Abstract Liquid metal (LM) elastomer composites offer promising potential in soft robotics, wearable electronics, and human‐machine interfaces. Direct ink write (DIW) 3D printing offers a versatile manufacturing technique capable of precise control over LM microstructures, yet challenges such as interfilament void formation in multilayer structures impact material performance. Here, a DIW strategy is introduced to control both LM microstructure and material architecture. Investigating three key process parameters–nozzle height, extrusion rate, and nondimensionalized nozzle velocity–it is found that nozzle height and velocity predominantly influence filament geometry. The nozzle height primarily dictates the aspect ratio of the filament and the formation of voids. A threshold print height based on filament geometry is identified; below the height, significant surface roughness occurs, and above the ink fractures, which facilitates the creation of porous structures with tunable stiffness and programmable LM microstructure. These porous architectures exhibit reduced density and enhanced thermal conductivity compared to cast samples. When used as a dielectric in a soft capacitive sensor, they display high sensitivity (gauge factor = 9.0), as permittivity increases with compressive strain. These results demonstrate the capability to simultaneously manipulate LM microstructure and geometric architecture in LM elastomer composites through precise control of print parameters, while maintaining geometric fidelity in the printed design.
more »
« less
Anisotropic and Heterogeneous Thermal Conductivity in Programmed Liquid Metal Composites Through Direct Ink Writing
Abstract Thermal management in electric vehicles, electronics, and robotics requires the systematic ability to dissipate and direct the flow of heat. Thermally conductive soft composites are promising for thermal management due to their high thermal conductivity and mechanical flexibility. However, composites typically have the same microstructure throughout a film, which limits directional and spatial control of thermal management in emerging systems that have distributed heat loads. Herein, directional and spatially tunable thermal properties are programmed into liquid metal (LM) soft composites through a direct ink writing (DIW) process. Through the local control of LM droplet aspect ratio and orientation this programmable LM microstructure has a thermal conductivity in the direction of LM elongation of 9.9 W m−1·K−1, which is ∼40 times higher than the unfilled elastomer (0.24 W m−1·K−1). The DIW process enables LM droplets to be oriented in specific directions with tunable aspect ratios at different locations throughout a continuous film. This introduces anisotropic and heterogeneous thermal conductivity in compliant films to control the direction and magnitude of heat transfer. This methodology and resulting materials can provide designed thermal management solutions for rigid and soft devices.
more »
« less
- PAR ID:
- 10576478
- Publisher / Repository:
- Wiley Blackwell (John Wiley & Sons)
- Date Published:
- Journal Name:
- Advanced Functional Materials
- Volume:
- 35
- Issue:
- 11
- ISSN:
- 1616-301X
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Abstract Gallium‐based liquid metal (LM) composite with metallic fillers is an emerging class of thermal interface materials (TIMs), which are widely applied in electronics and power systems to improve their performance. In situ alloying between gallium and many metallic fillers like copper and silver, however, leads to a deteriorated composite stability. This paper presents an interfacial engineering approach using 3‐chloropropyltriethoxysilane (CPTES) to serve as effective thermal linkers and diffusion barriers at the copper‐gallium oxide interfaces in the LM matrix, achieving an enhancement in both thermal conductivity and stability of the composite. By mixing LM with copper particles modified by CPTES, a thermal conductivity (κ) as high as 65.9 W m−1K−1is achieved. In addition, κ can be tuned by altering the terminal groups of silane molecules, demonstrating the flexibility of this approach. The potential use of such composite as a TIM is also shown in the heat dissipation of a computer central processing unit. While most studies on LM‐based composites enhance the material performance via direct mixing of various fillers, this work provides a different approach to fabricate high‐performance LM‐based composites and may further advance their applications in various areas including thermal management systems, flexible electronics, consumer electronics, and biomedical systems.more » « less
-
On‐Demand Programming of Liquid Metal‐Composite Microstructures through Direct Ink Write 3D PrintingAbstract Soft, elastically deformable composites with liquid metal (LM) droplets can enable new generations of soft electronics, robotics, and reconfigurable structures. However, techniques to control local composite microstructure, which ultimately governs material properties and performance, is lacking. Here a direct ink writing technique is developed to program the LM microstructure (i.e., shape, orientation, and connectivity) on demand throughout elastomer composites. In contrast to inks with rigid particles that have fixed shape and size, it is shown that emulsion inks with LM fillers enable in situ control of microstructure. This enables filaments, films, and 3D structures with unique LM microstructures that are generated on demand and locked in during printing. This includes smooth and discrete transitions from spherical to needle‐like droplets, curvilinear microstructures, geometrically complex embedded inclusion patterns, and connected LM networks. The printed materials are soft (modulus < 200 kPa), highly deformable (>600 % strain), and can be made locally insulating or electrically conductive using a single ink by controlling the process conditions. These capabilities are demonstrated by embedding elongated LM droplets in a soft heat sink, which rapidly dissipates heat from high‐power LEDs. These programmable microstructures can enable new composite paradigms for emerging technologies that demand mechanical compliance with multifunctional response.more » « less
-
This study experimentally and analytically examined the influence of carbon nanofiber (CNF) z-threads on the through-thickness (i.e., z-direction) thermal conductivity of unidirectional carbon fiber reinforced plastics (CFRPs). It was hypothesized that a network of CNF z-threads within CFRPs would provide a thermally conductive microstructure throughout the sample thickness that would increase the through-thickness thermal conductivity. The experiments showed that the through-thickness thermal conductivity of the CNF z-threaded CFRPs (9.85 W/m-K) was approximately 7.53 times greater than that of the control CFRPs (1.31 W/m-K) and 2.73 times greater than that of the unaligned CNF-modified CFRPs (3.61 W/m-K). Accordingly, the CNF z-threads were found to play a substantial role in increasing the through-thickness thermal conductivity of CFRPs. To better understand the role of the CNF z-threads in through-thickness thermal transport, simple logical models of the CFRPs were constructed and then compared with the experimental results. Through these analyses, it was determined that CNF z-threads substantially enhance the through-thickness thermal conductivity by creating carbon fiber-CNF linkages throughout the CFRP laminate; these linkages allow the heat flow to largely bypass the resistive resin that envelops the carbon fibers. In addition, thermal infrared tests illustrated that the increased through-thickness thermal conductivity of the CNF z-threaded CFRP enabled the location and visualization of defects within the laminate, which was not possible with the control CFRP.more » « less
-
null (Ed.)Gallium based liquid metals (LM) have prospective biomedical, stretchable electronics, soft robotics, and energy storage applications, and are being widely adopted as thermal interface materials. The danger of gallium corroding most metals used in microelectronics requires the cumbersome addition of “barrier” layers or LM break-up into droplets within an inert matrix such as silicone oil. Such LM-in-oil emulsions are stabilized by native oxide on the droplets but have decreased thermal performance. Here we show that mixing of the silicone oil into an LM-air foam yields emulsions with inverted phases. We investigate the stability of these oil-in-LM emulsions through a range of processing times and oil viscosities, and characterize the impact of these parameters on the materials’ structure and thermal property relationships. We demonstrate that the emulsion with 40 vol% of 10 cSt silicone oil provides a unique thermal management material with a 10 W m −1 K −1 thermal conductivity and an exterior lubricant thin film that completely prevents corrosion of contacting aluminum.more » « less