ABSTRACT Despite their high power density, microsupercapacitors (MSCs) are impractical for many energy storage applications due to their limited energy density. Their energy density can be increased by shaping the electrodes into 3D structures with high specific surface area (SSA). Direct printing of nanoporous 3D electrodes is a promising approach for achieving high SSA. However, conventional nanoscale 3D printing is too slow due to point‐by‐point processing. Here, we have employed the projection two‐photon lithography technique to fabricate nanoporous 3D electrodes via a rapid layer‐by‐layer mechanism. The 3D MSC electrodes are engineered as an array of nanoporous polymeric micropillars that are printed with customizable spacing and count over a 0.25 cm2area. After printing, these micropillars are conformally coated with titanium nitride to form conductive 3D electrodes, which exhibit a specific capacitance of 361 μF/cm2. This is two orders of magnitude higher than the capacitance of the flat surface and exceeds the capacitance of both traditional bare electrodes, such as single‐wall carbon nanotubes (< 100 μF/cm2), and electrodes produced by photo‐polymerization 3D printing (˜200 μF/cm2). As our work demonstrates that high energy density 3D electrodes can be rapidly fabricated, it significantly expands the utility of MSCs as miniaturized energy storage devices.
more »
« less
Green Fabrication of Stackable Laser‐Induced Graphene Micro‐Supercapacitors under Ambient Conditions: Toward the Design of Truly Sustainable Technological Platforms
Abstract Extensive research into green technologies is driven by the worldwide push for eco‐friendly materials and energy solutions. The focus is on synergies that prioritize sustainability and environmental benefits. This study explores the potential of abundant, non‐toxic, and sustainable resources such as paper, lignin‐enriched paper, and cork for producing laser‐induced graphene (LIG) supercapacitor electrodes with improved capacitance. A single‐step methodology using a CO2laser system is developed for fabricating these electrodes under ambient conditions, providing an environmentally friendly alternative to conventional carbon sources. The resulting green micro‐supercapacitors (MSCs) achieve impressive areal capacitance (≈7–10 mF cm−2) and power and energy densities (≈4 μW cm‐2and ≈0.77 µWh cm−2at 0.01 mA cm−2). Stability tests conducted over 5000 charge–discharge cycles demonstrate a capacitance retention of ≈80–85%, highlighting the device durability. These LIG‐based devices offer versatility, allowing voltage output adjustment through stacked and sandwich MSCs configurations (parallel or series), suitable for various large‐scale applications. This study demonstrates that it is possible to create high‐quality energy storage devices based on biodegradable materials. This development can lead to progress in renewable energy and off‐grid technology, as well as a reduction in electronic waste.
more »
« less
- PAR ID:
- 10535145
- Publisher / Repository:
- Wiley Blackwell (John Wiley & Sons)
- Date Published:
- Journal Name:
- Advanced Materials Technologies
- Volume:
- 9
- Issue:
- 16
- ISSN:
- 2365-709X
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Abstract Complex graphene electrode fabrication protocols including conventional chemical vapor deposition and graphene transfer techniques as well as more recent solution‐phase printing and postprint annealing methods have hindered the wide‐scale implementation of electrochemical devices including solid‐state ion‐selective electrodes (ISEs). Herein, a facile graphene ISE fabrication technique that utilizes laser induced graphene (LIG), formed by converting polyimide into graphene by a CO2laser and functionalization with ammonium ion (NH4+) and potassium ion (K+) ion‐selective membranes, is demonstrated. The electrochemical LIG ISEs exhibit a wide sensing range (0.1 × 10−3–150 × 10−3mfor NH4+and 0.3 × 10−3–150 × 10−3mfor K+) with high stability (minimal drop in signal after 3 months of storage) across a wide pH range (3.5–9.0). The LIG ISEs are also able to monitor the concentrations of NH4+and K+in urine samples (29–51% and 17–61% increase for the younger and older patient; respectively, after dehydration induction), which correlate well with conventional hydration status measurements. Hence, these results demonstrate a facile method to perform in‐field ion sensing and are the first steps in creating a protocol for quantifying hydration levels through urine testing in human subjects.more » « less
-
Abstract Lead halide perovskites have recently attracted intensive attention as competitive alternative candidates of legacy compound materials CdTe, CdZnTe, and TlBr for high sensitivity energy‐resolving gamma‐ray detection at room temperature. However, the use of lead in these lead halide perovskites, which is necessary for increasing the stopping power of gamma radiation, poses a serious environmental concern due to the high toxicity of lead. In this regard, environmental‐friendly perovskite‐based gamma‐ray detector materials with key energy‐resolving capabilities are highly desired. Here, the gamma energy‐resolving performance of a new class of all‐inorganic and lead‐free Cs2AgBiBr6double perovskite single crystals (SCs) is reported. Two types of Cs2AgBiBr6SCs, prepared by Bi‐normal and Bi‐poor precursor solutions, respectively, have been grown. Their mobilities and response to gamma radiation are presented. Density of trap states in Bi‐poor Cs2AgBiBr6SCs (2.65 × 109 cm−3) is one order of magnitude lower than that in Bi‐normal Cs2AgBiBr6SCs (3.85 × 1010 cm−3). Using laser‐induced photocurrent measurements, the obtained mobility–lifetime (μ–τ) product in Bi‐poor Cs2AgBiBr6SCs is 1.47 × 10−3 cm2 V−1, indicating their great potentials for gamma‐ray detection. Further, the fabricated detector based on Bi‐poor Cs2AgBiBr6SC shows response to 59.5 keV gamma‐ray with an energy resolution of 13.91%.more » « less
-
Abstract An ultra‐fast electrochemical capacitor (EC) designed for efficient ripple current smoothing was fabricated using vertically oriented MoS2(VOM) nanoflakes deposited on freestanding carbonized cellulose (CC) sheets as electrodes. The daily used cellulose tissue sheets were transformed into electrode scaffolds through a rapid pyrolysis process within a preheated furnace, on which VOM nanoflakes were formed in a conventional hydrothermal process. With these ~10 μm thick VOM‐CC electrodes, ultrafast ECs with tunable frequency response and specific capacitance density were fabricated. The ECs with a cell‐level areal capacitance density of 0.8 mF/cm2at 120 Hz were demonstrated for ripple current filtering from 60 Hz to 60 kHz. At a lower frequency response level, EC cell with a large capacitance density of 4.8 mF/cm2was also demonstrated. With the facile and easily scaled up process to producing the nanostructured electrode, the miniaturized VOM‐CC based ECs have the potential to substitute the bulky aluminum electrolytic capacitors for current smoothing and pulse power applications.more » « less
-
Abstract Lightweight energy storage devices are essential for developing compact wearable and distributed electronics, and additive manufacturing offers a scalable, low‐cost approach to fabricating such devices with complex geometries. However, additive manufacturing of high‐performance, on‐demand energy storage devices remains challenging due to the need for stable, multifunctional nanomaterial inks. Herein, the development of 2‐dimensional (2D) titanium carbide (Ti3C2TxMXene) ink that is compatible with aerosol jet printing for energy storage applications is demonstrated. The developed MXene ink demonstrates long‐term chemical and physical stability, ensuring consistent printability and achieving high‐resolution prints (≈45 µm width lines) with minimal overspray. The high‐resolution aerosol‐jet printed MXene supercapacitor achieves an areal capacitance of 122 mF cm−2and a volumetric capacitance of 611 F cm−3, placing them among the highest‐performing printed supercapacitors reported to date. These findings highlight the potential of aerosol jet printing with MXene inks for on‐demand, scalable, and cost‐effective fabrication of printed electronic and electrochemical devices.more » « less