Additive manufacturing allows fabrication of custom-shaped thermoelectric materials while minimizing waste, reducing processing steps, and maximizing integration compared to conventional methods. Establishing the process-structure-property relationship of laser additive manufactured thermoelectric materials facilitates enhanced process control and thermoelectric performance. This research focuses on laser processing of bismuth telluride (Bi 2 Te 3 ), a well-established thermoelectric material for low temperature applications. Single melt tracks under various parameters (laser power, scan speed and number of scans) were processed on Bi 2 Te 3 powder compacts. A detailed analysis of the transition in the melting mode, grain growth, balling formation, and elemental composition is provided. Rapid melting and solidification of Bi 2 Te 3 resulted in fine-grained microstructure with preferential grain growth along the direction of the temperature gradient. Experimental results were corroborated with simulations for melt pool dimensions as well as grain morphology transitions resulting from the relationship between temperature gradient and solidification rate. Samples processed at 25 W, 350 mm/s with 5 scans resulted in minimized balling and porosity, along with columnar grains having a high density of dislocations.
more »
« less
Micro- and Nano-structures Formed in Silicon Germanium Undergoing Laser Melting for Additive Manufacturing
Abstract Thermoelectric materials offer a unique solution for active cooling or conversion of heat to electricity within a thermal protection system due to their solid-state nature. Yet, the integration of thermoelectrics into thermal protection systems is hindered by conventional manufacturing processes, which limit the material’s shape. Laser additive manufacturing can enable freeform shapes that allow integration of thermoelectrics into systems that are favorable for thermoelectric energy conversion. Through modeling and experimentation, this work presents single melt line processing and structures of silicon germanium, a high-temperature thermoelectric material, for laser powder bed fusion. Experiments consisted of single melt lines with an Nd-YAG laser and 50-µm spot size on Si50Ge50and Si80Ge20powder compacts. We found that laser processing of silicon germanium alloys causes oxidation and processing defects that are resolved through rescanning strategies. Rapid cooling results in a microstructure with silicon-rich grains and germanium entrapped near grain boundaries for Si80Ge20and dendritic structures in Si50Ge50which are linked to the degree of undercooling during solidification. Laser-processed silicon germanium contains crystalline defects, nanoscale precipitates, and an average grain size of 24 µm. This work informs laser additive manufacturing of silicon germanium parts and uncovers process-structure relationships of laser-processed silicon germanium alloys.
more »
« less
- Award ID(s):
- 1943104
- PAR ID:
- 10556361
- Publisher / Repository:
- Springer Science + Business Media
- Date Published:
- Journal Name:
- JOM
- Volume:
- 77
- Issue:
- 2
- ISSN:
- 1047-4838
- Format(s):
- Medium: X Size: p. 793-808
- Size(s):
- p. 793-808
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Measurements of the dark conductivity and thermoelectric power in hydrogenated amorphous silicon–germanium alloys (a-Si 1- x Ge x :H) reveal that charge transport is not well described by an Arrhenius expression. For alloys with concentrations of Ge below 20%, anomalous hopping conductivity is observed with a power-law exponent of 3/4, while the temperature dependence of the conductivity of alloys with higher Ge concentrations is best fit by a combination of anomalous hopping and a power-law temperature dependence. The latter has been attributed to charge transport via multi-phonon hopping. Corresponding measurements of the Seebeck coefficient reveal that the thermopower is n-type for the purely a-Si:H and a-Ge:H samples but that it exhibits a transition from negative to positive values as a function of the Ge content and temperature. These findings are interpreted in terms of conduction via hopping through either exponential band tail states or dangling bond defects, suggesting that the concept of a mobility edge, accepted for over five decades, may not be necessary to account for charge transport in amorphous semiconductors.more » « less
-
Abstract Laser powder-bed fusion (L-PBF) additive manufacturing presents ample opportunities to produce net-shape parts. The complex laser-powder interactions result in high cooling rates that often lead to unique microstructures and excellent mechanical properties. Refractory high-entropy alloys show great potential for high-temperature applications but are notoriously difficult to process by additive processes due to their sensitivity to cracking and defects, such as un-melted powders and keyholes. Here, we present a method based on a normalized model-based processing diagram to achieve a nearly defect-free TiZrNbTa alloy via in-situ alloying of elemental powders during L-PBF. Compared to its as-cast counterpart, the as-printed TiZrNbTa exhibits comparable mechanical properties but with enhanced elastic isotropy. This method has good potential for other refractory alloy systems based on in-situ alloying of elemental powders, thereby creating new opportunities to rapidly expand the collection of processable refractory materials via L-PBF.more » « less
-
Abstract Refractory complex concentrated alloys (RCCAs) show potential as the next-generation structural materials due to their superior strength in extreme environments. However, RCCAs processed by metal additive manufacturing (AM) typically suffer from process-related challenges surrounding laser material interaction defects and microstructure control. Multimodalin situtechniques (synchrotron X-ray imaging and diffraction and infrared imaging) and melt pool-level simulations were employed to understand rapid solidification pathways in two representative RCCAs: (i) multi-phase BCC + HCP Ti0.4Zr0.4Nb0.1Ta0.1and (ii) single-phase BCC Ti0.486V0.375Cr0.111Ta0.028. As expected, laser material interaction defects followed similar systematic trends in process parameter space for both alloys. Additionally, both alloys formed a single-phase (BCC) microstructure after rapid solidification processing. However, significant differences in microstructure selection between these alloys were discovered, where Ti0.4Zr0.4Nb0.1Ta0.1showed a mixture of equiaxed and columnar grains, while Ti0.486V0.375Cr0.111Ta0.028was dominated by columnar growth. These behaviors were well described by the influence of undercooling effects on columnar-to-equiaxed transition (CET). Distinct microstructure formation in each alloy was verified through CET predictions via analytical melt pool simulations, which showed a ~ 5 × increase degrees in undercooling for Ti0.4Zr0.4Nb0.1Ta0.1compared to Ti0.486V0.375Cr0.111Ta0.028. Overall, these results show that microstructure control based on modulating the freezing range must be balanced with process considerations which resist defect formation, such as solidification crack formation in RCCAs. Graphical abstractmore » « less
-
Abstract Laser processing of thermoelectric materials provides an avenue to influence the nano‐ and micro‐structure of the material and enable additive manufacturing processes that facilitate freeform device shapes, a capability that is lacking in thermoelectric materials processing. This paper describes the multiscale structures formed in selenium‐doped bismuth telluride, an n‐type thermoelectric material, from laser‐induced rapid melting and solidification. Macroscale samples are fabricated in a layer‐by‐layer technique using laser powder bed fusion (also known as selective laser melting). Laser processing results in highly textured columnar grains oriented in the build direction, nanoscale inclusions, and a shift in the primary charge carriers. Sparse oxide inclusions and tellurium segregation shift the material to p‐type behavior with a Seebeck coefficient that peaks at 143 µV K–1at 95 °C. With an average relative density of 74%, fabricated parts have multiscale porosity and microscale cracking that likely resulted from low powder layer packing density and processing parameters near the transition threshold between conduction and keyhole mode processing. These results provide insights regarding the pathways for influencing carrier transport in thermoelectric materials via laser melting‐induced nanoscale structuring and the laser processing parameters required to achieve effective powder consolidation and hierarchical structuring in thermoelectric parts.more » « less