxygen‐resistant refractory high‐entropy alloy is synthesized in microlattice or bulk form by 3D ink‐extrusion printing, interdiffusion, and silicide coating. Additive manufacturing of equiatomic HfNbTaTiZr is implemented by extruding inks containing hydride powders, de‐binding under H2, and sintering under vacuum. The sequential decomposition of hydride powders (HfH2+NbH+TaH0.5+TiH2+ZrH2) is followed by in situ X‐ray diffraction. Upon sintering at 1400 °C for 18 h, a nearly fully densified, equiatomic HfNbTaTiZr alloy is synthesized; on slow cooling, both α‐HCP and β‐BCC phases are formed, but on quenching, a metastable single β‐BCC phase is obtained. Printed and sintered HfNbTaTiZr alloys with ≈1 wt.% O shows excellent mechanical properties at high temperatures. Oxidation resistance is achieved by silicide coating via pack cementation. A small‐size lattice‐core sandwich is fabricated and tested with high‐temperature flames to demonstrate the versatility of this sequential approach (printing, sintering, and siliconizing) for high‐temperature, high‐stress applications of refractory high‐entropy alloys.
-
Three typical types of defects, i.e., keyholes, lack of fusion (LoF), and gas-entrapped pores (GEP), characterized by various features (e.g., volume, surface area, etc.), are generated under different process parameters of laser beam powder bed fusion (L-PBF) processes in additive manufacturing (AM). The different types of defects deteriorate the mechanical performance of L- PBF components, such as fatigue life, to a different extent. However, there is a lack of recognized approaches to classify the defects automatically and accurately in L-PBF components. This work presents a novel hierarchical graph convolutional network (H-GCN) to classify different types of defects by a cascading GCN structure with a low-level feature (e.g., defect features) layer and a high-level feature (e.g., process parameters) layer. Such an H-GCN not only leverages the multi- level information from process parameters and defect features to classify the defects but also explores the impact of process parameters on defect types and features. The H-GCN is evaluated through a case study with X-ray computed tomography (CT) L-PBF defect datasets and compared with several machine learning methods. H-GCN exhibits an outstanding classification performance with an F1-score of 1.000 and reveals the potential effect of process parameters on three types of defects.more » « less