For next-generation superconducting radiofrequency (SRF) cavities, the interior walls of existing Nb SRF cavities are coated with a thin Nb3Sn film to improve the superconducting properties for more efficient, powerful accelerators. The superconducting properties of these Nb3Sn coatings are limited due to inhomogeneous growth resulting from poor nucleation during the Sn vapor diffusion procedure. To develop a predictive growth model for Nb3Sn grown via Sn vapor diffusion, we aim to understand the interplay between the underlying Nb oxide morphology, Sn coverage, and Nb substrate heating conditions on Sn wettability, intermediate surface phases, and eventual Nb3Sn nucleation. In this work, Nb-Sn intermetallic species are grown on a single crystal Nb(100) in an ultrahigh vacuum chamber equipped with in situ surface characterization techniques including scanning tunneling microscopy, Auger electron spectroscopy, and x-ray photoelectron spectroscopy. Sn adsorbate behavior on oxidized Nb was examined by depositing Sn with submonolayer precision on a Nb substrate held at varying deposition temperatures (Tdep). Experimental data of annealed intermetallic adlayers provide evidence of how Nb substrate oxidization and Tdep impact Nb-Sn intermetallic coordination. The presented experimental data contextualize how vapor and substrate conditions, such as the Sn flux and Nb surface oxidation, drive homogeneous Nb3Sn film growth during the Sn vapor diffusion procedure on Nb SRF cavity surfaces. This work, as well as concurrent growth studies of Nb3Sn formation that focus on the initial Sn nucleation events on Nb surfaces, will contribute to the future experimental realization of optimal, homogeneous Nb3Sn SRF films.
more »
« less
Thermodynamic route of Nb3Sn nucleation: Role of oxygen
Intermetallic Nb3Sn alloys have long been believed to form through Sn diffusion into Nb. However, our observations of significant oxygen content in Nb3Sn prompted an investigation of alternative formation mechanisms. Through experiments involving different oxide interfaces (clean HF-treated, native oxidized, and anodized), we demonstrate a thermodynamic route that fundamentally challenges the conventional Sn diffusion mechanism for Nb3Sn nucleation. Our results highlight the critical involvement of a SnOx intermediate phase. This new nucleation mechanism identifies the principles for growth optimization and new synthesis of high-quality Nb3Sn superconductors.
more »
« less
- Award ID(s):
- 1719875
- PAR ID:
- 10549413
- Publisher / Repository:
- AIP Publishing
- Date Published:
- Journal Name:
- APL Materials
- Volume:
- 11
- Issue:
- 7
- ISSN:
- 2166-532X
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Interface free energy is a fundamental material parameter needed to predict the nucleation and growth of new phases. The high cost of experimentally determining this parameter makes it an ideal target for calculation through a physically informed simulation. Direct determination of interface free energy has many challenges, especially for solid–solid transformations. Indirect determination of the interface free energy from the nucleation data has been done in the case of solidification. However, a slow on molecular dynamics (MD) simulation time scale atomic diffusion makes this method not applicable to the case of nucleation from the solid phase when precipitate composition is different from that in matrix. To address this challenge, we outline the development of a new technique for determining the critical nucleus size from an MD simulation using a recently developed method to accelerate solid-state diffusion. The accuracy of our approach for the Ni–Al system for Ni3Al (γ′) precipitates in a Ni–Al (γ) matrix is demonstrated well within experimental accuracy and greatly improves upon previous computational methods [Herrnring et al., Acta Mater. 215(8), 117053 (2021)].more » « less
-
Sn clusters have been grown on highly oriented pyrolytic graphite (HOPG) surfaces and investigated by scanning tunneling microscopy (STM), X-ray photoelectron spectroscopy (XPS), and density functional theory (DFT) calculations. At low Sn coverages ranging from 0.02-0.25 ML, Sn grows as small clusters that nucleate uniformly on the terraces. This behavior is in contrast with the growth of transition metals such as Pd, Pt, and Re on HOPG, given that these metals form large clusters with preferential nucleation for Pd and Pt at the favored low-coordination step edges. XPS experiments show no evidence of Sn-HOPG interactions, and the activation energy barrier for diffusion calculated for Sn on HOPG (0.06 eV) is lower or comparable to those of Pd, Pt and Re (0.04, 0.22, and 0.61 eV, respectively), indicating that the growth of the Sn clusters is not kinetically limited by diffusion on the surface. DFT calculations of the binding energy/atom as a function of cluster size demonstrate that the energies of the Sn clusters on HOPG are similar to that of Sn atoms in the bulk for Sn clusters larger than 10 atoms, whereas the Pt, Pd, and Re clusters on HOPG have energies that are 1-2 eV higher than in the bulk. Thus, there is no thermodynamic driving force for Sn atoms to form clusters larger than 10 atoms on HOPG, unlike for Pd, Pt, and Re atoms, which minimize their energy by aggregating into larger, more bulk-like clusters. In addition, annealing the Sn/HOPG clusters to 800 K and 950 K does not increase the cluster size but instead removes the larger clusters, while Sn deposition at 810 K induces the appearance of protrusions that are believed to be from subsurface Sn. DFT studies indicate that it is energetically favorable for a Sn atom to exist in the subsurface layer only when the Sn atom is located at a subsurface vacancy.more » « less
-
Formation kinetics of metal nanoparticles are generally describedviamass transport and thermodynamics‐based models, such as diffusion‐limited growth and classical nucleation theory (CNT). However, metal monomers are commonly assumed as precursors, leaving the identity of molecular intermediates and their contribution to nanoparticle formation unclear. Herein, liquid phase transmission electron microscopy (LPTEM) and reaction kinetic modeling are utilized to establish the nucleation and growth mechanisms and discover molecular intermediates during silver nanoparticle formation. Quantitative LPTEM measurements show that their nucleation rate decreases while growth rate is nearly invariant with electron dose rate. Reaction kinetic simulations show that Ag4and Ag−follow a statistically similar dose rate dependence as the experimentally determined growth rate. We show that experimental growth rates are consistent with diffusion‐limited growthviathe attachment of these species to nanoparticles. The dose rate dependence of nucleation rate is inconsistent with CNT. A reaction‐limited nucleation mechanism is proposed and it is demonstrated that experimental nucleation kinetics are consistent with Ag42+aggregation rates at millisecond time scales. Reaction throughput analysis of the kinetic simulations uncovered formation and decay pathways mediating intermediate concentrations. We demonstrate the power of quantitative LPTEM combined with kinetic modeling for establishing nanoparticle formation mechanisms and principal intermediates.more » « less
-
Iodine oxoacids are recognised for their significant contribution to the formation of new particles in marine and polar atmospheres. Nevertheless, to incorporate the iodine oxoacid nucleation mechanism into global simulations, it is essential to comprehend how this mechanism varies under various atmospheric conditions. In this study, we combined measurements from the CLOUD (Cosmic Leaving OUtdoor Droplets) chamber at CERN and simulations with a kinetic model to investigate the impact of temperature, ionisation, and humidity on iodine oxoacid nucleation. Our findings reveal that ion-induced particle formation rates remain largely unaffected by changes in temperature. However, neutral particle formation rates experience a significant increase when the temperature drops from +10 oC to −10 oC. Running the kinetic model with varying ionisation rates demonstrates that the particle formation rate only increases with a higher ionisation rate when the iodic acid concentration exceeds 1.5 × 107 cm^sup>−3, a concentration rarely reached in pristine marine atmospheres. Consequently, our simulations suggest that, despite higher ionisation rates, the charged cluster nucleation pathway of iodic acid is unlikely to be enhanced in the upper troposphere by higher ionisation rates. Instead, the neutral nucleation channel is likely to be the dominant channel in that region. Notably, the iodine oxoacid nucleation mechanism remains unaffected by changes in relative humidity from 2% to 80%. However, under unrealistically dry conditions (below 0.008% RH at +10 oC), iodine oxides (I2O4 and I2O5) significantly enhance formation rates. Therefore, we conclude that iodine oxoacid nucleation is the dominant nucleation mechanism for iodine nucleation in the marine and polar boundary layer atmosphere.more » « less
- Free Publicly Accessible Full Text
-
Accepted Manuscript
- Journal Article:
- https://doi.org/10.1063/5.0157659