Abstract MXenes are among the fastest‐growing families of 2D materials, promising for high‐rate, high‐energy energy storage applications due to their high electronic and ionic conductivity, large surface area, and reversible surface redox ability. The Ti3C2TxMXene shows a capacitive charge storage mechanism in diluted aqueous LiCl electrolyte while achieving abnormal redox‐like features in the water‐in‐salt LiCl electrolyte. Herein, variousoperandotechniques are used to investigate changes in resistance, mass, and electrode thickness of Ti3C2Txduring cycling in salt‐in‐water and water‐in‐salt LiCl electrolytes. Significant resistance variations due to interlayer space changes are recorded in the water‐in‐salt LiCl electrolyte. In both electrolytes, conductivity variations attributed to charge carrier density changes or varied inter‐sheet electron hopping barriers are detected in the capacitive areas, where no thickness variations are observed. Overall, combining thoseoperandotechniques enhances the understanding of charge storage mechanisms and facilitates the development of MXene‐based energy storage devices.
more »
« less
Universal salt-assisted assembly of MXene from suspension on polymer substrates
Abstract Two-dimensional carbides and nitrides, known as MXenes, are promising for water-processable coatings due to their excellent electrical, thermal, and optical properties. However, depositing hydrophilic MXene nanosheets onto inert or hydrophobic polymer surfaces requires plasma treatment or chemical modification. This study demonstrates a universal salt-assisted assembly method that produces ultra-thin, uniform MXene coatings with exceptional mechanical stability and washability on various polymers, including high-performance polymers for extreme temperatures. The salt in the Ti3C2Txcolloidal suspension reduces surface charges, enabling electrostatically hydrophobized MXene deposition on polymers. A library of salts was used to optimize assembly kinetics and coating morphology. A 170 nm MXene coating can reduce radiation temperature by ~200 °C on a 300 °C PEEK substrate, while the coating on Kevlar fabric provides comfort in extreme conditions, including outer space and polar regions.
more »
« less
- PAR ID:
- 10581375
- Publisher / Repository:
- Springer Nature Limited
- Date Published:
- Journal Name:
- Nature Communications
- Volume:
- 15
- Issue:
- 1
- ISSN:
- 2041-1723
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Abstract Modification of a surface with polymer brushes has emerged as an effective approach to tune the properties of a substrate. Brushes grown from an inimer‐containing cross‐linkable polymer coating provide significant advantages compared to other “grafting‐from” methods, such as improved stability, increased grafting density, and the potential to control the grafting density. So far, the inimer coating method has only been applied for surface‐initiated controlled radical polymerizations. In this work, an approach is presented for the fabrication of a stable cross‐linked ultra‐thin polymer coating containing hydroxyl groups which serve as initiating sites for surface‐initiated ring‐opening polymerization (SI‐ROP). The polymers used for the fabrication of the coatings consist of 2‐((tetrahydro‐2H‐pyran‐2‐yl)oxy)ethyl methacrylate (THPEMA), a small fraction of a cross‐linkable unit, and a diluent styrene. Three coatings with varying THPEMA and styrene content are fabricated, and poly(dimethyl siloxane) (PDMS) and poly(caprolactone) (PCL) brushes are grown by SI‐ROP of hexamethylcyclotrisiloxane (D3), and ε‐caprolactone respectively. The brushes are characterized by atomic force microscopy (AFM), X‐ray photoelectron spectroscopy (XPS), static contact angle measurements, ellipsometry and size exclusion chromatography (SEC). The results demonstrate a well‐controlled ROP of D3and ability to control grafting density by tuning the THPEMA content of the coatings.more » « less
-
Abstract 3D continuous mesoscale architectures of nanomaterials possess the potential to revolutionize real‐time electrochemical biosensing through higher active site density and improved accessibility for cell proliferation. Herein, 3D microporous Ti3C2TXMXene biosensors are fabricated to monitor antibiotic release in tissue engineering scaffolds. The Ti3C2TX‐coated 3D electrodes are prepared by conformal MXene deposition on 3D‐printed polymer microlattices. The Ti3C2TXMXene coating facilitates direct electron transfer, leading to the efficient detection of common antibiotics such as gentamicin and vancomycin. The 3D microporous architecture exposes greater electrochemically active MXene surface area, resulting in remarkable sensitivity for detecting gentamicin (10–1 mM) and vancomycin (100–1 mM), 1000 times more sensitive than control electrodes composed of 2D planar films of Ti3C2TXMXene. To characterize the suitability of 3D microporous Ti3C2TXMXene sensors for monitoring drug elution in bone tissue regeneration applications, osteoblast‐like (MG‐63) cells are seeded on the 3D MXene microlattices for 3, 5, and 7 days. Cell proliferation on the 3D microporous MXene is tracked over 7 days, demonstrating its promising biocompatibility and its clinical translation potential. Thus, 3D microporous Ti3C2TXMXene can provide a platform for mediator‐free biosensing, enabling new applications for in vivo monitoring of drug elution.more » « less
-
Abstract In this study, we demonstrate a novel environmental barrier coating processed from polymer‐derived ceramics (PDCs) with homogeneously distributed sub‐micrometer Y2O3as the filler. Under suitable conditions, dense and crack‐free coatings can be achieved for all the designed compositions with the volumetric content of Y2O3varied from 45 to 93 vol%. To process the PDC SiC–Y2O3composite coatings, Y2O3particles and SiC liquid precursor were uniformly dispersed in hexane and then dip‐coated on SiC substrates. After cross‐linking at 250°C and heat‐treated at 900°C in argon, dense and crack‐free PDC SiC–Y2O3composite coatings were formed. The effect of coating thickness and heat‐treatment temperature on the formation of cracks due to constrained pyrolysis was studied. The critical thickness for realizing crack‐free coatings of three compositions (i.e., 93, 77, and 45 vol% Y2O3) was studied for heat treatment from 1000 to 1300°C using atomic force microscope and scanning electron microscopy. As heat‐treatment temperature increases, the critical coating thickness decreases for the same coating compositions due to enhanced shrinkage at higher temperature. With higher Y2O3content, the critical thickness of the coating increased. The inert Y2O3particles reduce the amount of polymer leading to reduction in the overall constrained shrinkage of the coating during heat treatment.more » « less
-
Abstract Structural color arises from light scattering rather than organic pigments and can be found in Nature, such as in bird feathers and butterfly wings. Synthetic materials can mimic Nature by leveraging materials with contrasting optical characteristics by controlling each materials’ spatial arrangement in a heterostructure. Two-dimensional MXene nanosheets are particularly interesting due to their unique optical properties, but MXenes have not been used directly as a structural colorant because it is challenging to control the spatial placement of MXenes at the nanometer level. Here, we report the emergence of structural color in layer-by-layer (LbL) assemblies of Ti3C2TzMXene nanosheets and polyelectrolyte heterostructures with controlled block thicknesses. The block thickness and spatial placement of MXene are controlled by the assembly’s salt concentration and number of layer pairs. This work demonstrates that optical characteristics of MXene/polyelectrolyte heterostructures depend on MXene content and placement, while deepening the understanding of MXenes within structural color films.more » « less
- Free Publicly Accessible Full Text
-
Accepted Manuscript
- Journal Article:
- https://doi.org/10.1038/s41467-024-53840-y