Balancing strength and ductility is crucial for structural materials, yet often presents a paradoxical challenge. This research focuses on crafting a unique bimetallic structure, combining non-magnetic, stainless steel 316L (SS316L) with limited strength but enhanced ductility and magnetic, martensitic 17-4 PH with higher strength but lower ductility. Utilizing a powder-based laser-directed energy deposition (L-DED) system, two vertical bimetallic configurations (SS316L/17-4 PH) and a radial bimetallic structure (SS316L core encased in 17-4 PH) were fabricated. Monolithic SS316L, 17-4 PH, and a 50% SS316L/50% 17-4 PH mixture were printed. The printed samples' phase, microstructure, room temperature mechanical properties, and fracture morphology were examined in as-printed conditions. Bimetallic samples exhibited both phases, with a smooth grain transition at the interface. Radial bimetallic samples demonstrated higher mechanical strength than other compositions, except 17-4 PH. These findings showcase the potential of the L-DED approach for creating functional components with tailored mechanical properties.
more »
« less
This content will become publicly available on August 1, 2025
Process Parameter Optimization of Directed Energy Deposited QT17‐4+ Steel
The feasibility of using argon‐atomized QT 17‐4+ stainless steel powder for directed energy deposition (DED) additive manufacturing is studied. The QT 17‐4+ steel is a novel martensitic steel designed based on the compositional modification of the standard 17‐4 precipitation‐hardened (PH) stainless steel. This modification aims to achieve better mechanical properties of as‐deposited components compared to the heat‐treated wrought 17‐4PH steel. In this study, QT 17‐4+ steel powder is used for DED, for the first time. The influence of laser power, laser scan speed, powder feed rate, and hatch overlap on the density is studied. The central composite design is used to determine the experimental matrix of these factors. The response surface methodology is used to obtain the empirical statistical prediction model. Both columnar and equiaxed parent austenite grain structures are observed. X‐ray diffraction analyses reveal a decrease in the percentage of retained austenite from 19% in the powder to 5% after DED. The microhardness of the DED processed sample in the as‐deposited state is slightly higher than that of wrought 17‐4PH steel either solution‐annealed or H900‐aged. A higher 0.2% yield strength, a lower ultimate tensile strength, and lower elongation are observed for the vertically printed test sample, when compared to the horizontal one.
more » « less- Award ID(s):
- 2105362
- PAR ID:
- 10536971
- Publisher / Repository:
- Wiley-VCH GmbH, Weinheim
- Date Published:
- Journal Name:
- Advanced Materials Technologies
- Volume:
- 9
- Issue:
- 15
- ISSN:
- 2365-709X
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Wire arc additive manufacturing (WAAM) presents a highly promising alternative to conventional subtractive manufacturing methods to produce metallic components, particularly in the aerospace industry, where there is a demand for 17–4 precipitation-hardened (PH) stainless steel structures. This study focuses on investigating the microstructural characteristics, showing microhardness evaluations, and analyzing the tensile properties of the as-printed parts during the 17–4 PH manufacturing process at different locations and directions. The fabrication is carried out using gas metal wire arc additive manufacturing (GM-WAAM). As a result, it was found that the microstructure of the as-deposited part showed a complex configuration consisting of both finely equiaxed and coarsely formed δ-ferrite phases with vermicular and lathy morphologies. These phases were dispersed inside the martensitic matrix, while a small amount of retained austenite was also present. It was observed that the volume fraction of retained austenite (20–5%) and δ-ferrite phases (15.5–2.5%) decreased gradually from the bottom to the top of the as-deposited wall. This reduction in the fractions of these phases resulted in a progressive increase in both hardness (∼37%) and ultimate tensile strength (UTS) along the building direction. This study successfully fabricates a high-strength and ductile 17–4 PH as-printed part using WAAM. The findings provide evidence supporting the feasibility of employing WAAM for producing defect-free, high-strength components on a large scale while maintaining mechanical properties similar or better than wrought alloy 17–4 PH.more » « less
-
This study investigates the mechanical behavior of additively manufactured (AM) 17-4 PH (AISI 630) stainless steels and compares their behavior to traditionally produced wrought counterparts. The goal of this study is to understand the key parameters influencing AM 17-4 PH steel fatigue life under ULCF conditions and to develop simple predictive models for fatigue-life estimation in AM 17-4 steel components. In this study, both AM and traditionally produced (wrought) material samples are fatigue tested under fully reversed (R = −1) strain controlled (2–4% strain) loading and characterized using micro-hardness, x-ray diffraction, and fractography methods. Results indicate decreased fatigue life for AM specimens as compared to wrought 17-4 PH specimens due to fabrication porosity and un-melted particle defect regions which provide a mechanism for internal fracture initiation. Heat treatment processes performed in this work, to both the AM and wrought specimens, had no observable effect on ULCF behavior. Result comparisons with an existing fatigue prediction model (the Coffin–Manson universal slopes equation) demonstrated consistent over-prediction of fatigue life at applied strain amplitudes greater than 3%, likely due to inherent AM fabrication defects. An alternative empirical ULCF capacity equation is proposed herein to aid future fatigue estimations in AM 17-4 PH stainless steel components.more » « less
-
The goal of this stydy was to explore the potential of the enhanced corrosion resistance of Ti(N,O) cathodic arc evaporation-coated 304L stainless steel using oxide nano-layers deposited by atomic layer deposition (ALD). In this study, we deposited Al2O3, ZrO2, and HfO2 nanolayers of two different thicknesses by ALD onto Ti(N,O)-coated 304L stainless steel surfaces. XRD, EDS, SEM, surface profilometry, and voltammetry investigations of the anticorrosion properties of the coated samples are reported. The amorphous oxide nanolayers homogeneously deposited on the sample surfaces exhibited lower roughness after corrosion attack compared to the Ti(N,O)-coated stainless steel. The best corrosion resistance was obtained for the thickest oxide layers. All samples coated with thicker oxide nanolayers augmented the corrosion resistance of the Ti(N,O)-coated stainless steel in a saline, acidic, and oxidising environment (0.9% NaCl + 6% H2O2, pH = 4), which is of interest for building corrosion-resistant housings for advanced oxidation systems such as cavitation and plasma-related electrochemical dielectric barrier discharge for breaking down persistent organic pollutants in water.more » « less
-
This work reports on the measurement of the internal temperature distributions of parts being manufactured via the Powder Bed Fusion (PBF) process. Eight test coupons were machined from a piece of wrought 304 stainless steel (SS). Thermocouples were inserted into the test coupon interiors to sample internal thermal history. The coupons were then placed into the open architecture laser PBF machine housed at EWI and covered to their uppermost surfaces with 316 SS powder.Three tests were executed: First, the laser rastered over the coupons without inducing melting.Second, the laser rastered over the coupons while melting the exposed faces. Lastly, five layers of316 SS were built atop the coupons. The main result is a comprehensive data set of a multitude of measured physical inputs and outputs under typical build conditions: embedded thermocouple temperatures, laser centroid, laser power, and infrared imagery of the exposed coupon faces.more » « less