In this report, a facile wet chemical method using acetonitrile combined with thermal annealing was used to prepare Li2S‐P2S5(LPS) based glass‐ceramic electrolytes with (1 wt%, 3 wt%, and 5 wt% Ce2S3) and without Ce2S3doping. The crystal structure, ionic conductivity, and chemical stability of Li7P3S11glass‐ceramic electrolytes were examined at varying temperatures (250–350°C). The results indicated that the highest ionic conductivity of 3.15 × 10−4S cm−1for pure Li7P3S11was observed at a temperature of 325°C. By incorporating 1 wt% Ce2S3and subjecting it to a heat treatment at 250°C, the glass ceramic electrolyte attained a remarkable ionic conductivity of 7.7 × 10−4(S cm−1) at 25°C. Furthermore, it exhibited a stable and extensive electrochemical potential range, reaching up to 5 volts when compared to the Li/Li+reference electrode. By tuning the glass transition and crystallization temperature, cerium doping seems to make Li7P3S11more chemically stable, compared to its original 70Li2S‐30P2S5counterpart. According to Raman and X‐ray photoelectron spectroscopy analyses, cerium doping inhibits the decomposition of highly conductive P2S74‐(pyro‐thiophosphate) to PS43−and P2S64−. Doped LPS has a greater crystallinity and more uniform microstructure than pure LPS, according to XRD, Raman spectroscopy, and scanning electron microscopy analysis. Consequently, Li7P2.9Ce0.1S11electrolyte shows great potential as a solid‐state electrolyte for constructing high‐performance sulfide‐based all‐solid‐state batteries.
This content will become publicly available on January 1, 2025
Metal indium sulfides (ZnIn2S4, NiIn2S4, and CuInS2) were synthesized using a hydrothermal method for electrochemical reduction of CO2in to methane.
more » « less- Award ID(s):
- 2100710
- PAR ID:
- 10527382
- Publisher / Repository:
- RSC
- Date Published:
- Journal Name:
- Catalysis Science & Technology
- ISSN:
- 2044-4753
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
more » « less
Abstract -
more » « less
Abstract Addition of sub‐stoichiometric quantities of PEt3and diphenyl disulfide to a solution of [Ni(1,5‐cod)2] generates a mixture of [Ni3(SPh)4(PEt3)3] (
1 ), unreacted [Ni(1,5‐cod)2], and [(1,5‐cod)Ni(PEt3)2], according to1H and31P{1H} NMR spectroscopic monitoring of the in situ reaction mixture. On standing, complex1 converts into [Ni4(S)(Ph)(SPh)3(PEt3)3] (2 ), via formal addition of a “Ni(0)” equivalent, coupled with a CS oxidative addition step, which simultaneously generates the Ni‐bound phenyl ligand and the μ3‐sulfide ligand. Upon gentle heating, complex2 converts into a mixture of [Ni5(S)2(SPh)2(PEt3)5] (3 ) and [Ni8(S)5(PEt3)7] (4 ), via further addition of “Ni(0)” equivalents, in combination with a series of C–S oxidative addition and CC reductive elimination steps, which serve to convert thiophenolate ligands into sulfide ligands and biphenyl. The presence of1 –4 in the reaction mixture is confirmed by their independent syntheses and subsequent spectroscopic characterization. Overall, this work provides an unprecedented level of detail of the early stages of Ni nanocluster growth and highlights the fundamental reaction steps (i.e., metal atom addition, CS oxidative addition, and CC reductive elimination) that are required to grow an individual cluster. -
more » « less
Abstract A series of copper thiospinel compounds, CuCo2S4‐
x Sex (x = 0, 0.2, 0.4, 0.6, 0.8), have been successfully synthesized by solid‐state reaction and their structure and magnetic properties have been studied. The Rietveld refinements of X‐ray diffractions indicate that both the lattice constants and the nearest‐neighbor Cu‐Cu distances increase with increasing selenium doping. A weakly antiferromagnetic transition occurring at about 4 K is observed in CuCo2S4. Two antiferromagnetic transitions at about 3.5 K and 6 K are observed in selenium‐doped samples, which suggest that the exchange couplings associated with Cu‐S(Se)‐Cu and Cu‐Se(S)‐Cu, respectively, are responsible for the two antiferromagnetic transitions. Detailed analysis of the experimental results further indicates that the nearest‐neighbor molecular field coefficient is comparable to the next‐neighbor molecular field coefficient. We propose a reasonable model to explain this phenomenon. -
more » « less
Abstract A unique approach is used to relate the HOMO‐LUMO energy difference to the difference between the ionization potential (IP) and electron affinity (EA) to assist in deducing not only the colors, but also chromophores in elemental nonmetals. Our analysis focuses on compounds with lone pair electrons and σ electrons, namely X2(X = F, Cl, Br, I), S8and P4. For the dihalogens, the [IP – EA] energies are found to be: F2(12.58 eV), Cl2(8.98 eV), Br2(7.90 eV), I2(6.78 eV). We suggest that the
intera halogen X–X bond itself is the chromophore for these dihalogens, in which the light absorbed by the F2, Cl2, Br2, I2leads to longer wavelengths in the visible by a π → σ* transition. Trace impurities are a likely case of cyclic S8which contains amounts of selenium leading to a yellow color, where the [IP – EA] energy of S8is found to be 7.02 eV. Elemental P4with an [IP – EA] energy of 9.09 eV contains a tetrahedral and σ aromatic structure. In future work, refinement of the analysis will be required for compounds with π electrons and σ electrons, such as polycyclic aromatic hydrocarbons (PAHs). -
more » « less
Abstract Wet chemical screening reveals the very high reactivity of Mo(NMe2)4with H2S for the low‐temperature synthesis of MoS2. This observation motivated an investigation of Mo(NMe2)4as a volatile precursor for the atomic layer deposition (ALD) of MoS2thin films. Herein we report that Mo(NMe2)4enables MoS2film growth at record low temperatures—as low as 60 °C. The as‐deposited films are amorphous but can be readily crystallized by annealing. Importantly, the low ALD growth temperature is compatible with photolithographic and lift‐off patterning for the straightforward fabrication of diverse device structures.