Despite the importance of bulk lanthanide borides, nanoclusters of lanthanide and boron have rarely been investigated. Here we show that lanthanide–boron binary clusters, La 2 B x − , can form a new class of inverse-sandwich complexes, [Ln(η x -B x )Ln] − ( x = 7–9). Joint experimental and theoretical studies reveal that the monocyclic B x rings in the inverse sandwiches display similar bonding, consisting of three delocalized σ and three delocalized π bonds. Such monocyclic boron rings do not exist for bare boron clusters, but they are stabilized by the sandwiching lanthanide atoms. An electron counting rule is proposed to predict the sizes of the B x ring that can form stable inverse sandwiches. A unique (d-p)δ bond is found to play important roles in the stability of all three inverse-sandwich complexes.
more »
« less
This content will become publicly available on December 4, 2025
Synthesis and Stability Phase Diagram of Topological Semimetal Family LnSb x Te 2–x–δ
The solid solution LnSbxTe2−x−δ (Ln = lanthanide) is a family of square-net topological semimetals that exhibit tunable charge density wave (CDW) distortions and band filling dependent on x, offering broad opportunities to examine the interplay of topological electronic states, CDW, and magnetism. While several Ln series have been characterized, gaps in the literature remain, inviting a systematic survey of the remaining composition space that is synthetically accessible. We present our efforts to synthesize LnSbxTe2−x−δ across the remaining lanthanides via chemical vapor transport. Compiling our results with the reported literature, we generate a stability phase diagram across the ranges of Ln and x. We find a stability boundary for intermediate x beyond Tb, while x = 1 and x = 0 can be isolated up to Ho and Dy, respectively. SEM and XRD analyses of unsuccessful reactions indicated the formation of several stable binary phases. The presence of structurally related LnTe3 in samples suggests that stability is limited by the size of Ln, due to increasing compressive strain along the layer stacking axis with decreasing size. Finally, we demonstrate that late Ln can be stabilized in LnSbxTe2−x−δ via substitution into larger Ln members, synthesizing La1−yHoySbxTe2−x−δ as a proof of concept.
more »
« less
- Award ID(s):
- 2144295
- PAR ID:
- 10558402
- Publisher / Repository:
- Chemistry of Materials
- Date Published:
- Journal Name:
- Chemistry of Materials
- ISSN:
- 0897-4756
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
more » « less
Abstract Many topological semimetals are known to exhibit exceptional electronic properties, which are the fundamental basis for design of novel devices and further applications. Materials containing the structural motif of a square net are known to frequently be topological semimetals. In this work, the synthesis and structural characterization of the square‐net‐based magnetic topological semimetal candidates GdSb
x Te2−x −δ (0,δ indicating the vacancy level) are reported. The structural evolution of the series with Sb substitution is studied, finding a transition between a simple tetragonal square‐net structure to complex superstructure formations due to the presence of charge density waves. The structural modulations coincide with a significant modification of the magnetic order. This work thus establishes GdSbx Te2−x −δ as a platform to study the interplay between crystal symmetry, band filling, charge density wave, and magnetism in a topological semimetal candidate. -
Abstract We report the superconductivity of the topological nodal-line semimetal candidate Sn x NbSe 2- δ with a noncentrosymmetric crystal structure. The superconducting transition temperature T c of Sn x NbSe 2- δ drastically varies with the Sn concentration x and the Se deficiency δ , and reaches 12 K, relatively higher than those of known topological superconductors. The upper critical field of this compound shows unusual temperature dependence, inconsistent with the WHH theory for conventional type-II superconductors. In a low-T c sample, the zero-temperature limit of the upper critical field parallel to the ab plane exceeds the Pauli paramagnetic limit estimated from the simple BCS weak coupling model by a factor of ∼ 2, suggestive of unusual superconductivity stabilized in Sn x NbSe 2- δ . Together with the robust superconductivity against disorder, these observations indicate that Sn x NbSe 2- δ is a promising candidate to explore topological superconductivity.more » « less
-
more » « less
Abstract Magnetic skyrmions are topologically protected spin textures that are being investigated for their potential use in next generation magnetic storage devices. Here, magnetic skyrmions and other magnetic phases in Fe1−
x Cox Ge (x < 0.1) microplates (MPLs) newly synthesized via chemical vapor deposition are studied using both magnetic imaging and transport measurements. Lorentz transmission electron microscopy reveals a stabilized magnetic skyrmion phase near room temperature (≈280 K) and a quenched metastable skyrmion lattice via field cooling. Magnetoresistance (MR) measurements in three different configurations reveal a unique anomalous MR signal at temperatures below 200 K and two distinct field dependent magnetic transitions. The topological Hall effect (THE), known as the electronic signature of magnetic skyrmion phase, is detected for the first time in a Fe1−x Cox Ge nanostructure, with a large and positive peak THE resistivity of ≈32 nΩ cm at 260 K. This large magnitude is attributed to both nanostructuring and decreased carrier concentrations due to Co alloying of the Fe1−x Cox Ge MPL. A consistent magnetic phase diagram summarized from both the magnetic imaging and transport measurements shows that the magnetic skyrmions are stabilized in Fe1−x Cox Ge MPLs compared to bulk materials. This study lays the foundation for future skyrmion‐based nanodevices in information storage technologies. -
Combining experimental and theoretical studies, we investigate the role of R-site (R = Y, Sm, Bi) element on the phase formation and thermal stability of R 2 (Mn 1−x Fe x ) 4 O 10−δ ( x = 0, 0.5, 1) mullite-type oxides. Our results show a distinct R-site dependent phase behavior for mullite-type oxides as Fe is substituted for Mn: 100% mullite-type phase was formed in (Y, Sm, Bi) 2 Mn 4 O 10 ; 55% and 18% of (Y, Sm) 2 Mn 2 Fe 2 O 10−δ was found when R = Y and Sm, respectively, for equal Fe and Mn molar concentrations in the reactants, whereas Bi formed 54% O10- and 42% O9-mixed mullite-type phases. Furthermore, when the reactants contain 100% Fe, no mullite-type phase was formed for R = Y and Sm, but a sub-group transition to Bi 2 Fe 4 O 9 O9-phase was found for R = Bi. Thermogravimetric analysis and density functional theory (DFT) calculation results show a decreasing thermal stability in O10-type structure with increasing Fe incorporation; for example, the decomposition temperature is 1142 K for Bi 2 Mn 2 Fe 2 O 10−δ vs. 1217 K for Bi 2 Mn 4 O 10 . On the other hand, Bi 2 Fe 4 O 9 O9-type structure is found to be thermally stable up to 1227 K. These findings are explained by electronic structure calculations: (1) as Fe concentration increases, Jahn–Teller distortion results in mid band-gap empty states from unstable Fe 4+ occupied octahedra, which is responsible for the decrease in O10 structure stability; (2) the directional sp orbital hybridization unique to Bi effectively stabilizes the mullite-type structure as Fe replaces Mn.more » « less